Nanomaterials have been widely used in the past few decades due to their proven capacity to enhance the mechanical properties of materials. While many studies have sought to improve the understanding of how nanomaterials affect the behavior of concrete, additional research is needed in order to achieve the full potential of the material, especially in the presence of supplementary cementitious materials. This study aims to investigate the mechanical properties of cement mortars incorporating both nano-silica (NS) and class F fly ash (FA). Furthermore, mercury intrusion porosimetry (MIP) was performed to study its effect on pore characteristics, and thermogravimetric analysis (TGA) was performed to measure the calcium hydroxide Ca(OH) 2 content in the mixtures. It was found that using nano-silica enhances the compressive strength, reduces the total porosity and accelerates the pozzolanic reaction.
The use of supplementary cementitious materials (SCM) reduces the embodied energy in concrete considerably. Furthermore, it significantly improves the durability of concrete and increases its lifecycle thus leading to a more sustainable design. However, despite the available literature on nanotechnology and its applications in the construction industry, further research is needed on the effect of using nano silica (NS) in concrete, especially when combined with SCMs. Fly ash is the most commonly used supplementary cementitious material in the cement industry because of its various advantages like increased flowability [
Researchers have examined the effects of using NS in pastes [
Colloidal NS was used in the form of an alkaline aqueous solution with 50% silica by weight. The nano-silica dispersion was sodium stabilized and the particles have a negative surface charge. The properties are tabulated in
Nano-Silica, wt (%) | 50 |
---|---|
pH | 9 |
Viscosity, cP | 15 |
Density, g/cm3 | 1.4 |
Na2O, wt (%) | 0.4 |
Group number | Mixture ID | binder percentage | ||
---|---|---|---|---|
OPC | Fly ash | CNS | ||
Group 1 | OPC | 100 | 0 | 0 |
NS1 | 98 | 0 | 2 | |
NS2 | 96 | 0 | 4 | |
Group 2 | FA1 | 75 | 25 | 0 |
NF1 | 73 | 25 | 2 | |
NF2 | 71 | 25 | 4 | |
Group 3 | FA2 | 65 | 35 | 0 |
NF11 | 63 | 35 | 2 | |
NF22 | 61 | 35 | 4 |
The compressive strength gain of different mortars was assessed by testing standard cubes following ASTM C 109 [
Colloidal NS improved the compressive strength of mortar in all groups. With no FA replacement, introducing 2% and 4% NS improved the compressive strength from 6.54 ksi to 7.37 ksi and 7.71 ksi, respectively. With 25% FA replacement, the addition of 2% and 4% NS enhanced the compressive strength from 6.68 ksi to 7.14 ksi and 7.23 ksi, respectively. Finally, for 35% FA replacement, the addition of 2% and 4% NS improved the compressive strength from 6.48 ksi to 6.56 ksi and 6.93 ksi, respectively. These results are illustrated separately in
The observed improvement in compressive strength can be attributed to the accelerated pozzolanic reaction in the presence of NS along with a decreased porosity which will be discussed in the next section. The NS reacts with calcium hydroxide to produce calcium-silicate-hydrate (C-S-H). A smaller amount of calcium hydroxide is available in the mixtures containing FA since cement, the source of calcium silicates that react with water to form calcium hydroxide, is being partially replaced by FA. Accordingly, more calcium hydroxide is converted into C-S-H in the absence of FA which increases the relative improvement of strength between groups. Namely, in Group 1 where there is no FA replacement, a larger improvement in the compressive strength is observed when NS is added with respect to the control specimen whereas when NS is added to Groups 2 and 3, less improvement in f ′ c is observed in NF1, NF2, NF11, and NF22 when compared to FA1 and FA2 respectively. Furthermore, FA is known to refine the porosity of concrete [
Mercury intrusion porosimetry can be utilized to study the pore distribution of hardened cementitious materials over a range going from a few hundred microns to as small as few nanometers. In the MIP test, mercury is pressured to fill pores in the samples. As a non-wetting liquid, mercury does not naturally penetrate the pores and, therefore, the pressure required to force it into the pores can be correlated to the corresponding pore volume in the form:
| 2 γ cos θ | = Pr (1)
where γ is the surface tension of mercury, θ is the angle of contact, P is the pressure and r is pore radius. Subsequently, the recorded values are plotted in the form of a curve that traces the cumulative pore volume versus pressure. While this method is quite popular, it has some drawbacks pertaining to the assumptions made in order to get the total porosity. Particularly assuming constant surface tension within the sample and ignoring pore irregularity [
Using MIP, the measured average porosity of mortar samples decreased for all categories in the presence of NS. This can be attributed to the filler effect where the small NS particles fill smaller pores that cannot be filled by relatively larger cement particles, sand, or FA particles. Decreasing the porosity of samples leads to an increase in the compressive strength and a reduction of potential environmental deteriorations. The average pore diameters for all samples are illustrated in
Furthermore, as shown in
larger-sized pores are observed with the NS samples, an indication of potential agglomeration. Many of the benefits of NS can be compromised by agglomeration [
Thermogravimetric analysis was performed on paste rather than mortar. This was done to eliminate any impurities that may be introduced by sand. Closed plastic containers were used to mold the paste and parafilm was also used under the lid to prevent any carbonation. The impermeable containers were then kept at a room temperature of 24˚C. At the time of testing, the samples were removed from the plastic containers, ground using a mortar and pestle to pass sieve #200. Consequently, the powder was placed in the TGA under an inert gas (N2) to dry at 100˚C. After drying the sample and the weight loss stops, the sample is heated again at 15˚C/min and the weight loss was recorded. Additionally, the first derivative of the TG curve (DTG) is recorded with respect to temperature. Each peak in the DTG curve indicates a different phase and the mass loss in that region can be used to quantify the phase in question. In this study, Ca(OH)2 is of interest and any Ca(CO)3 resulting from carbonation. This is typically found between 400˚C and 550˚C and can be precisely detected by following the DTG peaks [
NS decreases the content of Ca(OH)2 for all groups at all ages as shown in Figures 4-6. This reduction in the amount of calcium hydroxide is very beneficial because it indicates the progress of the pozzolanic reaction and the production of additional C-S-H. In addition to the improved mechanical characteristics caused by C-S-H, low calcium hydroxide content reduces the potential for alkali-silica reactions where calcium is a vital element for that reaction [
The current study assessed the influence of colloidal NS on cement mortars in 3 separate groups that contained 0%, 25% and 35% FA replacements respectively. And the following conclusions are drawn:
・ The use of colloidal NS improves the compressive strength of all mortar groups, but it is most effective in the groups not containing FA. This improvement is attributed to the accelerated pozzolanic reaction and the filler effect.
・ The use of colloidal NS reduces the average pore diameter for all mixtures, the small particle size of NS helped reduce the amount of small pores but additional large-sized pores are observed which may be attributed to agglomeration.
・ Colloidal NS reduces the amount of calcium hydroxide in the mixtures and is therefore efficient in converting calcium hydroxide into calcium silicate hydrate and in enhancing the pozzolanic reaction even at early age.
Since potential signs of agglomeration were observed in the form of large pores, it is important to emphasize the need for dispersion thorough available methods including sonication or high energy mixing for best results. Also, Scanning Electron Microscopy (SEM) and other techniques could be used in order to verify the results and add more details about the hydration process and chemical composition of the resulting mixture.
Ayad, A. and Said, A. (2018) Using Colloidal Nano Silica to Enhance the Performance of Cementitious Mortars. Open Journal of Civil Engineering, 8, 82-90. https://doi.org/10.4236/ojce.2018.81007