Dielectric barrier discharge is used as a cheap technique for surface treatment of polycarbonate. The discharge system is working in open air at atmospheric pressure. The treatments are carried out at low discharge powers (1.5 and 2 W) for treatment time (2.5 - 15 min). The treated samples show decrease in the contact angle and increase in the crystallinity, thermal stability and surface roughness. The effect of ozone on the increase in the oxygen containing functional groups is discussed. The treatment process shows effective limitation of the migration of bisphenol A from the surface of polycarbonate due to the cross linking. Zero migration of bisphenole A is recorded as the sample is treated for 7.5 min. The treatment process is found to be very efficient with very low cost.
Bisphenol A, (2, 2-bis (4-hydroxyphenyl) propane, (BPA)) is a chemical used primarily as a monomer in the production of polycarbonate plastic (PC). Polycarbonate (PC) is widely used, especially in developing countries, in food contact materials such as infant feeding bottles, tableware (plates, mugs, jugs, and beakers), microwave ovenware, food containers, water bottles, milk and beverage bottles, processing equipment and water pipes. BPA can migrate into food from food containers made of polycarbonate plastic. The human BPA exposure from different sources has been proved [
Plasma has been introduced as an effective technique for treatment of polycarbonate surface. Different properties of the surface of polycarbonate can be changed by plasma treatment [
In the present work a dielectric barrier discharge (DBD) system, working in open air at atmospheric pressure, is introduced as a cheap source of plasma that overcomes the economical disadvantages of plasma treatment systems. For the first time, DBD has been used in the treatment of polycarbonate surface for the sake of limiting the migration of BPA. The effect of DBD treatment on the surface properties of polycarbonate samples has been studied.
The experimental arrangement of DBD plasma reactor used in the present treatment is shown in figure 1. The DBD cell consisted of two electrodes of stainless steel discs, and each one has a diameter of 20 cm and thickness of 2 mm. The lower and upper electrodes were fixed to a perspex base of 40 cm diameter and 2 cm thickness. A dielectric material made of glass has a thickness of 1.2 mm was pasted. The upper and lower perspex discs were collected to each other via rubber O-ring. The gap distance between the dielectric glass and the lower electrode was 3 mm. The cell was fed by air via the gas inlet where the air filled the gap space and then exhausted through the gas outlet. Before any treatments the gas is left to flow in the cell for about 5 minutes to sweep any impurities in the reactor. The gas pressure was kept at atmospheric pressure and the gas flow rate is 0.1 L/min. The two electrodes were connected to a high voltage AC power supply of 50 Hz frequency and a variable voltage of 0 - 10 kV. A limiting resistance of 250 kΩ was used to limit the discharge current. The applied voltage was measured via a resistive potential divider (PD) 500:1. The discharge current was measured by measuring the potential drop across a resistance of 1 kΩ. The accumulated charge on the electrodes was measured by measuring the potential drop across a capacitor of 14 μF. The waveforms of the voltage, current and charge was measured by a digital storage oscilloscope (Model HM-407). The concentration of ozone formed inside the DBD system was measured using ozone analyzer (model AFX H1). The exhaust gas of the DBD cell was collected by the analyzer
Schematic diagram of DBD plasma reactor
and measured with accuracy less than 0.1 g/m3.
PC samples were taken from baby bottles which were collected from the local market in Egypt. The samples were cut into 3 × 2 cm2. The treated samples were fixed at the lower electrode where the upper surface of the sample was exposed to the plasma reactive species. For double face treatments, the samples were retreated on the other surface at the same treatment conditions. The samples were treated in the DBD system at different treatment times (2.5 - 15 min) and different discharge currents (1 and 1.5 mA).
The properties of the samples were examined using different techniques. X-Ray Diffraction (XRD) patterns of the samples were recorded by Shimadzu-XRD-7000 Diffractometer—Japan, operating at room temperature with Cu (Kα) radiations of wavelength (λ = 1.5406 Å), generated at 30 Kv - 30 mA. The 2θ range for all samples was in the range from 4˚ to 80˚ with scan speed 0.2˚/s.
Thermo-Gravimetric Analysis (TGA) (Model TGA-50H, Shimadzu—Japan) was used to study the changes in thermal stability of the treated samples. The measurements were carried out with a heating rate of 10˚C/min under flow of N2 gas where the temperature were elevated up to 600˚C.
The contact angle measurements were carried out using the sessile drop method. A contact angle goniometer (ramé-hatr Model 500) using an optical subsystem was used to capture the profile of a pure drop of water on the surface of the sample and then the contact angle was measured.
Scanning Electron Microscope (SEM) was used to study the morphology of the surface of the samples. The samples were coated with gold by the use of Carbon Sputter Coater SPI, Module control, SPI supplies—USA. After coating the samples were placed in the cavity of JEOL JSM-6390 LA, Scanning Electron Microscope (SEM), with a power supply of 30 kV was used as an electron source, and the magnification was X = 7500.
Gas Chromatography/Mass spectrometry GC/MS (Model GC-2010 with GC/MS-QP 2010 Shimadzu—Japan) was used in the present work to measure the migration of BPA from the polycarbonate samples. The samples were put in a beaker with the stimulant (Methy-tert-butyl ether, from Fisher Sci., UK, HPLC Grade), then shacked at a water bath shaker for one hour, then collected at a glass vials to the chromatographic analysis. GC-MS is frequently used for the determination of BPA concentration because of its high accuracy [
According to the design of present treatment system, the running cost of the treatment process depends only on the consumed power in the discharge cell. To evaluate the consumed power in the DBD cell, it is wrong to express it as the product of current and voltage because of the capacitive reactance of the cell and the filamentary behavior of the current. In the present work, the consumed power has been measured using Lissajous method [
Voltage and current waveforms of DBD
Discharge current and consumed power in the DBD cell as a func- tion of the discharge voltage
DBD cell as a function of the discharge voltage. The consumed power in the DBD cell has been found to be very low, even at high voltage (around 8 kV) the consumed power is less than 8 W. In the present work the treatment processes has been carried out at two applied voltages 4 and 5 kV which correspond to discharge currents 1 and 1.5 mA and consumed powers 1.5 and 2 W respectively. The gas temperature under these conditions varies from 30˚C to 40˚C. At higher discharge voltages the gas temperature is elevated to unwanted values which decrease the efficiency of the treatment process.
The decomposition behavior and thermal stability of the untreated and plasma treated PC samples have been studied using TGA. The thermograms of the untreated and the treated samples are shown in figure 5. The
XRD spectra of the untreated and treated (1.5 W & 7.5 min) PC samples
TGA thermograms of the untreated and the treated (1.5 W & 7.5 min) PC samples
weight loss of the untreated PC sample starts at 400˚C, while it starts at 440˚C for the plasma treated sample. The weight loss reaches a maximum at 570˚C with a value of around 76% for the untreated sample and reaches a maximum at 590˚C with a value of around 70% for the plasma treated samples. These results show that the thermal stability of the PC samples has been increased due to the plasma treatment.
The weight loss of PC sample in TGA is attributed to the decomposition (thermal and oxidative) of carbonate link in between the monomers of BPA with vaporization and elimination of volatile products [
Contact angle as a function of the treatment time at two different discharge powers
to around its half value by plasma treatment showing a saturation behavior with both the treatment time (from 2.5 to 15 min) and the discharge power (1.5 and 2 W). The decrease in contact angle can be attributed to increase in surface roughness and incorporation of hydrophilic functional groups which increases the surface energy and hence decreases the contact angle.
The increase in surface roughness has been proved by the SEM examination of untreated and treated samples, shown in figure 7. Such increase in the surface roughness of the treated sample can be referred to the etching process of PC surface by plasma active species (electrons, ions and UV). In the beginning, the etching process is carried out by removal of low-molecular contaminates such as additive and absorbed species. After that the etching process starts to ablate the polymer chain itself. These etching processes are due to the physical removal of molecules by the impact of energetic plasma species and by the breaking up of bonds and chain scission [
The incorporation of hydrophilic functional groups is mainly related to the increase in the concentration of oxygen containing functional groups at the PC surface [
At atmospheric pressure there is a high probability of the reaction between the excited atomic oxygen and the oxygen molecules to form ozone molecules [
The formation of ozone molecules has been studied as a function of the discharge power by measuring the ozone concentration in the exhaust gas of the DBD cell using ozone analyzer (model AFX H1). This relation is shown in figure 8. The increase of the ozone concentration with the discharge power can be attributed to the increase in the electron density and electron energies which increase the reactions of ozone formation (reaction 1 and 2). The saturation effect at discharge powers higher than 4 W can be referred to the elevation of the gas temperature which increases the dissociation rate of ozone molecules. At discharge powers (1.5 and 2 W) valuable concentrations of ozone (2 and 3 g/m3 respectively) have been measured. The oxidation potential of ozone (2.1 V) is comparable to that of atomic oxygen (2.4 V) [
SEM micrographs of the untreated and treated (1.5 W & 7.5 min) PC samples
Ozone concentration in the exhaust gas of the DBD cell as a function of the discharge power
ment time of 10 min. The limitation of BPA migration by plasma treatment up to 7.5 min can be referred to the effect of surface treatment of PC samples by plasma species. Plasma species break chemical bonds leaving free radicals at the PC surface. Ozone molecules and atomic oxygen react with the free radicals to produce new functional groups. The new fictional groups increase the cross-linking at the PC surface and hence increase the resistance to the dissociation of BPA monomers. The increase in the resistance to the dissociation by the treatment process has been indicated in TGA measurements. The cross linking at the surface of PC can explain the increase in the crystallinity of the treated samples showed by XRD pattern.
The increase in BPA migration at 10 min can be explained by the effect of etching process. At long treatment
The migration of BPA from PC samples as a function of the treatment time at different consumed powers
. Migration of BPA and the cost of the treatment process expressed as the surface density of consumed energy at different treatment conditions.
Power (W) | Treatment Time (min) | Migration of BPA (ppm) | % Limitation | (Cost) Surface density of consumed energy (kWh/m2) |
---|---|---|---|---|
1.5 | 2.5 | 0.55 | 90 | 0.003 |
1.5 | 5 | 0.4 | 92 | 0.006 |
1.5 | 7.5 | 0 | 100 | 0.009 |
1.5 | 10 | 2.6 | 53 | 0.012 |
2 | 2.5 | 1.7 | 70 | 0.004 |
2 | 5 | 0.4 | 92 | 0.008 |
2 | 7.5 | 0 | 100 | 0.012 |
2 | 10 | 1.35 | 75 | 0.016 |
Untreated | 5.5 | 0 | 0 |
time (10 min) the temperature of a thin layer at the surface of the sample is elevated due to the impact of the plasma species on the sample surface and due to the elevation of the gas temperature. Such elevation of the surface temperature of the sample increases the etching rate whereas the etching of the treated layer is faster than the treatment of new layer. So, keeping the sample in low temperature is very important for efficient treatments.
As discussed above the most important advantage of the present system is the low cost of the treatment process. The cost of the treatment process here depends only on the consumed electric energy. The surface density of consumed energy, i.e., the consumed electric energy per unit area of the treated PC samples, has been calculated and shown in table 1. It can be notice that: at optimum treatment conditions, discharge power 1.5 W and treatment time of 7.5 min, the surface density of the consumed energy is only about 0.009 kWh/m2 which is very low cost compared with the cost of the syntheses of PC. According to the present work, DBD is recommended as an economical treatment technique of PC instead of using more expensive materials or more expensive treatment techniques.
Dielectric barrier discharge has been found to be a cheap and effective technique for surface treatment of polycarbonate. The system has shown effective treatment of PC surface even at low consumed power and short treatment time. Examinations of the untreated and treated samples have shown decrease in the contact angle and increase in the crystallinity, thermal stability, and surface roughness. Effect of etching processes on the surface roughness has been indicated. The effect of ozone on the increase in the oxygen containing functional groups has been discussed. Effect of the treatment process on the migration of BPA from the surface of PC has been studied. Optimum limitation of the migration of BPA has been found at treatment time of 7.5 min where there is no any migration of BPA recorded. At longer time of treatment the migration of BPA increases again where the ablation of the treated layers due to high etching rate becomes more effective than the treatment process. The treatment process has been found to be very efficient in the limitation of the migration of BPA with very low cost.