Urea-formaldehyde (UF) resin is widely used as an adhesive for the manufacture of a range of wood and fiber based products. Although the microstructure of this resin has been examined at high resolution by field-emission scanning electron microscopy and atomic force microscopy, transmission electron microscopy (TEM) has thus far not been used, perhaps because of difficulties in ultrathin sectioning this resin in cured (polymerized) state. In the technical note presented here, a novel sample preparation method is described which enabled us to examine the microstructural morphology of UF resin by transmission electron microscopy in ultrathin sections, revealing the presence of spherical particles within the resin. Our initial attempt to ultrathin section the resin directly was not successful as it was too brittle to trim blocks for sectioning. Then, we developed a sample preparation technique that involved impregnation ofPinus radiatawood tissues with the UF resin, and then embedding of resin impregnated wood tissues with Spurr’s low viscosity embedding medium, which has been widely employed in plant and wood ultrastructure work. The TEM images illustrated and the information on the microstructural morphology of the UF resin presented are based on this novel sample preparation approach.
Urea-formaldehyde (UF) is an aminoplastic thermosetting resin that forms from chemical reaction between urea and formaldehyde. Under certain temperature and pH conditions the liquid UF resin polymerizes (cures) through condensation and cross-linking reactions. UF resin has been widely used industrially as an adhesive in the manufacture of a range of wood and fiber based products, such as plywood, particleboards and medium density fiberboards, because of its high reactivity, fast curing rate, light and clear appearance in manufactured products and low purchase and application costs amongst its many desirable properties and advantages. However, there are some important issues related to its use that must be addressed to make UF resin also environmentally acceptable, such as formaldehyde emission during the service life of wood based products made using this resin. Because of its hydrolytic sensitivity to moisture [
Polymer microand nano-scale structural characterization requires use of high resolution imaging tools and techniques, and scanning and transmission electron microscopes (SEM and TEM) have been widely used to examine microstructural features of a wide range of polymers individually and in combinations, including the polymers which serve as wood adhesives [1,4-11]. In anticipation to develop formulations and processes to minimize formaldehyde emission from UF resin, the micromorphology of this resin has been investigated by SEM in relation to different proportions of formaldehyde and urea (FU mole ratio) in the urea-formaldehyde mix and the effect of factors, such as hydrolytic reactions under acidic and moisture conditions [
The susceptibility of UF resin to hydrolytic degradation is thought to be related to its chemical structure and degree of cross linking, and in this regard microand nano-textures may serve as a useful signature for assessing the extent of degradation from the factors that can induce chemical and physical changes in the cured UF resin. TEM is a powerful tool to examine microand nano-textures of polymeric materials. However, to date TEM has not been used to investigate the microstructural features of UF resin, possibly because of technical difficulties with sample preparation and ultrathin sectioning. We report here a novel sample preparation method that enabled us to obtain ultrathin sections of UF resin and examine its micromorphological features with TEM.
UF resin is sensitive to exposure to moisture or water and may undergo hydrolysis. UF resin also becomes hard and extremely brittle after cure. Therefore, in preparing samples for TEM observation attention was given to avoid contact of samples with water, particularly prior to embedding in the polymeric embedding medium. For these reasons and the fact that UF resin proved to be an extremely difficult polymer for preparing ultrathin sections, the methods are described here in much greater detail than the description published for routine sample preparation for TEM.
Urea and formaldehyde (37%) were mixed in proportions suitable to prepare UF resins containing low (FU mole ratio 1.2) and high (FU mole ratio 1.4) proportions of formaldehyde (F) to urea (U) in the resin mix. Resin preparation and curing methods were adapted from [
A method was developed to fill the lumens of wood tissues with liquid UF resin and subsequently cure it, hoping that it may be possible to ultrathin section the resin contained within the confines of wood cell walls. This method worked and is described here in detail. The approach taken was similar to that used to prepare plywood products by gluing several veneers in cross orienttations of their wood grain (long direction of major wood tissues), except that we used only two veneer pieces (each ca 2 mm thick) and glued them with UF resin adhesive (UF resin), keeping the direction of wood grain of paired veneers same for ease in obtaining sections with a sliding microtome.
Liquid UF resin adhesive, containing 0.1% NH4CL as hardener, was uniformly spread over one surface of a Pinus radiata (radiata pine) veneer piece and then a matching veneer piece was placed over the UF resin adhesive keeping the orientation of the wood grain of the two veneer pieces same. The paired veneers were then clamped at either end to apply pressure to spread the resin adhesive uniformly over contact surfaces on the veneers, and the set was kept at room temperature for 24 hours to allow the liquid resin adhesive to penetrate into wood cells from the adhesive bond line. Subsequently, the resin adhesive was cured at 60˚C in an oven for 24 hours, and then the paired veneer set was prepared for sectioning by cutting into small rectangular pieces.
To avoid direct contact of UF resin adhesive with water, the veneer pieces were sectioned dry (without softening the wood with water) on a sliding microtome in the long direction of wood grain to obtain about 90 µm thick sections. The sections were placed between two glass slides, clamped on either end to prevent the sections from curling and stored at room temperature until sample processing for TEM observation.
Prior to infiltration and embedding in Spurr’s resin, the sections were placed in 100% acetone in plastic vials for 15 minutes. The sections were then infiltrated with the spurr’s resin mix by gradually increasing the concentration of the resin to 50% in acetone over a 2-hour period. Caps were then removed from the vials to allow the acetone to evaporate overnight. The vials were placed under vacuum for 5 - 6 hours to remove any remaining traces of acetone and to facilitate resin infiltration into veneer sections. Subsequently, two changes of fresh resin were made over a period of 48 hours, with vacuum applied after each change. To embed the samples, fresh resin was poured into the slots of an embedding mould, and the sections were then placed (one section per slot) and allowed to sink to the bottom. The mould was placed in an oven set at 65˚C for 1 hour, and then taken out to remove any air bubbles that had surfaced as well as to reposition the sections (if they had moved) correctly to obtain transverse sections through wood tissues (
The resin blocks were placed under a light microscope on
a glass slide for locating the UF resin adhesive bond line and selecting blocks where one end of the section was positioned closest to the conical tip of the block. The adhesive line was readily distinguishable from wood tissues, which facilitated selection of the sample region for trimming to obtain a block face suitable for smoothening with a glass knife. Final trimming was done to reduce the size of the block face to contain 6 - 8 wood cells, including those that were in contact with or near the adhesive line and were filled with UF resin adhesive. The blocks were sectioned with a diamond knife on an ultramicrotome to obtain 80 - 90 nm thick sections (it was not possible to cut any thinner sections without considerable distortion because of the extreme hardness of UF resin adhesive containing wood tissues). The sections were stained for 7 minutes with either 2% aqueous uranyl acetate or 2% uranyl acetate prepared in 50% ethanol. Aqueous uranyl acetate was slightly superior to alcoholic uranyl acetate in improving the contrast of UF resin microstructure, and therefore the images illustrated are based only on staining with aqueous uranyl acetate. Although the exact mechanism of uranyl acetate staining still remains unclear, it has been suggested that this reagent reacts with amino group, and this was the basis for selection of uranyl acetate for staining ultrathin sections, as UF resin is an aminoplastic resin. The sections were viewed with H-7100 Hitachi TEM operating at 75 kV.
Micromorphological features of UF resin are also being investigated using SEM. However, here the sample preparation is only briefly described as SEM observation was not the main focus of the work reported, and the images illustrated (
Sections cut from UF resin adhesive glued veneers on a sliding microtome were mounted on SEM stubs using a carbon adhesive tape, coated with Osmium [
The results presented are based on a novel sample preparation technique developed for TEM examination of ultrathin sections of UF resin. Although TEM has been widely used to examine ultrathin sections from a range of polymeric materials without embedding or after embedding in an embedding medium [5,9,15], UF resin has not been previously examined by TEM. This may be because UF resin becomes very hard and brittle upon curing. Although it has been possible to obtain ultrathin sections directly from polymeric materials in several TEM studies without the need for embedding them in an embedding medium [16-18], our initial attempt to trim pieces of thin UF resin films prepared for ultrathin sectioning was not successful, as the film was very brittle and turned powdery at the surface during trimming with a blade. Embedding UF resin films in Spurr’s resin for ultrathin sectioning also did not work, as the films were compact and un-penetrable by Spurr’s resin. The exact reason for resin compactness is not known; we assume that the release of water as a byproduct of reaction of urea with formaldehyde and its escape during resin curing may be responsible, as the resin is known to shrink greatly due to loss of water.
Knowing that it has been possible to obtain ultrathin sections from Spurr’s resin embedded wood tissues in contact with polyvinyl acetate (PVA) glue line in PVA bonded P. radiata boards [
There are no previous reports of TEM studies of UF resin, and the novel sample preparation method developed is enabling us to undertake a TEM imaging based comparison of the microstructure of UF resins differing in the proportions of formaldehyde to urea (FU mole ratios) and also curing methods, such as the level of hardener used to accelerate the curing process. Here we illustrate images from TEM examination of ultrathin sections cut through UF resin adhesive contained within the lumens of cells located close to and in contact with the adhesive line (
We are investigating the microstructure of UF resin of a range of FU mole ratios cured using different levels of the hardener (NH4Cl), but the illustrations presented are of the UF resin of only two FU mole ratios, selected to represent a low (FU mole ratio 1.2) and a high (FU mole ratio 1.4) mole ratio, that differ greatly in their micromorphological features. In the image depicted in
During curing, UF resin undergoes cross-linking reactions, and it is considered that higher mole ratio resins are more highly cross linked than lower mole ratio resins. The exact relationship of spherical particles to changes occurring at the molecular level during curing of different mole ratio UF resins is not fully understood. Presence of greater number of spherical particles in the 1.2 mole ratio UF resin than in 1.4 mole ratio resin suggests that there may be a link. Lower mole ratio UF resins are considered to be less cross linked than higher mole ratio UF resins, and this may be relevant in this regard. Our current work employing FE-SEM in combination with TEM to characterize the micromorphologies of liquid and
cured UF resins of different mole ratios and planned work involving high resolution chemical and physical characterization to understand the nano-architecture and molecular changes underlying the transformation of liquid to cured state UF resins may shed some light on the organization and functional relevance of the particulate phase of UF resin. In this regard, presence of greater amount of ordered crystallites in cured lower FU mole ratio UF resins than in higher mole ratio UF resins is of interest [
In conclusion, the novel sample preparation technique described made it possible to ultrathin section and examine for the first time cured UF resins by TEM, which will no doubt prove to be an important high resolution tool, filling the much needed gap in structural characterization in this area of work, that may be useful in developing formulations and processes to minimize formaldehyde emission from the UF resin in use as wood adhesive.
This work was supported by the Korean Ministry of Education, Science and Technology and the Korean Federation of Science and Technology Societies. This work was also supported by Basic Science Research Program through the National Research Foundation (NRF) of Korea funded by the Ministry of Education, Science and Technology (2011-0022112).