This paper discusses the development method of strain sensors based on acicular single crystal compound TlInTe 2 is grown by Bridgman-Stockbarger technique. Creating mechanically reliable ohmic contacts on said obtained single crystals was carried out directly by spot welding wires corresponding to the ends of the capacitor discharge heated in a stream of inert gas from the single crystal TlInTe2. This method of creating contacts proved effective and reliable. Sensors made by this manner stuck to the calibrated beams of steel thickness of 1 mm, a length of 30 mm and a corresponding optimal regime got sensors with a maximum piezo-sensitivity. It was found that if enshrined at one end of a thin steel sheet with glued crystals TlInTe2 initiate periodic mechanical vibrations to the same frequency, occurs conductivity modulation. The effect of piezo-modulation conductance depending on the degree of deformation, illumination in interval of deformation and lux illumination in room temperature were studied. The study showed that the more mechanical deformation and illumination are, the more modulation amplitude is. We studied the modulation of the conductivity of crystals during mechanical deformation values of 8, 14, 19, 23 and 27 × 10 -5and illuminance 1000, 2750, 4750 and 6500 suites. Investigations the level piezo-signal depending on the amplitude of mechanical vibrations at frequency of 85 Hz, it is found that with increasing magnitude of the mechanical deformation of 7 × 10 -5 and 26 × 10 -5 amplitude increases six times. It is shown that the piezoresistive effect is clearly manifested in dynamic mode. Additional conductivity occurs during mechanical deformation. When the illuminated samples piezoconductivity magnitude increases linearly.
The interest in semiconductor compound of АIIIВIIIХ2V types, being similar to АIIIВVI arises from the presence of unpaired number of valence electrons, sharp asymmetry of chemical bond, specific peculiarities of crystal lattice structure and the possibility to realize variation at wide range in chemical composition in the frame of lattice [
The research of fundamental physical properties of semiconductors is important to obtain information on zone parameters, energy spectrum of charge carrier and their scattering mechanism in the crystal.
Since kinetic phenomena in semiconductors is heavily dependent on type, quantity and impurity distribution and is very sensitive to such external actions as electric, magnetic, acoustic and temperature fields, deformation and illumination, these processes are the physical basis of numerous transformers used in up-to-date electronic, optical, photoelectric, magnetic, acoustic, strain gauge and piezoelectric devices. Clearly, profound research of new properties of compounds and solid solutions results in the discovery of new effects and possibilities in an advanced instrumentation [
However, there is no any information on piezomodulation of conductance in TlInTe2 crystals. This paper aims at studying the effects of piezo-modulation in TlInTe2 ternary compound.
Fresh cleavages easily splits from massive ingot of thin standard-gauge plates in TlInTe2 crystals with four opposed mirror edges of natural cleavage were used to produce strain sensors.
The similar TlInTe2 crystals used to produce strain sensors-gauges can easily be derived with a simple pressing in of a sharp knife (blade thickness―0.01 mm) on loose tip of a thin but wide and long TlInTe2 plate at an acute angle.
After choosing the further step, determining the width of workpieces, the plate along with the stages of micromanipulator is moved under a microscope across the line of spallation.
Obtained zone melting methods needle crystals TlInTe2 with mirrored facets without any additional treatments were ready for welding pins and landing them on a base substrate (
Mechanically reliable ohmic contacts on the mentioned workpieces were produced by spot welding of wires by capacitor discharge to the ends of a workpiece heated in the flow of inert gas. This method was effective and reliable.
Steel plates with a thickness of 1 mm and a length of 30 mm were used like tared beams for glued transducers. The substrate surface corresponded to the 7th class of
processing. Before applying the sublayer, the given substrates were treated in toluene to be defatted, being later washed in ethyl alcohol. The sublayer of epoxy-cresol varnish (EP-96), being a solution of epoxy resin (E-40) modified by equal acid with butanolizedresol “RB” and K-421-02 resin, was brushed on cleaned substrates (surface patch).
A thickness of sublayer is 16 micrometers. In the process applying of sublayer was ensured uniform coating by thicker.
After 2 hour exposure in room temperature, the substrate is moved to drying cabinet for high-temperature polymerization.
Slow rise of temperature to 480 K and 2 hour exposure in room temperature contributes to full polymerization, preventing from air bubbles. A second layer of varnish, exceeding the size of resistance strain gauge, is applied on substrate over sublayer.
TlInTe2 crystals with welded pins are landed on a layer of varnish and are slightly pressed, while, crystal surface is completely varnished. At the same time, crystal is properly positioned in substrate plane.
A device is covered with 1.5 mm thin width fluoroplastic (PTFE) tape for a tighter contact with transducer and maintenance of specified orientation of transducer in regard to substrate. A transducer is dried an hour at 300 K with post annealing and two hours at 460 K.
If necessary, after drying, fluoroplastic (PTFE) tape is easily removed from ready transducer. This drying mode proved to be optimal and the instruments showed the highest sensitivity (
The following step is to study tensometric features of the strain sensor on the basis of TlInTe2 single crystals.
We found that if mechanical oscillations are excited on a thin steel plate fixed at one end with TlInTe2 glued crystals, modulation of conductance has the same frequency then.
The effect of piezo-modulation was recorded by the scheme in
υ frequency and ΔVon amplitude values of piezo-signal were recorded by a F510 selective amplifier. Depending on the task, piezo-signal in some cases was recorded on the tapes of 8LS type recorders. Similarly, C 1-29 type storage oscilloscopes proved to be convenient.
In the study of piezo-modulation in TlInTe2 crystals, a recorded piezo-signal on the display screen is shown in
Experimental values on the study of piezo-modulation effects in different peaks of mechanical deformation and illumination are in
The modulation of conductance and mechanical deformation of sample were considered to be at equal (
crystals.
The variable component of total conductance, i.e. piezo-conductance is determined by the formula
It should be noted that, the main practical and methodical tasks of semiconducting strain gauging aim at determining pure piezo-conductance:
It is known that the latter is determined by a variable component of the current
According to Ohm, the absence of deformation:
When with deformation the resistance of crystal decreases in ΔRn(n, t), the current increases in In(n, t), then
After simple transformations in the last three equations [
Thus, strain gauge for the constant field (
Here, the relative deformation is determined by
with
It should be noted that, the presence of piezo-resistive effect is more observed in dynamic mode. In fact, if a crystal is undergoes to proportional deformation
The amplitude values increases with an increasing degree of deformation.
However, when an optical illumination is laid, additional conductance
Consequently, piezo-photoconductance:
Thus it is possible to track changes of piezo-photoconductance with an increasing intensity of illumination, while measuring amplitude values at the same degree of deforma-
tion in the dark
For this purpose, the recording was made (
the amplitude of piezophoto-conductance
According to oscillograms in
According to experimental data, an observed piezo-photoresistive effect may significantly broaden the possibilities of semiconducting strain gauging to record dynamic processes (
The investigation of the piezo-modulation effects and conductivity of single crystal TlInTe2 revealed that with the change of the value mechanical deformation and optical illumination can be obtained materials with high strain sensitivity for recording dynamic processes.
Gojaev, E.M., Agaeva, S.Kh., Kulieva, S.O. and Dadashov, M.T. (2016) Piezomodulation of Connection Conductance TlInTe2. Open Journal of Inorganic Non-Metallic Materials, 6, 25-32. http://dx.doi.org/10.4236/ojinm.2016.64005