Colloidal and molecular solutes in suspension are excluded from the vicinity of various hydrophilic surfaces, leaving an exclusion zone (EZ) of hundreds of micrometers. Such exclusion zones were observed in the vicinity of many types of surface including artificial and natural hydrogels, biological tissues as well as hydrophilic polymers. Old studies have shown that the near-surface exclusion zone expands extensively in the presence of incident radiant energy, especially the infrared light. Developments of electromagnetic biology and quantum biology indicate that electron and nuclear spin may have a direct impact on the biological process. Inspired by these researches, the effects of spinning magnetic ferrite on EZ were studied. It is shown that spinning magnetic ferrite profoundly expands these zones in an irreversible manner.
The exclusion zone (EZ) of water develops in the direct vicinity of hydrophilic materials [
Quantum biology studies have shown that electron and nuclear spin plays important roles in many life processes, such as long-range electron transfer, the oxidation of water, and neural processing [
In the present study, we utilize a nickel-manganese ferrite rotator designed by Alexander A. Shpilman [
As a hydrophilic substance, Nafion 117 per-fluorinated membrane was used in the experiments. Nafion is a perfluorosulfonic ionomer that consists of a polytetrafluoroethylene backbone and regularly spaced side chains terminated by sulfonate ionic groups [
The nickel-manganese ferrite rotator used in experiments was designed by Alexander A. Shpilman (
All experiments were carried out at 20˚C - 23˚C and in a dark room to minimize background noise.
Nafion membranes were cut into 1 cm × 2 cm squares. Peel off the thin backing layer, then dunk in water to separate the Nafion from the thick coversheet. All these square membranes were processed as follow steps: 1 hour in lightly boiling (~80˚C) 5% H2O2 0.5 hour in DI water 1 hour in lightly boiling 5% H2SO4. At last, Store these membranes in DI water for experiments [
To observe whether microscopes were excluded from the zones near the Nafion-117 surface, a chamber with floor was used. This chamber was made using 3D printing technology. It was a cuboid of length 5cm × width 2 cm × height 1 mm with a hole in the center. The hole was a rectangle of length 3 cm × width 1.6 cm × height 1 mm.
For sample illumination, an ordinary LED was used for experiment. After pretreatment, the Nafion membrane was attached to the medial surface of the chamber and illuminated by LED with the optical axis perpendicular to it. The chamber was filled with an aqueous suspension of microspheres and placed on a slide. The slide was viewed under an electron microscopy.
The ferrite rotator was used to investigate the effect of spin field on EZ size. The procedure of the experiment was the same as above in addition to replacing the LED with the ferrite rotor. Since the ferrite rotor can only work continuously for no more than 20 minutes at a time, it would be stopped for about 10minutes after working for 15 minutes. The distance between the ferrite rotor and the Nafion membranes are usually 20 cm. The position of the ferrite rotor is slightly higher than the chamber so that the membranes were exposed directly to the field generated.
Microspheres immediately translated away from the edges of the Nafion sheet, forming an exclusion zone of 250 um within 10 minutes. The width of the zone then grew more slowly at an almost unseen speed after 30 minutes. The results illustrated in
The effect of radiant energy on EZ size was very obvious. An ordinary LED was applied 40minutes after the establishment of the exclusion zone to ensure that the establishment of the EZ was stable. The EZ size began to increase, and expanded almost double times as the baseline EZ size after 120 minutes of exposure (Figures 2(a)-(d)). To minimize any effects of microscope illumination, the microscope lamp was turned off when the EZ was not been observed.
Similar with the experiments of radiant energy on Nafion membranes, ferrite rotor was applied when there were not obvious changes of EZ size. The baseline EZ size was selected after 30 minutes when the width was no longer significantly changed. Pause time of rotor were not been calculated. The microscope lamp was turned off when the EZ was not been observed. The width of EZ increased to about 1.5 times as the baseline EZ size after 60 minutes of exposure (Figures 3(a)-(d)).
Generally, it is hard to establish EZ with non-pretreatment nafion membranes. There is another simple method to form EZ without the special designed chamber. A membrane could be placed between two large glass cover slips. Microspheres solution was drooped along the edge of slips. However, EZ was unstable as there was only a small amount of microsphere solution which was often evaporated in a short time. The chamber was able to accommodate more solution, which was suitable for long observation.
A series of LEDS were used in the work of Binghua Chai [
The most important result of this study is that the width of EZ grows in the presence of a nickel-manganese ferrite rotator. Although the mechanism of exclusion is not yet clear, growth of this more ordered, negatively charged zone may be dependent on the presumed spin field relating with the circular rotating electron spin.
In conclusion, EZ was established using Nafion membranes which must be pretreated and the width expanded with Irradiation of an ordinary LED. This study reveals that the effects of the field generated by a ferrite rotator could promote the growth of exclusion zones. Considering the universality of electron spin and structured water in the organisms, our study may be of significance for quantum biology research.
This work is supported by National Natural Science Foundation of China (NSFC) (No. 61471010) and Dunhe Foundation.
Zhou, Y., Wen, X., Shpilman, A.A. and Ren, Q.S. (2017) Effect of Spinning Magnetic Ferrite on the Exclusion Zone. Journal of Biosciences and Medicines, 5, 1-7. https://doi.org/10.4236/jbm.2017.512001