ABSTRACT

In this research, polyethylene terephthalate bottles (PET) waste was added to styrene-butadiene rubber (SBR) to manufacture road bumps, as a technological procedure for recycling this PET waste, in order to maintain a clean and sustainable environment. Polyethylene terephthalate bottles were cut as grooved strips and added to bump SBR batch with various percentages (0 - 100 pphr). Mechanical tests were performed before and after the addition of PET waste including tensile strength, hardness, and resilience. Nanoparticles of carbon black, zinc oxide and sulfur were used, and compare the results with samples with micro particles additions. The result shows that the developed and manufactured bump SBR in this research conforms to the mechanical characteristics of the original bump model especially with nanoparticles additives, and the best results obtained with the nanoparticles additions.

Subject Areas:

Material Experiment

Keywords:

PET Waste, Road Bumps, SBR, Sustainable Environment

1. Introduction

A real revolution in the manufacturing of new compounds and materials occurs in the mid of the 20^th century, and the most important of all these materials was the production of plastic, which was used in all aspects of practical life due to its many advantages, including the ease of its formation and manufacturing. The global production of this important material has increased widely, which led researchers to call the last half of 20^th century as “plastic age”. However, although there are benefits of plastic, it was accompanied by many negative results, including the accumulation of millions of tons of waste of this material, which has a very long decay and it has devastating effects on the human health and all elements of the environment [1] [2] [3] [4] [5] .

Studies have shown that plastic wastes have a degradation life such as polyethylene, polyvinyl chloride, and many others can’t be treated like any other industrial waste, where they produce the most dangerous toxins and harmful gases when burned like dioxins and heavy metals which cause air, water, and soil pollution. Scientific research has shown that plastic materials cause a large number of health problems because they are basic components and additives during manufacturing and formation. One of the compounds involved in the manufacturing of plastic bottles is polyethylene terephthalate (PET), as well as Diethylhydroxylamine (DEHA), which both toxic compounds cause cancer if taken directly [6] [7] [8] [9] . In the case of exposure to these bottles to heat or washing and repeated use, the chemical granules, which are located in the walls of these bottles, will decompose and dissolve from the inner walls of the bottle and then be mixed with the foods. Therefore, these wastes must be recycled so as to ensure the safety of the environment and have economic feasibility [10] [11] [12] [13] [14] .

2. Materials and Methods

Materials: Styrene butadiene rubber (SBR); PET waste as grooved strips with 100 mm length and 2 mm width; carbon black as a nanoparticles (14 nm); Zinc oxide with (50 nm) nanoscale particles; Stearic acid 800, Dioctyl phthalate plasticizer (DOP); Antioxidant; Sulfur as a nanoparticles (55 nm); Wax-E as Lubricant; and Tetramethyl thiuram disulfide (TMTD) as accelerator. The percentage of materials is shown in Table 1. Two roll mills Comerio Ercole Busto Avsizo machine was used to for mixing materials and manufacturing of batch.

Testes and Samples Standards

1) Tensile Test: Tensometer T10 device was used to carry out tensile test according to the ASTM D412 standard by. The samples of this test have a circular cross-section with 6 mm diameter and 115mm length.

2) Hardness Test: Wallace bead load hardness instrument was used to accomplish this test. This test was done according to the ASTM D2240 standard. Hardness samples dimensions are 40 mm diameter and 4 mm thickness.

3) Resilience test: this test was done according to ASTM D1054 standard with the resilience tester. Samples are placed in the furnace for 30 minutes at 50˚C and then the test is performed.

4) Energy-dispersive X-ray spectroscopic micro-analyser (EDS): for PET has been done by Carl Zeiss EVO MA10 SEM, as shown in Figure 1.

3. Results and Discussion

One of the most important characteristics of rubber is that it can add 120% fillers due to its high elasticity. Figure 2 represents the hardness of road bumps as a function of PET waste content with nanoparticles and microparticles of C, ZnO and S additives. The hardness of rubber bump will increase after adding PET strips because these strips will act as a reinforcing material for rubber which will raise the value of its hardness. The hardness increases with the increase in the PET additions. When comparing the results obtained from the nanoparticles of C, ZnO and S additives and the results obtained with microparticles of C, ZnO, and S additives, we will see that the results obtained with nanoparticles are the best.

Figure 3 represents the tensile strength of road bumps as a function of PET waste content with nanoparticles and microparticles of C, ZnO and S additives. The tensile strength of rubber will decrease when the PET waste is added and this decrease continues with the increase in the PET content. This is due to the fact that the PET will be a weakness points in the structure of the rubber, which

is reflected on the tensile strength and causes weakening, and this state is normal for the solid additives. Also, we can observe that the results obtained with nanoparticles are better than microparticles results.

Figure 4 represents the resilience of road bumps as a function of PET waste content with nanoparticles and microparticles of C, ZnO and S additives. We can observe that the resilience value will decrease when adding PET waste and this decrease will be non-linear. Because these additions of the oxide lead to the formation of defects and gaps in the rubber structure and thus lead to a decline in resilience value. Also, the results obtained with nanoparticles are better than microparticles results.

4. Conclusions

Using of PET improves the hardness of SBR, but at the same time, the tensile strength and resilience have decreased at specific rates of PET addition. This change in properties was within the limits of international standards. As a result of the use of PET waste, the cost of manufacturing bumps has decreased significantly. Since the bumps manufactured in this research are a rubber material, it will have a longer operating life than the imported ones, which are manufactured from plastic instead of rubber. In addition, the environmental and health effects of PET waste can be eliminated because the rubber prevents PET from decomposing and it completely surrounds completely by rubber. The best results were obtained when adding nanoparticles of carbon black, zinc oxide and sulfur.

Cite this paper

Al-Mosawi, A.I. and Abdulsada, S.A. (2018) Technological Procedure for Recycling of PET Waste for Sustainable Environment Concept Achieve- ment. Open Access Library Journal, 5: e4327. https://doi.org/10.4236/oalib.1104327