Open Access Library Journal
Vol.05 No.09(2018), Article ID:87695,6 pages

Preparation and Study of Dielectric and Electrical Conductivity of Ba5NdTi3V7O30 Ceramics

Jagatananda Panda1, Bana Bihari Mohanty2*, Priyadarshini Sanghamitra Sahoo3, Ram Naresh Prasad Choudhary4

1Department of Physics BIET, Bhadrak, India

2Department of Physics, Betnoti College Betnoti, Mayurbhanj, India

3Department of Physics, North Orissa University, Baripada, India

4Department of Physics I T E R, Bhubaneswar, India

Copyright © 2018 by authors and Open Access Library Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY 4.0).

Received: August 13, 2018; Accepted: September 27, 2018; Published: September 30, 2018


Ba5NdTi3V7O30 is a tungsten bronze structured ceramic sample, prepared by Solid State reaction route at high temperature (950˚C). The room temperature XRD analysis confirms orthorhombic crystal structure of the compound. Dielectric peak is observed at ~460˚C showing the transition of the compound from ferroelectric to paraelectric phase. Appearance of hysteresis loop confirms the existence of ferroelectric properties in the materials. Different values of activation energy in different temperature regions of the ac conductivity versus inverse absolute temperature graph exhibit mixed type of conduction process in the compound (i.e., ionic-polaronic and space charge generated from the oxygen ion vacancies).

Subject Areas:



Solid-State Reaction, X-Ray Diffraction, Dielectric Properties, Tungsten Bronze Structure

1. Introduction

Materials with various structural forms have always hypnotized the Materials researchers for their massive implementation in Scientific and industrial research. The development of nanoscience & technology enable a step forward to intensify the physical properties suitable for a broad field of challenging applications.

Materials with tungsten-bronze (TB) structure belong to family of dielectric materials, which exposes many exciting properties like ferroelectric, pyroelectric, piezoelectric, and nonlinear optical properties for various devices applications, such as transducers, actuators, capacitors, and ferroelectric random access memory [1]- [6].

The TB structure compose of a framework of distorted BO6 octahedral sharing corners with three different types of interstices (A, B and C) available for different array of cations filling in a general formula (A1)2(A2)4(C)4(B1)2(B2)8O30. The substitution of different ionic size at the above-mentioned sites plays significant role in tailoring various physical properties of the materials. This paper reports on the preparation and study of dielectric and electrical conductivity of Ba5NdTi3V7O30.

2. Experimental Details

2.1. Material Preparation

The polycrystalline compound Ba5NdTi3V7O30 (BNTV) was prepared using high purity (>99.9%) ingredients; BaCO3, Nd2O3, TiO2, V2O5 by Mixed Oxide Method. These materials were mixed in appropriate amount satisfying the stoichiometry of Ba3Sr2NdTi3V7O30, with formula;

5BaCO3 + 1/2Nd2O3 + 3TiO2 + 7/2V2O5 = Ba5NdTi3V7O30 + 5CO2

The ingredients were mixed in an agate mortar in air atmosphere for 3 h, followed by wet (methanol) condition to get homogeneous mixture. The mixture was then calcined in an alumina crucible starting from 700˚C in steps of 50˚C and was found to be calcined at an optimized temperature and time (950˚C, 12 h). This process was repeated till the formation of single-phase compound was confirmed by X-ray diffraction technique. After mixing the calcined powder with polyvinyl alcohol (PVA) as binder, cylindrical pellets of 10 mm diameter and 1 - 2 mm in thickness were made by a hydraulic press at a pressure of ~ 5 × 106 N/m2. The pellets were then sintered in an air atmosphere at an optimized temperature and time (950˚C, 12 h) The pellets were then polished to make their faces flat and parallel and finally coated with high purity conductive silver paint, and dried at 150˚C for 2 h before carrying out electrical measurements to make them moisture free.

2.2. Material Characterization

The structure of the material was studied from X-ray diffraction (XRD) and Scanning electron micrograph. The room temperature.XRD pattern of the material was obtained in a wide range of Bragg’s angle 2θ (20˚ ≤ 2θ ≤ 75˚) at a scanning speed of 3˚ min−1 by an X-ray diffractometer (Rigaku, Miniflex) with CuKα radiation (λ = 1.5405 Å) Using high-resolution scanning electron microscope (SEM: JOEL-JSM model: 5800F), the surface morphology of the sample was studied. The dielectric measurement was done in a wide range of temperature (33˚C - 500˚C) and frequency (100 Hz - 1 MHz), using a computer-controlled impedance analyzer (PSM 1735, model: N 4L). Then (P~E) hysteresis loop was recorded on the poled sample at room temperature using a high precision workstation (M/S-Radiant Technologies, Inc. USA).

3. Results and Discussion

3.1. Structural Analysis

The XRD pattern of the sample shown in Figure 1 confirms the formation of a single-phase new compound. The reflection peaks were indexed and the lattice parameters were determined in various crystal systems and with cell configurations using computer software “POWDMULT” [7]. A suitable orthorhombic unit cell with lattice parameters: a = 23.0868(26) Å, b = 4.2284(26) Å, c = 6.3899(26) Å were chosen. The crystallite size of the sample was evaluated from the broadening of the peaks (β1/2) using Scherrer’s equation [8]; P = Kλ/β1/2 cosθhkl, where K = constant = 0.89, k = 1.5405 Å and β1/2 = peak width of the reflection at half height. The crystallite size of the compound was observed to be 8 nm.

The room temperature scanning electron micrograph of the compound shown in Figure 1 (inset) resembles polycrystalline arrangement of the material with grains of irregular in shape and size distributed non-uniformly and densely over the entire surface of the sample. A similar microstructure is also observed in some of our materials of this family [9][10]. The grain size of the sample from histogram (Figure 1 (right)) was measured to be in the range of 220 nm.

3.2. Dielectric Analysis

The temperature dependent relative dielectric constant (εr) and loss tangent (tan δ) (inset) of Ba5NdTi3V7O30 compoundis shown in Figure 2 at some selected frequencies. Figure 2 describes the decreasing trend of both εr and tan δ (inset) with increase in frequency which is exhibited by polar dielectrics. The compound

Figure 1. Room temperature XRD pattern, SEM (inset) and histogram of Ba5NdTi3V7O30.

has a frequency independent dielectric anomaly at ~460˚C indicating the possible occurrence of ferroelectric-paraelectric phase transition. The value of εr is more at low frequencies confirms the presence of all types of polarization whereas at high frequencies it is mainly due to the contribution of electronic polarization [11].

The value of loss (tanδ) is observed to be low indicating good quality of the material. The value of tanδ is observed to be increased at higher temperature region (Figure 2 inset) caused by the intensifying conductivity for setting up of space charge polarization, and also due to trimming in ferroelectric domain wall’s contribution at high temperature [11].

3.3. Conductivity Study

The variation of a.c. conductivity (σac) as a function of inverse temperature at two different frequencies (50 kHz and 500 kHz) shown in Figure 3.

Figure 3 obeys the Arrhenius relation: σac = σ0 exp(−Ea/kBT), where the symbols have their usual meanings. The plot is divided into two distinct regions as I in high temperature and II in low temperature regions for both the frequencies. From calculation, the activation energy (Ea) are found to be 0.105 eV and 0.051

Figure 2. Variation of εr and tanδ (inset) with temperature of Ba5NdTi3V7O30 at some selected frequencies.

Figure 3. Variation of σac with 1000/T of Ba5NdTi3V7O30, at two selected frequencies.

eV in region-I and 0.5162 eV and 0.464 eV in region-II which are low and different and informs the existence of different conduction mechanisms. The small values of activation energy implies that little amount of energy is sufficient to activate the carriers for electrical conduction. Frequency independent dc conduction is confirmed from merging of the two curves at high temperature.

3.4. Hysteresis Study

The ceramics of this family have dielectric breakdown at even low electric field, the saturation polarization could not be observed at the given field; hence we could not get a proper hysteresis loop. The dielectric anomaly in the studied compounds is assumed to be related to ferroelectric-paraelectric phase transition. This assumption was confirmed by appearance of hysteresis loop as seen in Figure 4. Even with smaller remnant polarization the existence of ferroelectric properties in the compounds can be concluded.

Figure 4. Room temperature hysteresis loop of Ba5NdTi3V7O30.

4. Conclusion

The polycrystalline sample of BGTV ceramics is synthesized by solid-state reaction root. The formation of the compound is verified from XRD to form the orthorhombic tungsten-bronze structure. The compound has dielectric anomaly of ferroelectric to paraelectric type at 460˚C. The dielectric constant of the ceramics decreases with increasing frequency. The comparatively low room temperature dielectric constant indicates that these materials may have attractive benefits in electro-optic and infrared pyroelectric detector applications when grown in bulk single crystal or thin-film form. The temperature dependence of ac conductivity was found to obey Arrhenius equation. The activation energy of the compound was found to be different in different region indicating presence of different conduction mechanism. The remanent polarization is found out to be very small.


J. Panda acknowledges North Orissa University for the co-operation and help during his Ph.D. research work. The authors are thankful to Prof R.N.P. Choudhary, ex-Professor, Department of Physics, IIT Kharagpur, presently Prof. ITER, Bhubaneswar who had helped us and permitted us to use his laboratory during synthesis of compound and analysis of its properties.

Conflicts of Interest

The authors declare no conflicts of interest regarding the publication of this paper.

Cite this paper

Panda, J., Mohanty, B.B., Sahoo, P.S. and Choudhary, R.N.P. (2018) Preparation and Study of Dielectric and Electrical Conductivity of Ba5NdTi3V7O30 Ceramics. Open Access Library Journal, 5: e4834.


  1. 1. Zhang L.X., Chen, W. and Ren, X. (2004) Large Recoverable Electrostrain in Mn-Doped (Ba,Sr) TiO3 Ceramics. Applied Physics Letters, 85, 5658-5660.

  2. 2. She, W.L., Lee, K.K. and Lee, W.K. (2000) All Optical Quasi Steady-State Photorefractive Spatial Solitons. Physical Review Letters, 85, 2498-2501.

  3. 3. Lines, M.E. and Glass, A.M. (1977) Principles and Applications of Ferroelectrics and Related Materials. Clarendon Press, Oxford.

  4. 4. Jaffe, B., Cook, W.R. and Jaffe, H. (1971) Piezoelectric Ceramics. Academic Press, London.

  5. 5. Uchino, K. (1997) Piezoelectric Actuators and Ultrasonic Motors. Kluwer Academics, Boston.

  6. 6. Neurgaonkar, R.R., Kalisher, M.H., Lim, T.C., Staples, E.J. and Keester, K.L. (1980) Czochralski Single Crystal Growth of Sr.61Ba39Nb2O6 for Surface Acoustic Wave Applications. Materials Research Bulletin, 15, 1235-1240.

  7. 7. Wu, E. POWD, an Interactive Powder Diffraction Data Interpretation and Index Program, Ver.2.1, School of Physical Science, Flinders University South Bedford Park, Australia.

  8. 8. Klug, H.P. and Alexander, L.E. (1974) X-Ray Diffraction Procedures for Polycrystalline and Amorphous Materials. Willey-Interscience, New York.

  9. 9. Geiss, E.A., Scott, B.A., Burns, G., O’Kane, D.F. and Segmuller, A. (1969) Alkali Strontium-Barium-Lead Niobate Systems with a Tungsten Bronze Structure: Crystallographic Properties and Curie Points. Journal of the American Ceramic Society, 52, 276-279.

  10. 10. James, A.R., Priya, S., Uchino, K., Srinivas, K. and Kiran, V.V. (2002) Investigation of Intrinsic Defect Structure in 0.91Pb(Zn1/3Nb2/3)O3-0.09PbTiO3 Single Crystal through AC Conductivity. Japanese Journal of Applied Physics, 41, 5272-5276.

  11. 11. Jonscher, A.K. (1977) The Universal Dielectric Response. Nature, 267, 673-679.