The polyaddition of isocyanate and polyol to form polyurethane elastomers has rarely been applied to the construction of chiral polyurethane elastomers. Hence, the introduction of chiral units via polyaddition remains a challenging subject in polymer chemistry. In this study, the synthesis of chiral polyurethane elastomers using an aromatic isocyanate, polyols (polyether and polyester polyols), and L(+)-, D(−)-, or meso-tartaric acid by a one-shot method is investigated. The polymers are characterized using FTIR and NMR spectroscopy, and their thermal properties are investigated by TGA, DMA, and DSC analyses. The optical activities of the polymers are confirmed by rotation. The use of chiral tartaric acids is essential to obtain the desired chiral polyurethane elastomers.
Polyurethane elastomers (PUEs) can be easily prepared by the polyaddition of isocyanate and polyol. Therefore, PUEs [
In this article, we report the synthesis of PUEs containing L(+)-, D(−)-, or meso-tartaric acid using an aromatic isocyanate, 4,4’-diphenylmethane diisocyanate (MDI), one of three different polyols (polytetramethylene glycol (PTMG), polycaprolactone diol (PCL), and polycarbonate diol (PCD)), and L(+)-, D(−)-, or meso-tartaric acid as a cross-linker via a one-shot method. The molecular structure analyses of these PUEs were conducted, and their chemical and physical properties were described. The appearance of asymmetry in PUEs containing L(+)-, D(−)-, or meso-tartaric acid was also investigated.
PTMG (molecular weight = 2000; PTMG2000) was supplied by Invista Industry, Texas, USA. PCL (molecular weight = 2000; PCL2000) was supplied by Daicel Industry, Osaka, Japan. MDI and PCD (molecular weight = 2000; PCD2000) were supplied by Tosoh Industry, Tokyo, Japan (Tosoh). MDI was purified by distillation under reduced pressure (267 - 400 Pa) at 100˚C before use. L(+)- and D(−)-tartaric acid were purchased from Nacalai Tesque Inc., Kyoto, Japan (Nacalai) and used without further purification. Meso-tartaric acid was purchased from Tokyo Chemical Industry, Tokyo, Japan. Tetrahydrofuran (THF; Nacalai) was dried using CaH2 for several days and was distilled prior to use under an Ar atmosphere. Benzene was purchased from Nacalai. N,N- Dimethylformamide (DMF) (Nacalai) and dimethyl sulfoxide (DMSO) (Nacalai) were purchased and stored over 4 Å molecular sieves before use. The following compounds were purchased from commercial suppliers and used as received: DMSO-d6 (Euriso Top, Saint-Aubin, France), hexane (Nacalai), and acetone (Nacalai).
Scheme 1 shows the preparation procedure for the L(+)-, D(−)-, or meso-tartaric-acid-containing PUEs. PUEs containing tartaric acid were prepared from MDI, a polyol (either PTMG2000, PCL2000, or PCD2000), and L(+)-, D(−)-, or meso-tartaric acid by a one-shot method. White solids separated out with increasing tartaric acid content. When the quantities of tartaric acid were 0.65 wt%, 1.4 wt%, and 2.3 wt%, the reaction time was 30 min. Conversely, when the quantities of tartaric acid were 3.4 wt% and 4.8 wt%, the reaction time was 60 min. The compositions of the PUEs are shown in
A sheet (thickness = 0.5 - 0.6 mm) was obtained by casting the resulting solution (20 g). Sheets of PUE-PTMG-
Scheme 1. Preparation of the chiral polyurethane elastomers containing tartaric acid.
Sample | MDI (mol × 10−2) | Polyola (mol × 10−2) | Sucrose (mol × 10−3) | Sucrose content (wt%) |
---|---|---|---|---|
PUET1 (L/D/meso) | 2.0 | 0.90 | 0.10 | 0.65 |
PUET2 (L/D/meso) | 2.0 | 0.80 | 0.20 | 1.4 |
PUET3 (L/D/meso) | 2.0 | 0.70 | 0.30 | 2.3 |
PUET4 (L/D/meso) | 2.0 | 0.60 | 0.40 | 3.4 |
PUET5 (L/D/meso) | 2.0 | 0.50 | 0.50 | 4.8 |
PUE | 2.0 | 1.0 | - | - |
aPolyol: polyoxytetramethylene glycol (molecular weight = 2000), polycaprolactone diol (molecular weight = 2000), polycarbonate diol (molecular weight = 2000).
1H nuclear magnetic resonance (NMR; 300 MHz) and 13C NMR (75.4 MHz) spectra were recorded on a Varian Unity Plus-300 spectrometer using tetramethylsilane in dimethyl sulfoxide-d6 (DMSO-d6) at room temperature (23˚C ± 2˚C) as an internal standard. The 13C NMR acquisition parameters were as follows: spectral width = 18.859 kHz; acquisition time = 1.816 s; recycle delay = 0.185 s; transients = 4000; and spectral frequency = 75.4 MHz.
All analyses and tests were performed at room temperature (23˚C ± 2˚C) unless otherwise indicated.
1H nuclear magnetic resonance (NMR; 300 MHz) and 13C NMR (75.4 MHz) spectra were recorded on a Varian Unity Plus-300 spectrometer using tetramethylsilane in dimethyl sulfoxide-d6 (DMSO-d6) at room temperature (23˚C ± 2˚C) as an internal standard. The 13C NMR acquisition parameters were as follows: spectral width = 18.859 kHz; acquisition time = 1.816 s; recycle delay = 0.185 s; transients = 4000; and spectral frequency = 75.4 MHz.
Fourier transform infrared (FTIR) spectra were recorded on a JASCO FT/IR-5300 using the attenuated total reflection (ATR) method and the transmission method at room temperature (23˚C ± 2˚C). The ATR spectrum was measured by an ATR500/M using an ATR KRS-5 prism.
The measurement conditions for GPC were as follows: sample, 0.1% N,N’-dimethylformamide (DMF) solution; solvent, DMF; column, TSK gels α-M and TSK Gurdcolumnα; flow rate, 500 μL/min at 40˚C; quantum, polystyrene transformation method.
Solubility tests were performed using 15 × 15 mm test pieces. Each test piece was soaked in a solvent (benzene, hexane, acetone, THF, DMF, or DMSO; 8.0 mL) at room temperature (23˚C ± 2˚C) or 100˚C (for DMF and DMSO) for 24 h.
Swelling tests were conducted using a test piece with dimensions of 15 × 15 mm. The degree of swelling (Rs) was calculated using the formula Rs (%) = W’/W × 100, where W’ is the weight of the test piece soaked in benzene for 24 h, and W is the weight of the test piece after drying at 30˚C for 24 h in vacuo.
The hardness was investigated using a Kobunshi Keiki Asker Durometer (JIS A type) at room temperature (23˚C ± 2˚C). The test pieces for measurement were stacked up to a thickness of 6 mm.
Tensile tests were conducted using an Orientec RTC-1225A with model-U-4300. A JIS 3-dumbel was used as the standard sample. The measurement conditions for the tensile tests were as follows: crosshead speed = 100 mm/min and room temperature (23˚C ± 2˚C). Tensile tests were performed on an Orientec RTC-1225A with a model-U-4300 using a JIS 3-dumbell as the standard sample and a crosshead speed of 100 mm/min.
Dynamic mechanical analysis (DMA) was performed on a Seiko Instruments DMS 6100 at a heating rate of 5˚C/min from −100˚C to 300˚C and a frequency of 20 Hz under an N2 atmosphere.
Differential scanning calorimetry (DSC) measurements were performed on a Rigaku Thermo-Plus DSC-8230 at a heating rate of 10˚C/min from −120˚C to 200˚C under an Ar atmosphere. Approximately 9.5 mg of each composite was weighed and sealed in an aluminum pan. The samples were quickly cooled to −120˚C and then heated to 200˚C at 10˚C/min.
Thermogravimetric analysis (TGA) was performed with a Seiko Instruments TG/DTA6200 at a heating rate of 10˚C/min from 30˚C to 500˚C under an N2 atmosphere.
Optical rotation was measured by an Atago Polax-2L using a 200 mm observation pipe. The concentration of the sample was 10 wt% in N-methylpyrrolidone solution. The specific optical rotation was calculated using the following formula: [α]D = 100α/L × C.
The molecular structures were calculated using Gaussian09W with the B3LYP/6-31G basis set. The molecular model was depicted using GaussView5.0.
Analyses by 1H NMR and 13C NMR spectroscopy revealed that the polymers obtained were undoubtedly PUEs containing tartaric acid and that these polymers were composed from a urethane segment and tartaric acid. The NMR analyses indicated that tartaric acid was attached to the main PU chain as a cross-linker. For example, the 1H NMR (DMSO-d6) spectrum of PUE-PTMG-T1L included peaks at 8.55 ppm (-CO-NH-), 7.34 ppm and 7.08 ppm (-C6H4-), 4.05 ppm and 3.31 ppm (-O-CH2-), 3.78 ppm (-C6H4-CH2-C6H4-), and 1.48 ppm (-CH2-CH2-, -CH(R)-) (
The IR spectra of PUE-PTMG-TL1-5 are shown in
polyurethane molecule, whereas the bands at 2936 cm−1, 2850 cm−1, and 2795 cm−1 are attributable to the stretching vibration absorptions of aliphatic and aromatic -CH. The bands at 1729 cm−1 and 1708 cm−1 are related to the stretching vibration absorptions of =CO of urethane and the end of the polyurethane molecule, respectively.
The GPC of PUEs containing tartaric acid units is reported in Tables 2-4. For example, PUE-PTMG-TL1-5; Mw 47,000 - 150,000; Mw/Mn 2.2 - 6.1, PUE-PCL-TL1-5; Mw 34,000 - 85,000; Mw/Mn 2.8 - 7.2, PUE-PCD-TL1-5;
Sample | Hardnessa (JIS A) | Swelling rateb (%) | [α]Dc | Tgd (˚C) | T10e (˚C) | Mwf (×104) | Mw/Mnf |
---|---|---|---|---|---|---|---|
PUE-PTMG-T1L | 80 | 240 | - | −67.1 | 355 | 15 | 3.3 |
PUE-PTMG-T2L | 82 | 231 | +2.5 | −65.1 | 352 | 10 | 2.4 |
PUE-PTMG-T3L | 84 | 222 | +4.2 | −68.8 | 350 | 7.4 | 2.2 |
PUE-PTMG-T4L | 86 | 190 | +5.0 | −67.8 | 338 | 6.6 | 4.2 |
PUE-PTMG-T5L | 87 | 174 | +5.8 | −67.7 | 338 | 4.7 | 6.1 |
PUE-PTMG | 77 | 229 | ±0.0 | −67.0 | 351 | 38 | 4.8 |
PUE-PCL-T1L | 78 | 200 | +0.50 | −46.7 | 349 | 8.5 | 2.8 |
PUE-PCL-T2L | 83 | 195 | +1.0 | −46.2 | 350 | 6.8 | 6.5 |
PUE-PCL-T3L | 88 | 182 | +2.2 | −44.6 | 347 | 4.8 | 5.9 |
PUE-PCL-T4L | 91 | 168 | +3.0 | −47.2 | 342 | 3.4 | 6.2 |
PUE-PCL-T5L | 94 | 148 | +5.2 | −48.0 | 334 | 3.4 | 7.2 |
PUE-PCL | 67 | 204 | ±0.0 | −45.0 | 338 | 16 | 3.5 |
PUE-PCD-T1L | 77 | 193 | - | −27.8 | 337 | 14 | 3.2 |
PUE-PCD-T2L | 83 | 189 | - | −28.6 | 336 | 9.4 | 3.3 |
PUE-PCD-T3L | 84 | 184 | +2.2 | −28.6 | 332 | 8.0 | 2.6 |
PUE-PCD-T4L | 88 | 175 | +3.0 | −28.5 | 330 | 6.1 | 2.3 |
PUE-PCD-T5 | 92 | 172 | +5.2 | −28.5 | 327 | 4.3 | 4.7 |
PUE-PCD | 79 | 195 | ±0.0 | −26.4 | 313 | 21 | 3.6 |
aMeasurement conditions: JIS A type, total thickness = 6 mm, measurement temperature = room temperature (23˚C ± 2˚C). bMeasurement conditions: solvent = benzene, measurement temperature = room temperature (23˚C ± 2˚C), measurement time = 24 h. cMeasurement conditions : solvent = NMP, sample = 10 wt%, measurement temperature = room temperature (23˚C ± 2˚C). dDifferential scanning calorimetry performed at 10˚C/min from −120˚C to 200˚C under Ar atmosphere. eThermogravimetric analysis performed at 10˚C/min from 30˚C to 500˚C under N2 atmosphere. fMeasurements conditions: solvent = N,N-dimethylformamide, sample = 0.1 wt% (N,N-dimethylformamide/dimethyl sulfoxide = 1/1 solution), flow rate 500 μL/min, measurement temperature = 40˚C.
Sample | Hardnessa (JIS A) | Swelling rateb (%) | [α]Dc | Tgd (˚C) | T10e (˚C) | Mwf (×104) | Mw/Mnf |
---|---|---|---|---|---|---|---|
PUE-PTMG-T1D | 78 | 237 | - | −66.9 | 354 | 16 | 3.4 |
PUE-PTMG-T2D | 82 | 239 | −2.5 | −67.3 | 354 | 10 | 2.2 |
PUE-PTMG-T3D | 84 | 216 | −2.8 | −66.8 | 350 | 6.8 | 2.4 |
PUE-PTMG-T4D | 86 | 190 | −3.5 | −68.6 | 346 | 3.9 | 6.8 |
PUE-PTMG-T5D | 90 | 175 | −5.0 | −68.6 | 336 | 4.7 | 2.2 |
PUE-PTMG | 77 | 229 | ±0.0 | −67.0 | 351 | 38 | 4.8 |
PUE-PCL-T1D | 76 | 196 | −0.80 | −45.8 | 345 | 10 | 2.9 |
PUE-PCL-T2D | 86 | 191 | −2.0 | −47.6 | 349 | 5.7 | 7.6 |
PUE-PCL-T3D | 90 | 185 | −2.5 | −44.8 | 345 | 5.1 | 5.6 |
PUE-PCL-T4D | 92 | 165 | −3.8 | −46.8 | 338 | 2.6 | 8.3 |
PUE-PCL-T5D | 92 | 150 | −5.5 | −47.1 | 338 | 3.2 | 6.3 |
---|---|---|---|---|---|---|---|
PUE-PCL | 67 | 204 | ±0.0 | −45.0 | 338 | 16 | 3.5 |
PUE-PCD-T1D | 80 | 192 | - | −27.4 | 337 | 15 | 3.6 |
PUE-PCD-T2D | 83 | 188 | - | −27.4 | 336 | 7.7 | 2.0 |
PUE-PCD-T3D | 86 | 181 | −3.8 | −26.2 | 333 | 5.5 | 4.3 |
PUE-PCD-T4D | 90 | 172 | −4.0 | −28.9 | 320 | 5.6 | 6.8 |
PUE-PCD-T5D | 92 | 164 | −5.8 | −27.5 | 326 | 4.2 | 8.5 |
PUE-PCD | 79 | 195 | ±0.0 | −26.4 | 313 | 21 | 3.6 |
aMeasurement conditions: JIS A type, total thickness = 6 mm, measurement temperature = room temperature (23˚C ± 2˚C). bMeasurement conditions: solvent = benzene, measurement temperature = room temperature (23˚C ± 2˚C), measurement time = 24 h. cMeasurement conditions : solvent = NMP, sample = 10 wt%, measurement temperature = room temperature (23˚C ± 2˚C). dDifferential scanning calorimetry performed at 10˚C/min from −120˚C to 200˚C under Ar atmosphere. eThermogravimetric analysis performed at 10˚C/min from 30˚C to 500˚C under N2 atmosphere. fMeasurements conditions: solvent = N,N-dimethylformamide, sample = 0.1 wt% (N,N-dimethylformamide/dimethyl sulfoxide = 1/1 solution), flow rate 500 μL/min, measurement temperature = 40˚C.
Sample | Hardnessa (JIS A) | Swelling rateb (%) | [α]Dc | Tgd (˚C) | T10e (˚C) | Mwf (×104) | Mw/Mnf |
---|---|---|---|---|---|---|---|
PUE-PTMG-T1meso | 78 | 254 | ±0.0 | −67.4 | 350 | 13 | 3.2 |
PUE-PTMG-T2meso | 81 | 236 | ±0.0 | −67.4 | 354 | 9.8 | 2.9 |
PUE-PTMG-T3meso | 84 | 218 | ±0.0 | −67.9 | 349 | 7.6 | 8.2 |
PUE-PTMG-T4meso | 86 | 200 | ±0.0 | −68.1 | 344 | 5.7 | 2.3 |
PUE-PTMG-T5meso | 87 | 163 | ±0.0 | −67.7 | 348 | 3.9 | 7.5 |
PUE-PTMG | 77 | 229 | ±0.0 | −67.0 | 351 | 38 | 4.8 |
PUE-PCL-T1meso | 71 | 202 | ±0.0 | −45.5 | 345 | 14 | 4.8 |
PUE-PCL-T2meso | 83 | 198 | ±0.0 | −47.6 | 346 | 9.3 | 2.5 |
PUE-PCL-T3meso | 85 | 190 | ±0.0 | −47.5 | 345 | 8.6 | 2.5 |
PUE-PCL-T4meso | 88 | 178 | ±0.0 | −48.7 | 338 | 6.8 | 2.4 |
PUE-PCL-T5meso | 89 | 162 | ±0.0 | −45.2 | 325 | 4.4 | 2.1 |
PUE-PCL | 67 | 204 | ±0.0 | −45.0 | 338 | 16 | 3.5 |
PUE-PCD-T1meso | 80 | 190 | ±0.0 | −30.1 | 336 | 20 | 5.0 |
PUE-PCD-T2meso | 83 | 187 | ±0.0 | −29.7 | 335 | 11 | 3.2 |
PUE-PCD-T3meso | 84 | 182 | ±0.0 | −30.6 | 333 | 6.4 | 2.8 |
PUE-PCD-T4meso | 87 | 178 | ±0.0 | −30.7 | 340 | 6.1 | 2.8 |
PUE-PCD-T5meso | 90 | 163 | ±0.0 | −28.0 | 338 | 4.4 | 2.6 |
PUE-PCD | 79 | 195 | ±0.0 | −26.4 | 313 | 21 | 3.6 |
aMeasurement conditions: JIS A type, total thickness = 6 mm, measurement temperature = room temperature (23˚C ± 2˚C). bMeasurement conditions: solvent = benzene, measurement temperature = room temperature (23˚C ± 2˚C), measurement time = 24 h. cMeasurement conditions : solvent = NMP, sample = 10 wt%, measurement temperature = room temperature (23˚C ± 2˚C). dDifferential scanning calorimetry performed at 10˚C/min from −120˚C to 200˚C under Ar atmosphere. eThermogravimetric analysis performed at 10˚C/min from 30˚C to 500˚C under N2 atmosphere. fMeasurements conditions: solvent = N,N-dimethylformamide, sample = 0.1 wt% (N,N-dimethylformamide/dimethyl sulfoxide = 1/1 solution), flow rate 500 μL/min, measurement temperature = 40˚C.
Mw 43,000 - 140,000; Mw/Mn 2.6 - 4.7. The results indicate that the molecular weights of PUEs with tartaric acid decrease with increasing tartaric acid content in the composite.
The solvent resistances of the chiral tartaric-acid-containing PUEs were investigated. The sheets were immersed in various organic solvents (hexane, toluene, acetone, THF, DMF, and DMSO) for 24 h. The results are shown in
The results of the hardness test for the PUEs containing L(+)-, D(−)-, and meso-tartaric acid are shown in Tables 2-4, respectively. The results indicate that the hardness increases with increasing tartaric acid content in the composite.
The tensile properties of the L(+)-, D(−)-, and meso-tartaric-acid-containing PUEs are reported in Tables 6-8, respectively. The tensile strengths of PUE-(PTMG/PCL)-T1(L/D), PUE-(PTMG/PCL/PCD)-T1 and 2(meso), and PUE-PCL-T1(meso) were greater and the tensile strengths of PUE-(PTMG/PCL)-T2-5(L/D), PUE-PCL-T2- 5(meso), and PUE-(PTMG/PCL/PCD)-T3-5(meso) were smaller than those of the PUEs without tartaric acid. The tensile strengths of PUEs with tartaric acid decreased with increasing tartaric acid content. The elongation at the breaking points of PUE-(PTMG/PCL)-T1-3(L/D), PUE-PCL-T4(meso), PUE-PCD-T1-4 (L/D/meso), and PUE-PCD-T5(L) were greater and the elongation at the breaking points of PUE-(PTMG/PCL)-T4 and 5(L/D), PUE-PCL-T5(D) and PUE-PCD-T5(meso) were smaller than those of the PUEs without tartaric acid. The mixture of the tartaric acid and polyurethane chains in the soft amorphous phases reduced the mobility of the macromolecular chains, thereby generating stiff PUEs with tartaric acid when tartaric acid was in the matrix phase. Tartaric acid is a rigid, whereas polyurethane is a ductile elastomer. As a result, the tensile strengths and elongation at the breaking points of PUE-(PTMG/PCL/PCD)-T1 (L/D/meso) were better than those of the PUEs without tartaric acid. In addition, the comprehensive mechanical properties of the PUEs containing tartaric acid were superior to those of the PUEs without tartaric acid content, as shown in
The addition of tartaric acid has a wide range of effects when its content is over 1.4 wt%. The initial modulus increases with increasing tartaric acid content in the composite. The PUE calcifies upon the addition of tartaric acid. The PUE with 0.65 wt% tartaric acid content showed the best elastomeric behavior.
Agreement between the results of the tensile and hardness tests suggests that the network chain density in the composites increases with increasing tartaric acid content.
Samplea,b | Benzenec | Hexanec | THFc | DMFd | DMSOd | ||
---|---|---|---|---|---|---|---|
23˚C | 100˚C | 23˚C | 100˚C | ||||
PUE-Polyol-T1 | △ | × | × | △ | △ | ○ | △ |
PUE-Polyol-T2 | △ | × | × | △ | △ | ○ | △ |
PUE-Polyol-T3 | △ | × | × | △ | △ | ○ | △ |
PUE-Polyol-T4 | △ | × | × | △ | △ | ○ | △ |
PUE-Polyol-T5 | △ | × | × | △ | △ | ○ | △ |
PUE-Polyol | △ | × | △ | △ | △ | ○ | △ |
○: dissolve, △: swell, ×: insoluble. aPolyol: polyoxytetramethylene glycol (molecular weight = 2000), polycaprolactone diol (molecular weight = 2000), polycarbonate diol (molecular weight = 2000). bMeasurement conditions: room temperature (23˚C ± 2˚C). cMeasurement conditions: room temperature (23˚C ± 2˚C) and 100˚C.
Samplea | M10 (MPa) | M50 (MPa) | M100 (MPa) | M200 (MPa) | M300 (MPa) | M400 (MPa) | M500 (MPa) | M600 (MPa) | M700 (MPa) | TBb (MPa) | EBc (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
PUE-PTMG-T1L | 2.38 | 4.13 | 4.86 | 6.62 | 10.5 | 17.7 | 32.1 | 55.5 | - | 59.9 | 615 |
PUE-PTMG-T2L | 2.47 | 4.36 | 5.32 | 7.41 | 11.0 | 16.3 | 24.2 | 33.4 | 43.8 | 45.6 | 715 |
PUE-PTMG-T3L | 2.31 | 4.21 | 5.20 | 7.34 | 10.6 | 14.7 | 19.7 | 24.9 | - | 28.9 | 677 |
PUE-PTMG-T4L | 3.31 | 5.76 | 6.79 | 8.68 | 10.2 | 11.5 | - | - | - | 12.2 | 452 |
PUE-PTMG-T5L | 4.01 | 6.70 | - | - | - | - | - | - | - | 7.37 | 91.0 |
PUE-PTMG | 2.07 | 3.43 | 4.13 | 4.78 | 5.68 | 17.7 | 36.8 | - | - | 55.0 | 551 |
PUE-PCL-T1L | 2.07 | 3.25 | 2.37 | 7.26 | 14.7 | 26.0 | 56.2 | - | - | 61.3 | 509 |
PUE-PCL-T2L | 3.31 | 4.52 | 3.95 | 9.47 | 15.1 | 21.7 | 30.8 | - | - | 45.2 | 590 |
PUE-PCL-T3L | 6.55 | 7.27 | 5.44 | 11.2 | 16.0 | 21.8 | 28.2 | - | - | 35.3 | 582 |
PUE-PCL-T4L | 7.27 | 7.95 | 7.76 | 12.4 | 15.5 | 18.4 | - | - | - | 18.4 | 401 |
PUE-PCL-T5L | 7.96 | 9.40 | 8.64 | - | - | - | - | - | - | 10.5 | 109 |
PUE-PCL | 1.37 | 2.74 | 3.39 | 6.49 | 17.8 | - | - | - | - | 49.1 | 398 |
PUE-PCD-T1L | 2.51 | 4.35 | 5.89 | 15.4 | 52.0 | - | - | - | - | 66.0 | 398 |
PUE-PCD-T2L | 3.17 | 5.66 | 8.17 | 18.5 | 41.3 | - | - | - | - | 60.7 | 320 |
PUE-PCD-T3L | 4.32 | 7.58 | 10.6 | 20.7 | 38.7 | - | - | - | - | 55.1 | 352 |
PUE-PCD-T4L | 5.61 | 9.73 | 13.2 | 23.2 | 36.5 | - | - | - | - | 39.2 | 371 |
PUE-PCD-T5L | 7.09 | 11.5 | 14.4 | 23.7 | - | - | - | - | - | 29.0 | 326 |
PUE-PCD | 1.25 | 2.87 | 3.95 | 11.9 | - | - | - | - | - | 58.9 | 273 |
aTensile properties measured at room temperature (23˚C ± 2˚C) with strain speed of 100 mm/min. bTensile strength at breaking point. cElongation at breaking point.
Samplea | M10 (MPa) | M50 (MPa) | M100 (MPa) | M200 (MPa) | M300 (MPa) | M400 (MPa) | M500 (MPa) | M600 (MPa) | M700 (MPa) | TBb (MPa) | EBc (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
PUE-PTMG-T1D | 4.63 | 5.39 | 6.09 | 8.15 | 12.2 | 18.5 | 30.7 | 47.3 | - | 55.7 | 637 |
PUE-PTMG-T2D | 2.75 | 4.75 | 5.61 | 7.32 | 10.1 | 13.8 | 18.7 | 25.0 | 31.0 | 38.7 | 819 |
PUE-PTMG-T3D | 3.77 | 6.07 | 7.00 | 8.84 | 11.1 | 13.4 | 16.0 | 19.2 | 21.6 | 22.7 | 740 |
PUE-PTMG-T4D | 3.73 | 5.89 | 6.78 | 8.23 | 9.09 | - | - | - | - | 9.12 | 307 |
PUE-PTMG-T5D | 4.94 | 7.75 | 8.57 | - | - | - | - | - | - | 9.10 | 152 |
PUE-PTMG | 2.07 | 3.43 | 4.13 | 4.78 | 5.68 | 17.7 | 36.8 | - | - | 55.0 | 551 |
PUE-PCL-T1D | 1.62 | 2.70 | 3.34 | 6.04 | 12.3 | 20.8 | 36.3 | - | - | 57.5 | 564 |
PUE-PCL-T2D | 5.42 | 6.48 | 7.25 | 11.3 | 16.0 | 21.6 | 28.4 | 39.2 | - | 42.5 | 625 |
PUE-PCL-T3D | 6.01 | 7.25 | 8.07 | 12.0 | 16.1 | 20.5 | 25.4 | 30.7 | - | 32.6 | 627 |
PUE-PCL-T4D | 6.67 | 7.91 | 8.76 | 12.1 | 14.9 | - | - | - | - | 16.7 | 388 |
PUE-PCL-T5D | 9.00 | - | - | - | - | - | - | - | - | 9.56 | 23.5 |
PUE-PCL | 1.37 | 2.74 | 3.39 | 6.49 | 17.8 | - | - | - | - | 49.1 | 398 |
PUE-PCD-T1D | 2.71 | 4.92 | 7.53 | 20.1 | 52.3 | - | - | - | - | 70.1 | 331 |
PUE-PCD-T2D | 3.14 | 5.65 | 8.18 | 19.2 | 45.6 | - | - | - | - | 65.1 | 345 |
PUE-PCD-T3D | 4.08 | 6.97 | 9.37 | 18.8 | 38.7 | - | - | - | - | 53.3 | 352 |
PUE-PCD-T4D | 5.15 | 9.02 | 12.4 | 21.6 | 35.3 | - | - | - | - | 36.7 | 311 |
PUE-PCD-T5D | 6.42 | 11.0 | 14.5 | 23.7 | - | - | - | - | - | 29.1 | 266 |
PUE-PCD | 1.25 | 2.87 | 3.95 | 11.9 | - | - | - | - | - | 58.9 | 273 |
aTensile properties measured at room temperature (23˚C ± 2˚C) with strain speed of 100 mm/min. bTensile strength at breaking point. cElongation at breaking point.
Samplea | M10 (MPa) | M50 (MPa) | M100 (MPa) | M200 (MPa) | M300 (MPa) | M400 (MPa) | M500 (MPa) | M600 (MPa) | M700 (MPa) | TBb (MPa) | EBc (%) |
---|---|---|---|---|---|---|---|---|---|---|---|
PUE-PTMG-T1meso | 2.11 | 3.68 | 4.51 | 6.33 | 9.74 | 15.5 | 26.1 | 38.0 | 54.0 | 54.3 | 702 |
PUE-PTMG-T2meso | 4.09 | 6.82 | 7.91 | 1.00 | 12.8 | 16.9 | 22.5 | 3.04 | 38.2 | 46.1 | 795 |
PUE-PTMG-T3meso | 3.92 | 6.22 | 7.27 | 9.33 | 11.8 | 14.4 | 17.3 | 21.1 | - | 23.9 | 688 |
PUE-PTMG-T4meso | 4.13 | 7.09 | 8.42 | 10.4 | 12.5 | 13.8 | - | - | - | 13.8 | 409 |
PUE-PTMG-T5meso | 3.49 | 5.68 | 6.49 | - | - | - | - | - | - | 6.61 | 113 |
PUE-PTMG | 2.07 | 3.43 | 4.13 | 4.78 | 5.68 | 17.7 | 36.8 | - | - | 55.0 | 551 |
PUE-PCL-T1meso | 3.61 | 4.61 | 5.11 | 8.59 | 15.0 | 24.6 | 46.2 | - | - | 62.3 | 539 |
PUE-PCL-T2meso | 5.77 | 6.34 | 7.00 | 10.5 | 15.0 | 20.6 | 27.0 | 37.5 | - | 40.4 | 624 |
PUE-PCL-T3meso | 5.50 | 6.13 | 6.78 | 10.3 | 14.2 | 18.7 | 24.6 | - | - | 27.7 | 558 |
PUE-PCL-T4meso | 5.62 | 6.55 | 7.48 | 10.8 | 14.3 | 17.5 | - | - | - | 17.8 | 411 |
PUE-PCL-T5meso | 4.54 | 6.09 | 7.28 | 10.7 | - | - | - | - | - | 13.7 | 291 |
PUE-PCL | 1.37 | 2.74 | 3.39 | 6.49 | 17.8 | - | - | - | - | 49.1 | 398 |
PUE-PCD-T1meso | 2.91 | 5.17 | 7.39 | 18.7 | 56.3 | - | - | - | - | 63.5 | 312 |
PUE-PCD-T2meso | 3.42 | 5.89 | 8.54 | 19.8 | 44.3 | - | - | - | - | 61.8 | 340 |
PUE-PCD-T3meso | 4.20 | 7.40 | 10.5 | 20.8 | 39.2 | - | - | - | - | 49.4 | 341 |
PUE-PCD-T4meso | 4.81 | 8.23 | 11.4 | 21.3 | 35.3 | - | - | - | - | 38.2 | 320 |
PUE-PCD-T5meso | 4.93 | 8.85 | 12.2 | - | - | - | - | - | - | 29.1 | 266 |
PUE-PCD | 1.25 | 2.87 | 3.95 | 11.9 | - | - | - | - | - | 58.9 | 273 |
aTensile properties measured at room temperature (23˚C ± 2˚C) with strain speed of 100 mm/min. bTensile strength at breaking point. cElongation at breaking point.
In Tables 2-4, one main transition of the composites is observed in the DSC scans in the range from −100˚C to 200˚C. The values of the glass transition temperature (Tg) for the composites are −67.0˚C for PUE-PTMG, −45˚C for PUE-PCL, and −26.4˚C for PUE-PCD. The values of Tg for the tartaric-acid-containing PUEs do not increase with increasing tartaric acid content. The Tg values of the PUEs with tartaric acid significantly fall in comparison with those of the PUEs without tartaric acid.
The thermal stability of the tartaric-acid-containing PUEs was examined by TGA under an N2 atmosphere. In Tables 2-4, the 10 wt% weight loss temperature (T10) for all samples decreases with increasing tartaric acid content. The T10 values of PUE-PCL-T1-5 (L/D/meso) and PUE-PCD-T1-5 (L/D/meso) are greater than those of PUE-PCL and PUE-PCD, respectively. There were two distinct stages of decomposition. In the first stage, PUEs decomposed slowly until 300˚C, which accounted for the first 10% of the weight loss. Weight loss was very rapid in the temperature range from 300˚C to 500˚C. The main degradation process can be observed at temperatures around 450˚C. The weight loss of the PUEs containing tartaric acid increases when the hard segment content (tartaric acid) increases, a fact which is in accordance with the existence of a higher number of weaker urethane bonds. The first stage of degradation is dominated by urethane bond decomposition.
DMA of the tartaric-acid-containing PUEs was carried out in temperature range from −100˚C to 300˚C. The results are shown in Tables 2-4. The rubber flat regions of the PUEs with tartaric acid are unaltered for all samples. The peak positions of tanδ for the PUEs with tartaric acid are unaltered for all samples. However, in the cases of PUE-PTMG-T1-5 (L/D/meso) and PUE-PCD-T1-5 (L/D/meso), the peaks broaden with increasing tartaric acid content.
The specific optical rotations of the chiral tartaric-acid-containing PUEs are shown in Tables 2-4. Optical rotation of the L(+)-tartaric-acid-containing PUEs occurs in the positive direction. Conversely, optical rotation of the D(−)-tartaric-acid-containing PUEs occurs in the negative direction. The PUEs containing meso-tartaric acid do not exhibit any optical rotation. In addition, the specific optical rotations of the tartaric-acid-containing PUEs increase with increasing tartaric acid content. These results suggest that the asymmetric center remains in the main chains of PUEs containing L(+)- or D(−)-tartaric acid.
The reactivity of the NCO group towards highly acidic functional groups is very low. Therefore, a reaction between the carboxyl group in tartaric acid and the NCO group would not be expected. The molecular structures of PUE and the tartaric-acid-containing PUEs were predicted using Gaussian molecular calculations. The results are shown in
In the present work, a series of chiral PUEs containing tartaric acid was synthesized from chiral tartaric acid, polyether or polyester polyol, and diisocyanate by a one-shot method. Sheets of the colorless translucent tartaric-acid-containing PUEs were obtained when PTMG2000 was used as the polyol, while translucent light-green and yellow sheets were obtained using PCL2000 and PCD2000, respectively. The sheets showed solvent resistances similar to that of the mother polyurethane due to the formation of network structures. They changed from
elastic (PUE-(PTMG/PCL/PCD)-T1 and 2 (L/D/meso)) to plastic-like (PUE-(PTMG/PCL/PCD)-T3-5 (L/D/meso)) due to the effect of an increase in tartaric acid content on the chemical structure and crosslink density. The inclusion of 0.65 wt% and/or 1.4 wt% tartaric acid improved the mechanical properties such as tensile strengths and elongation at the breaking points of the PUEs, and the sheets were elastic. The chiral PUEs containing tartaric acid had asymmetric structures. These results provide a better understanding of the relationships between the structures and properties of chiral PUEs.
KazunoriKizuka,Shin-IchiInoue, (2016) Synthesis and Properties of Chiral Polyurethane Elastomers Using Tartaric Acids. Open Journal of Organic Polymer Materials,06,38-52. doi: 10.4236/ojopm.2016.61005