Adsorption techniques using meshed groundnut husk s and plantain peels have provided cheap alternative to the conventional methods of crude oil spillage control and also for good waste management approach. The biodegradable nature of these adsorbents makes it a better alternative to the non biodegradable synthetic polymers. Dry unripe plantain peels and groundnut husk s were used to prepare the adsorbents. The adsorption and percentage removal of crude oil from effluent produce water was dependent on adsorbent dosage, contact time,temperature and particle size. The particle size of the adsorbents should not be less than 150 μm to avoid making the particles so loosed thus posing difficulty in recovery . The two adsorbents exhibit high affinity for oil adsorption with time especially at 75 μm, groundnut husk has a better performance because of its larger surface area and the presence of residual oil in the plantain peels. Agitation at 150 r.min-1 and contact time between 15 - 75 min are recommended. The optimum adsorption temperature ranged between 25°C - 45°C and 15°C - 45°C for groundnut husks and plantain peels respectively. The adsorption data indicated that a pseudo-second- order equation could be used to study the adsorption kinetics of both adsorbents.
The release of liquid petroleum hydrocarbon into the environment especially marine areas due to human activity is a form of pollution. There are existing methods for remediation but their limitations and impact to the environment have called for a more environmentally friendly spill control, some of the methods used are: in-situ burning of oil slick [
Meshing machine (Magimix Cuisine System 5000), Mesh sieve (B.S.410/43), Hygrometer (Fisher Scientific Company), Orbital shaker bath (HY-2 model NYC), Distillation Apparatus (ASTM D4006-11), Thermometer, Graduated bottles and beakers (Pyrex, England), Weighing balance (AL meter Toledo Gmbh 2004) and boat, 0.45 µm micro-porous membrane filter (ASTME-11 spec, Fisher Scientific Co), Separation funnel (Pyrex, England), Oven (Gallenkamp, England), Groundnut husks, Crude Oil (Bonny export blend, xylene), De-ionized water.
The groundnut husks and plantain peels were sourced from a local groundnut oil processing plant and plantain chips industry in Port Harcourt, Rivers State, Nigeria. The samples were thoroughly washed with de-ionized water to remove any occluded impurities and dried in an oven to remove any moisture in order to stabilize the weights. After which; they were meshed and sieved into different particle sizes for use in several Batch adsorption experiments. The effluent produced water was taken from the Nigeria Agip Oil Company Limited (NAOC) facility. The crude oil contents in the produced water was determined using the American Society for Testing and Materials (ASTM D3921-73). Produced water containing 12.0 g of the crude oil having a volume of 1litre of which 75 ml (containing 0.9443 g of crude) was withdrawn for each experiment. The effluent water was put in a 1 liter beaker, a specified amount of 150 mm groundnut husks adsorbent was then added to the mixture. The beaker containing the mixture was placed on an orbital shaker at 150 r∙min−1 at a specified temperature for 45 min. The wetted adsorbent was then removed from the beaker; oil and water was filtered through a 0.45 μm micro porous membrane filter and weighed. The water content in the adsorbent was measured using the Dean and stack distillation technique described in ASTM D4006-11. The wetted adsorbent to the oil/water was refluxed with xylene. Organic solvent and water was continuously condensed into a trap. The water settled in the graduated section of the trap and the solvent returned to the still. This procedure was repeated using plantain peels adsorbent under the same operating conditions. For each experiment the above procedures were followed under the specified operating conditions.
Batch adsorption experiments were carried out using the two adsorbents with the following dosages: 10.0 g; 15.0 g; 20.0 g; 25.0 g and 30.0 g at 25˚C. The weight of oil adsorbed was recorded as g∙g−1 of sorbent.
The adsorption dynamics in terms of contact time was investigated using 15.0 g of 150 μm adsorbent and then shaken at 150 r∙min−1 at 25˚C and at 60˚C for a 15, 30, 45, 60 and 75 minutes. The weights of oil adsorbed at the specified time intervals were determined by subtracting the water content and the initial adsorbent weight from the total wetted sorbent and was recorded as g∙g−1 of sorbent.
Batch adsorption experiment was carried out at 15˚C, 25˚C, 35˚C, 45˚C, 55˚C and 60˚C for 15.0 g of the meshed adsorbents which were shaken at 150 r∙min−1 for 60 min. The weights of oil adsorbed using the adsorbents at specified temperatures were determined by subtracting the water content and the initial adsorbent weight from the total wetted sorbent and were recorded as g∙g−1 of sorbents.
The adsorbents were meshed and sieved into different particle sizes: 75, 150, 212, 400 and 500 μm. Batch adsorption experiments was carried out for the various sizes of the adsorbents by using 15.0 g of the meshed adsorbents. The weights of oil adsorbed at various particle sizes were determined by subtracting the water content and the initial adsorbent weight from the total wetted sorbent and was recorded as g∙g−1 of sorbent.
Adsorption kinetics of crude oil in produced water onto groundnut husks and plantain peels were determined from the data obtained from those experiments using Equations (1)-(4):
The amount of oil adsorbed in g∙g−1 from t = 0 to t = t will be:
Q t = G s − ( W H 2 O + G o ) G o (1)
where; Qt is the amount of oil adsorbed (Adsorption capacity) at time t in (g∙g−1), Gs is the mass of wetted Adsorbents (g), Go is the initial Mass of adsorbent (g) and W H 2 O is the Mass of water adsorbed (g).
The percentage removal of crude oil in solution will be:
%Removal = W s W o × 100 (2)
where, Ws is the Mass of oil adsorbed (g), Wo is the Initial Mass of Crude oil (g).
The kinetics of the crude oil adsorption onto meshed adsorbents was analyzed using the pseudo-second order kinetic model developed by Ho and Mckary [
d q d t = − k 2 ( q e − q ) 2 (3)
where, k2 is the pseudo-second order kinetic rate constant.
Integrating under the boundary condition of t = 0 to t = t and q = 0 to q = q gives:
t q t = 1 q e t + 1 k 2 q e 2 (4)
A plot of t/qt against t gives a linear relationship from which qe and k2 were determined from the slope and intercept of the plot, respectively.
The initial adsorption rate, h (g/gmin) at t = 0 was defined as:-
h = k 2 q e 2 (5)
The results of the effect of adsorbents dosage from the experiments are given in
Initial Mass of adsorbent Go (g) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|
10 | 13.6583 | 3.0 | 0.6583 | 0.066 | 69.7 | 0.22 |
15 | 19.5893 | 3.9 | 0.6893 | 0.046 | 73 | 0.18 |
20 | 25.8715 | 5.1 | 0.7715 | 0.039 | 81.7 | 0.15 |
25 | 32.5583 | 6.7 | 0.8583 | 0.034 | 90.89 | 0.13 |
30 | 38.0819 | 7.2 | 0.8819 | 0.029 | 93.4 | 0.12 |
Initial Mass of adsorbent Go (g) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|
10 | 12.5053 | 3.0 | 0.5053 | 0.051 | 53.5 | 0.25 |
15 | 18.0761 | 2.5 | 0.5761 | 0.038 | 61 | 0.23 |
20 | 24.3253 | 3.6 | 0.7253 | 0.036 | 76.81 | 0.2 |
25 | 29.9231 | 4.1 | 0.8231 | 0.033 | 87.2 | 0.2 |
30 | 35.8462 | 5.0 | 0.8462 | 0.028 | 89.61 | 0.18 |
Time (min) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | t/Qt (min∙g∙g−1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|---|
15 | 18.103 | 2.51 | 0.6275 | 0.042 | 357.14 | 66.45 | 0.25 |
30 | 20.06 | 4.4 | 0.6601 | 0.044 | 681.82 | 69.9 | 0.15 |
45 | 22.54 | 6.8 | 0.7454 | 0.051 | 882.35 | 78.9 | 0.11 |
60 | 23.70 | 7.9 | 0.8042 | 0.054 | 1111.11 | 85.16 | 0.102 |
75 | 23.73 | 7.9 | 0.8277 | 0.055 | 1363.64 | 87.65 | 0.105 |
Time (min) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | t/Qt (min∙g∙g−1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|---|
15 | 19.14 | 3.5 | 0.6380 | 0.043 | 348.84 | 67.56 | 0.18 |
30 | 20.36 | 4.7 | 0.6619 | 0.044 | 681.82 | 70.09 | 0.14 |
45 | 21.02 | 5.3 | 0.07156 | 0.048 | 937.5 | 75.78 | 0.135 |
60 | 21.78 | 6.0 | 0.7815 | 0.52 | 1153.83 | 82.76 | 0.13 |
75 | 22.01 | 6.2 | 0.8102 | 0.054 | 1388.89 | 85.81 | 0.13 |
Time (min) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | t/Qt (min∙g∙g −1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|---|
15 | 17.51 | 1.92 | 0.5768 | 0.031 | 483.87 | 61.08 | 0.3 |
30 | 19.19 | 3.36 | 0.6393 | 0.036 | 883.33 | 60.7 | 0.19 |
45 | 20.21 | 4.5 | 0.7146 | 0.044 | 1022.73 | 75.68 | 0.16 |
60 | 20.83 | 5.07 | 0.7607 | 0.048 | 1250 | 80.6 | 0.15 |
75 | 21.16 | 5.36 | 0.8041 | 0.051 | 1470.59 | 85.15 | 0.15 |
Time (min) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed wads (g) | Qt (g∙g−1) | t/Qt (min∙g∙g−1) | % Removal | Adsorbed oil-water ratio (−) |
---|---|---|---|---|---|---|---|
15 | 18.085 | 2.5 | 0.5850 | 0.039 | 384.615 | 63.07 | 0.23 |
30 | 18.92 | 3.3 | 0.6204 | 0.041 | 731.71 | 65.7 | 0.19 |
45 | 20.106 | 4.4 | 0.7057 | 0.047 | 957.45 | 74.73 | 0.16 |
60 | 20.58 | 4.8 | 0.7825 | 0.052 | 1153.85 | 82.87 | 0.162 |
75 | 21.0 | 5.16 | 0.08457 | 0.056 | 1339.286 | 89.56 | 0.164 |
Temperature (˚C) | K (g∙g−1 min) | Qe (g∙g−1) | h (g∙g−1∙min) | R2 |
---|---|---|---|---|
25 | 1.809257 | 0.061418 | 0.006825 | 0.9942 |
60 | 2.120118 | 0.058774 | 0.007324 | 0.9926 |
Temperature (˚C) | K (g∙g−1 min) | Qe (g∙g−1) | h (g∙g−1∙min) | R2 |
---|---|---|---|---|
25 | 0.760403 | 0.0641 | 0.003124 | 0.9743 |
60 | 1.129261 | 0.064337 | 0.004674 | 0.9816 |
Temperature (˚C) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed Wads (g) | Qt g∙g−1 | % Removal | Adsorbed oil water ratio (−) |
---|---|---|---|---|---|---|
15 | 19.49 | 3.9 | 0.5871 | 0.039 | 62.170 | 0.15 |
25 | 19.71 | 4 | 0.7125 | 0.048 | 75.45 | 0.178 |
35 | 19.94 | 4.19 | 0.7506 | 0.05 | 79.49 | 0.179 |
45 | 20.12 | 4.34 | 0.7814 | 0.052 | 82.75 | 0.18 |
60 | 20.30 | 4.49 | 0.8128 | 0.054 | 86.07 | 0.181 |
Temperature (˚C) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed Wads (g) | Qt g∙g−1 | % Removal | Adsorbed oil water ratio (−) |
---|---|---|---|---|---|---|
15 | 17.81 | 2.32 | 0.4871 | 0.032 | 51.58 | 0.21 |
25 | 18.11 | 2.48 | 0.6198 | 0.039 | 65.64 | 0.25 |
35 | 18.25 | 2.58 | 0.6712 | 0.045 | 71.08 | 0.26 |
45 | 18.97 | 2.61 | 0.6881 | 0.045 | 72.87 | 0.265 |
60 | 18.99 | 2.67 | 0.7201 | 0.040 | 76.26 | 0.27 |
Particle size (µm) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed Wads (g) | Qt g∙g−1 | % Removal | Adsorbed oil water ratio (−) |
---|---|---|---|---|---|---|
75 | 20.693 | 4.8 | 0.8930 | 0.0595 | 94.57 | 0,106 |
150 | 20.912 | 5.14 | 0.7718 | 0.0514 | 81.73 | 0.15 |
212 | 20.6501 | 5 | 0.6501 | 0.043 | 68.84 | 0.13 |
400 | 21.2861 | 5.72 | 0.5661 | 0.038 | 59.95 | 0.099 |
500 | 21.425 | 5.9 | 0.5251 | 0.035 | 55.61 | 0.089 |
Particle size (µm) | Mass of wetted adsorbent Gs (g) | Mass of water adsorbed W H 2 O (g) | Mass of oil adsorbed Wads (g) | Qt g∙g−1 | % Removal | Adsorbed oil water ratio (−) |
---|---|---|---|---|---|---|
75 | 20.155 | 4.31 | 0.8450 | 0.056 | 89.48 | 0.196 |
150 | 20.195 | 4.49 | 0.7057 | 0.047 | 74.67 | 0.157 |
212 | 20.129 | 4.515 | 0.6141 | 0.041 | 65.03 | 0.135 |
400 | 21.235 | 5.71 | 0.5250 | 0.035 | 55.597 | 0.092 |
500 | 21.41 | 5.93 | 0.04801 | 0.032 | 50.84 | 0.081 |
The adsorption capacity (g/g), percentage oil removal and adsorbed oil-water ratio at different sorbent doses are shown in Figures 1(a)-(c) respectively.
The adsorption increased with increase in adsorbent dose as shown in
process since more adsorption sites were available for the same concentration of sorbent (crude oil).The percentage removal of oil increased from 69.7% to 93.4% for groundnut husks and 53.5% to 89.61% for plantain peels as sorbent dose increased from 10 g to 30 g as shown in
The effect of contact time on adsorption for the two adsorbents at 25˚C and 60˚C are shown in Figures 2(a)-(f). The adsorption capacity of groundnut husk at 25˚C increased from 0.042 to 0.055 g∙g−1 and that of plantain peels from 0.031 to 0.051 g∙g−1 whereas the percentage removal at 25˚C for groundnut husks increased from 66.45% to 87.65% and for plantain peels from 61.08% to 85.15% as the time increase from 15 to 75 min. While at 60˚C with the same time increase, the adsorption capacity of groundnut husks increased from 0.043 to 0.054 g∙g−1 and plantain peels from 0.039 to 0.056 g∙g−1 whereas percentage removal of groundnut increased from 67.56% to 85.81% and that of plantain peels from 63.07% to 89.56%.
The adsorbed oil-water ratio at different time interval at 25˚C and 60˚C for the two adsorbents decreased from 0.25 to 0.105 for groundnut husks and 0.3 to 0.15 for plantain peels at 25˚C and from 0.18 to 0.13 for groundnut husks and 0.23 to 0.164 for plantain peels at 60˚C. An increase in adsorption capacity and percentage removal suggests that 150 r∙min−1 agitation speed was adequate to allow the binding sites adsorbed more crude oil as the contact time increased for the two adsorbents. Increased in adsorbed oil-water ratio implied that more water was adsorbed on exceeding the time equilibrium concentration of oil but groundnut husks absorbed more water than plantain peels.
Using the pseudo-second order equation to describe the type of adsorption as has been suggested as being more appropriate for this type of adsorption [
The result of batch adsorption experiment carried out for different temperatures of adsorbent is given in
of crude oil was 25˚C - 45˚C indicating that the sorption process was an adsorption process and depended on the temperature whereas that of plantain peels showed an increase from 15˚C - 45˚C and a sharp decrease; the optimum temperature was 45˚C. The sharp decrease shows a low adsorption interaction between the adsorbent and the adsorbate at increased temperature for plantain peels but a better interaction with groundnut husk.
The result of batch adsorption experiment carried out for different particle sizes of the adsorbents are given in
both adsorbents have relatively higher adsorption capacity percentage removal and adsorbed oil-water ratio respectively and the rate of adsorption increased with increase in surface area of the adsorbent while sorption efficiency increased with holding capacity. The differences in adsorption capacity, percentage removal of oil and adsorbed oil-water ratio between the different particle sizes of groundnut husks and plantain peels could be explained by the fact that smaller particles possessed not only larger surface areas and interstitial packing; but also the tendency of producing shorter time of equilibration.
The adsorption of crude oil using meshed groundnut husk and plantain peels as adsorbents have been studied. The results obtained showed that the percentage removal of crude oil from effluent produced water were dependent on adsorbent doses, contact time, temperature and particle size. The two adsorbents exhibited high affinity for oil adsorption especially at a particle size of 75 µm. Meshed groundnut husks had a better performance than plantain peels due to its larger surface areas and the presence of occluded residual oil retained in the meshed unripe plantain peels. The optimum adsorption temperature ranged for groundnut husks was 25˚C - 45˚C and 15˚C - 45˚C for plantain peels with a decrease at 60˚C. The adsorption data indicated that a pseudo-second-order equation could be used to study the adsorption kinetics of both adsorbents and the correlation coefficient indicated that the sorption process was dominated by adsorption process. As a result of the high affinity for oil and low water pick up; meshed groundnut husks and plantain peels adsorbent could be said to be oleophilic or hydrophobic. 150 r∙min−1 and contact time between 15 - 75 minutes is recommended for proper agitation so as to allow adsorption at the binding sites for the two adsorbents.
Dagde, K.K. (2018) Biosorption of Crude Oil Spill Using Groundnut Husks and Plantain Peels as Adsorbents. Advances in Chemical Engineering and Science, 8, 161-175. https://doi.org/10.4236/aces.2018.83011