Preparation, Characterization and in Vitro Evaluation of the Antitumor Activity of the Biologically Synthesized Silver Nanoparticles

Omama E. Elshawy1*, Eman A. Helmy2, Laila A. Rashed3

1Health Radiation Research Department, National Centre for Radiation Research and Technology (NCRRT), Atomic Energy Authority (AEA), Cairo, Egypt

2Regional Centre of Mycology and Biotechnology (RCMB), Al-Azhar University, Cairo, Egypt

3Medical Biochemistry Department, Faculty of Medicine, Cairo University, Cairo, Egypt

Copyright © 2016 by authors and Scientific Research Publishing Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY).

Received 14 March 2016; accepted 27 May 2016; published 30 May 2016


This study was concentrated on the biosynthesis of silver nanoparticles from Penicillium aurantiogresium (IMI 89372) with a focus on its cytotoxicity in MCF-7 and MCT cancer cell lines as well as Vero (normal) cell line that was assessed by crystal violet assay after treatment with various concentrations (0.44 ? 145 µg/ml) for 24 h. The cell morphology was examined by inverted light microscopy. Further, the radiosensitizing effect of silver nanoparticles (AgNPs) on MCF-7 was also demonstrated by assessing cell morphology, cell proliferation of MTT assay, LDH activity and induction of apoptosis through checking of some apoptotic genes that altered during carcinogenesis, including caspase-3, Bax and Bcl-2. Caspase-3 activity was also estimated. Synthesis of AgNPs was determined by UV-Visible spectrum and it was further characterized by TEM, FT-IR and X-Ray analysis (EDX, XRD). The biosynthesized AgNPs were spherical and of 12.7 nm in size as recorded by direct electron microscopy visualization. The biosynthesized AgNPs showed variation in cytotoxicity against MCF-7, MCT and Vero cell lines in a concentration dependant response with a varied degree of alteration in cell morphology. The result showed that AgNPs were highly toxic towards MCF-7 with IC50 value of 10.5 µg/ml. Treatment of MCF-7 (10.5 µg/ml) prior to irradiation improved the effect of irradiation dose (6 Gy) via increasing alteration of cell morphology, inhibition of cell proliferation, activation of the lactate dehydrogenase (LDH) and caspase-3 leading to induction of apoptosis which was further confirmed through increasing nuclear DNA damage and up regulation of caspase 3 and Bax genes and downrgulation of Bcl-2 genes. In conclusion, the present findings clearly indicated that AgNPs showed dose dependant cytotoxicity and verified that AgNPs acted as a potent radiosensitizer and could enhance gamma irradiation induced killing of MCF-7 breast cancer cells.


Penicillium aurantiogriseum, Silver Nanoparticles, in Vitro, Cytotoxicity, Radio-Sensitivity

1. Introduction

Numerous complications are associated with the use of conventional anticancer drugs, including insolubility in water, rapid clearance, and lack of selectivity, resulting in non-specific toxicity regarding normal cells and insufficient dose of drug delivered to the cancer cells [1] .

Nanobiotechnology is the most promising field for generating new kinds of nanomaterials for biomedical applications [2] . Because nano-particles (NPs) have the affinity to an acidic environment, which characterized tumor tissue, it is believed that selective targeting strategies with NPs facilitate more effective cancer detection and treatment with minimized side effects to normal cells [1] .

Various natural resources have been used for green synthesis of NPs: plants, plant products, bacteria, fungi, algae, yeast, and viruses [3] . The most commonly preferred method is using bacteria or fungi due to the fact that they are easy to handle, and the possible genetic manipulation [4] .

“Green synthesis” of nanoparticles makes use of environmental friendly, non-toxic and safe [5] . Silver nanoparticles are of particular interest for applications in medical devices and healthcare products because of their antibacterial activity and low toxicity to human cells.

AgNPs have gained much interest in the field of nanomedicine due to their unique properties and obvious therapeutic potential in treating a variety of diseases [6] and have a great potential in cancer management because they have selectivity involved in disruption of mitochondrial respiratory chain leading to the production of reactive oxygen species (ROS), induced the expression of genes associated with DNA damage, and enhanced apoptosis of tumor cells [7] . AgNPs induce cell damage in a dose- and size-dependent manner; a higher dose and a smaller size lead to increased cytotoxic effects [8] .

On the basis of the aforementioned, this study was designed to assess the cytotoxicity of the mycosynthesized AgNPs in MCF-7, HCT human cancer cells as well as the non-cancerous (Vero) normal cells. We also attempt to provide concentrated insight into AgNPs as a radio sensitizing agent.

2. Materials and Methods

2.1. Microorganisms

The Fungal type of Penicillium aurantiogresium (IMI 89372) strain used in this study and was kindly provided by the culture collection unit of the Regional Centre for Mycology and Biotechnology (RCMB), Al-Azhar University, Cairo, Egypt. The culture strain was maintained and sub cultured on malt extract agar (MEA) slants and plates containing; 20gm malt extract; 20 gm glucose; 1 gm peptone; 20 gm agar (Ingredients in one litre of distilled water).

2.2. Biomass Production and Biosynthesis of Silver Nanoparticles

The biomass of biosynthesized AgNPs was prepared previously [9] . In brief, the fungus was grown aerobically in a liquid medium containing (g/l) KH2PO4―7.0; K2HPO4―2.0; MgSO4―0.1; (NH4)2SO4―1.0; yeast extract―0.6; and glucose―10.0 (pH: 6.2 ± 0.2). The flasks were inoculated and incubated on orbital shaker at 25˚C and agitated at 150 rpm. The biomass were harvested after 72 hours of growth by sieving through Whatmann filter paper No.1 followed by extensive washing with distilled water to remove any undesired component from the biomass.

To prepare extracellular fungal cell-free extract for the synthesis of AgNPs, 20 g of fresh, clean fungal biomass was brought in contact with 100 ml of de-ionized water in an Erlenmeyer flask and incubated at 25˚C in dark shaking incubator (150 rpm) for 72 hours. After incubation, the cell filtrate was obtained by passing it through Whatmann filter paper no.1. For synthesis of silver nanoparticles, 50 ml AgNO3 (1 mM) was mixed with 50 ml of extracellular fungal cell-free extract in a 250 ml Erlenmeyer flask and agitated at 25˚C and pH 4.0 in the dark shaking incubator at 150 rpm for 72 hours. Two controls were used; first negative control containing only biomass without the silver ion, and second positive control containing 1 mM AgNO3 that run along with the experimental flasks.

The formation of silver nanoparticles was detected by turning the color of the mixture after incubation from light yellow to dark reddish brown. The reduction of silver ions was confirmed by qualitative testing of the supernatant by UV-visible spectrophotometer (Spectronic Milton Roy 1201 UV). 1 mM of AgNO3 was mixed with 50 ml of the cell filtrate in a 250 ml Erlenmeyer flask at 25˚C and pH 4 and agitated in the dark. Optical density was measured each 10 min starting of incubation until 72 hours and at different wavelength ranging from 200 to 800 nm and plotted the values on a graph.

2.3. Characterization of the Biosynthesized Silver Nanoparticles (AgNPs)

The characterization of silver nanoparticles was carried out according to Helmy and Mekawy (2013) using different instruments and techniques including visual observation, UV-Visible spectrophotometer, X-ray diffraction (XRD) of TEM, energy-dispersive X-ray (EDX) of SEM, Fourier transform infra-red (FT-IR) analysis and TEM.

2.3.1. UV-Visible Spectroscopy

The UV-Visible spectrophotometer has proved to be a very useful technique for the analysis of some metal nanoparticles and is a significant technique to authenticate the formation and stability of AgNPs in aqueous solution.

2.3.2. Transmission Electron Microscopy (TEM) and X-Ray Diffraction Analysis

Silver nanoparticles (AgNPs) size diameter and shape were reported and determined by Transmission Electron Microscopy (TEM JEOL 1010, Japan) and the crystalline AgNPs were determined by X-ray diffraction analysis using X-ray diffraction (XRD) of (XRD/TEM JEOL 1010, Japan). Samples for TEM were prepared by putting a drop of the AgNPs solution onto a conventional carbon coated copper TEM grid (400 meshes, Plano Gmbh, Germany), allowing the drop to dry overnight at room temperature before imaging. X-ray diffraction analyses as well as the TEM images of the samples were obtained using an accelerating voltage of 30 KV and 80 KV, respectively. At least three images of each sample were taken to have a clear representation of its morphology.

2.3.3. Scanning Electron Microscope (SEM) Analysis

For SEM imaging, a sample of a solution was placed on a carbon strip attached to an SEM brass support and dried at 50˚C for 5 min. The energy-dispersive X-ray (EDX) spectra (SEM/EDX, JSM-5500 LV JEOL, SEM, Japan) were used to examine the dimension, morphology, and chemical composition of the samples. Surface binding elements were analyzed with X-ray photoelectron spectroscopy. Silver nanoparticle which was excited by an electron beam showed the peak values of Ag element.

2.3.4. Fourier Transform Infra Red (FT-IR) Spectroscopy Analysis

The infrared analysis of the nanoparticles was performed on a Fourier transform infrared (FT-IR) spectrometer (IRPrestige-21®, German) to understand the protein―nanoparticle interaction and to identify the possible biomolecules which are responsible for reduction of Ag+ ion and capping of the bio-reduced nanoparticles synthesized by the fungal cells. Prior to analysis, the fungal filtrate containing nanoparticles was stirred at a speed of 5000 rpm for 10 min, and it was then washed with deionized water three times and air-dried. The dried samples were pressed into pellets. The sample pellets were placed into the sample holder and FT-IR spectra were recorded in the range of 450 - 4000 cm−1 at a resolution of 4 cm−1.

2.4. Determination of Nanoparticle Concentration

Accurate determination of the size and concentration of nanoparticles is essential for the biomedical application of nanoparticles and was determined according to the method previously reported [6] . The concentration of AgNPs to be administered at the level was determined by a method which has been previously reported. The calculation was as follows: Initially the average number of atoms per nanoparticles was calculated using the formula:

where N = number of atoms per nanoparticle, π = 3.14, ρ = density of face-centered cubic silver = 10.5g/cm3, D = average diameter of nanoparticles = 50 nm = 50 × 10−7 cm, M = atomic mass of silver = 107.868 g , NA = number of atoms per mole (Avogadro’s number = 6.023 × 1023).

Therefore, assuming 100% conversion of all silver ions to silver nanoparticles:

i.e., N = 3837233.003, then the molar concentration of the nanoparticle solution determined by

where; C =molar concentration of the nanoparticle solution, NT = total number of silver atoms added as AgNO3 =1 M, N =number of atoms per nanoparticle (from the calculation above), V =volume of the reaction solution in L, NA =Avogadro’s number (6.023 × 1023).

The required concentrations were thereafter made up from the obtained values.

2.5. Mammalian Cancer Cell Lines

Colon (HCT), breast (MCF-7) human cancer cell lines, and Vero (normal cell lines) were obtained from the tissue culture unit of the Holding Company for Biological Products and Vaccines (VACSERA), Giza, Egypt and supplied through the American Type Culture Collection (ATCC).

2.5.1. Subculture of Cell Lines

Cultures were viewed using an inverted microscope to assess the degree of confluence and to confirm the absence of bacterial and fungal contaminants. Cell monolayer washed with PBS using a volume equivalent half of the volume of culture medium. Trypsin/EDTA was added on to the washed cell monolayer using 1 ml per 25 cm² of surface area. The flask was rotated to merge the monolayer with Trypsin/EDTA. The flask was returned to the incubator and left for 2 - 10 minutes. The cells were examined using an inverted microscope (CKX41; Olympus, Japan) to ensure that all the cells were detached and floated.

2.5.2. Culture Media

The cells were cultured in a humid environment at 37˚C and 5% CO2 atmosphere in RPMI-1640 medium supplemented with Penicillin (100 IU/ml), Streptomycin (100 μg /ml) and 10% fetal bovine serum.

2.6. Irradiation Conditions

In order to investigate the enhancement the radiosensitivity of MCF-7 cell lines, the cells were exposed to AgNPs at a concentration of 10.5 μg/ml for 24hrs then exposed to 6 Gy irradiation at a dose rate of (0.657 Gy/minute) in the Canadian Gamma Cell-40 (137Cs) at the National Centre for Radiation Research and Technology (Cairo, Egypt).

2.7. Cytotoxicity Assay

Crystal violet assay as described previously [10] was applied to demonstrate the viability of MCF-7, HCT and Vero cell lines under the effect of silver nanoparticles (AgNPs). Briefly, cells were plated in 96-well culture plates and exposed to various concentrations (0.44, 0.88, 1.75, 3.5, 7.0 and14 μg/ml) of AgNPs. In addition to control untreated cells. All cultures were incubated for 24 hours at (37˚C, 5% CO2 in a humid atmosphere) in a humidified incubator. At the end of the incubation period, the plates were inverted or aspirated to remove the medium. The wells were washed with 100 µl of PBS. Finally, the dye was extracted from the cells by adding and mixing glacial acetic acid (33%) to the contents of each well. The absorbance was measured in triplicates at 490 nm using ELISA Reader system (SunRise TECAN, Inc., USA). The cytotoxicity was evaluated as crystal violet reduction end point. The survival percentage was calculated as the ratio of the percentage optical density according to the following equation:

The quantitative external morphology of exposed cells under the effect of AgNPs of 14 µg/ml concentration was analyzed using an inverted microscope (Leica, Germany) equipped with the digital microscopy camera to capture the images representing the morphological changes in MCF-7, MCT and Vero treated cell lines cells in relation to control cells.

2.8. Enhancing the Radiosensitivity of MCF-7 by Mycosynthesized AgNPs

The MCF-7 cell lines were selected to evaluate the potential effect of AgNPs to enhance the killing effect of radiotherapy. The cytotoxic activity of combined treatment with γ-ray irradiation and AgNPs in comparison to the cytotoxic effect of each treatment applied alone. Thus four sets of treatments were prepared. 1st is the negative untreated MCF-7 cells, 2nd is MCF-7 with 10.5 µg/ml AgNPs for 24 hrs. 3rd group: cells was exposed to 6 Gy of gamma rays alone at a dose rate of 0.675 Gy/sec. 4th group is the combined treatment, AgNPs was added to the cultures 24 hrs prior exposure to 6 Gy irradiation.

Cell morphology under the effect of different treatments was analyzed by the inverted microscopy as mentioned in the cytotoxicity set.

The radio sensitizing effect of AgNPs in MCF-7 cell lines was demonstrated in cellular and molecular levels via estimation of cell proliferation, membrane integrity (LDH assay), DNA fragmentation, caspase-3, Bax and Bcl-2.

2.8.1. Cell Proliferation Assay

Cell proliferation of MCF-7 cells of all groups was determined using the MTT (3-[4,5-dimethylthiazol-2-yl]-2.5- diphenyl tetrazolium bromide) cell proliferation kit (Trevigen Inc., Gaithersburg, MD, USA) as per manufacturer’s protocol. Briefly, cells were plated in 96-well tissue culture plates in a range of 103 - 105 cells/well in the presence or absence of AgNPs (10.5 μg/ml) in a final volume of 100 μL of medium and were allowed to attach overnight. The MTT reagent was added (10 μL per well) and the plate is incubated for 2 to 12 h to allow for intracellular reduction of the soluble yellow MTT to the insoluble purple formazan dye. Detergent reagent is added to each well to solubilize the formazan dye prior to measuring the absorbance of each sample in a microplate reader at 550 - 600 nm. Six wells were used for each group. The sham control (irradiated) group was assigned a value 100%. Inhibition of cell proliferation (%) of the treated cells (AgNPs + IRR) was determined relative to that of irradiated cells set as 100%. The results are presented as the mean ± standard error (SE) of three independent experiments.

2.8.2. LDH Assay

Lactate dehydrogenase (LDH) was assayed in the current investigation to evaluate the capability of AgNPs to enhance the IR induced membrane damage of MCF-7 cells with the leakage of LDH out of the cell. The radiosensitivity of MCF-7 was examined by quantitative measurement of the activity of LDH in the supernatant and compared with the IR treatment.

In brief, 50 μl of the culture supernatants from each well were transferred to the corresponding well in another microtitre plate. The LDH activity of the supernatant was measured by an LDH cytotoxicity detection kit, according to the manufacturer’s instructions (Takara Biochemicals, Otsu, Japan). The LDH activity was monitored by the reduction of a tetrazolium salt (yellow) to formazan (red). One hundred microlitres of diaphorase/β-nico- tinamide adenine dinucleotide (NAD+, oxidized form) dissolved in 2-(4-indophenyl)-3-(4-nitrophenyl)-5- phenyltetrazolium chloride/Na-lactate was added to each well, and the plate was incubated for 30 min at room temperature. After incubation, the absorbance was measured at wavelengths, 490 nm with microplate reader (Model 550, BioRad Laboratories, Hercules, CA, USA).

2.8.3. DNA Fragmentation Assay

To investigate the potential of AgNPs to enhance the radiosensitivity of MCF-7 to the IR dose induce internucleosomal DNA fragmentation, the standard method for DNA laddering assay [11] was performed. In brief, cells from each treated group were collected and then mixed with extraction buffer (10 mM/lTris-HCl [pH 8.0], 0.1 M/l EDTA [pH 8.0]) and 0.5% SDS, was first incubated for 1 hour at room temperature and then digested in the same buffer with 200 μg/ml proteinase K (Sigma) at 50˚C. An equal volume of phenol equilibrated with 1 mol/lTris buffer (pH 8.0) was then added, and the tubes were placed on a roller apparatus for 1 hour. After the two phases were separated by centrifugation at 5000 g for 30 minutes at room temperature, the viscous aqueous phases were transferred to clean tubes, and the extractions were repeated with an equal volume of phenol/chloroform. After the second extraction, the aqueous phase was transferred mannitol, 70 mM sucrose, 5 mM Hepes (MSH) buffer, pH 7.5. The extracted DNA was separated on agarose gel electrophoresis to assess fragmentation. The bands were visualized using a UV transilluminator of a gel documentation system (BIO-RAD, Gel Doc 2000).

2.8.4. Caspase Activity Assay

A Caspase-3 level was demonstrated in plasma using ELISA kit [Cat No. MBS261814] and according to manufacturer’s instruction provided with the kits.

2.8.5. Detection of Apoptotic Gene Expression by Real-Time Polymerase Chain Reaction (RT-PCR)

Apoptotic signalling genes include; Caspase-3, Bax and Bcl-2 were detected by RT-PCR. The housekeeping β-actin genes were used as internal control. Total RNA was extracted from each frozen sample using TRIzol® reagent (Invitrogen) according to a standard protocol. The isolated total RNA was converted into complementary DNA (cDNA) using Moloney murine leukemia virus (M-MLV) reverse transcriptase (Promega, Madison, USA).Real-time PCR was performed using an ABI 7500 Real-Time PCR System (Applied Biosystems, Foster City, CA, USA) and an SYBR® Green PCR Master Mix (Applied Biosystems) in a final volume of 10 µl with the following thermal cycling conditions: 95˚C for 10 min, followed by 40 cycles of 95˚C for 15 s and 60˚C for 1 min. The sequences of PCR primer pairs used for each gene are shown in Table 1. Data were analyzed with the ABI Prism sequence detection system software and quantified using the v1・7 Sequence Detection Software from PE Biosystems (Foster City, CA, USA). The relative expression of studying genes was calculated using the comparative threshold cycle method. All values were normalized to the β-actin genes as an invariant endogenous control (reference gene). The relative quantification was then calculated by the 2−∆∆Ct method.

2.9. Statistical Analysis

Statistical evaluation of the data was performed using one-way analysis of variance (ANOVA), one-way analysis of variances using the SPSS package program, version 14. The results were shown as mean ± SE and P < 0.05 accepted as the minimum level of significance.

3. Results

3.1. Characterization of the Biosynthesized Silver Nanoparticles (AgNPs)

Extracellular biosynthesis of silver nanoparticles by Penicillium aurantiogresium (IMI 89372) was carried out during this work. After incubation for 72 hours with sterilized deionized distilled water, the fungal biomass was separated by filtration. The fungal cell free filtrates incubated with silver ion at the beginning of the reaction. The flasks being incubated in the dark in an environmental shaker showed a gradual change and increasing in color intensity of the medium to brown during the incubation period. The result showed synthesis of silver nanoparticles of silver ions appeared in contact with the filtrate (Figure 1).

Table 1. The sequences of PCR primer pairs.

Figure 1. Culture filtrate with silver ions: (a) at the beginning of reaction and (b) after 72 h of reaction.

The change in color of the medium was noted by visual observation. The solution remained as hydrosol and no precipitation was observed. Control (without silver ion) showed no change in colour of the cell filtrate when incubated in the same environmental condition.

The present results revealed that the fungal isolate Penicillium aurantiogresium (IMI 89372) formed nanoparticles with silver nitrate in extra cellular filtrates.

In the current study, TEM micrograph of AgNPs was obtained at 25˚C and pH 4 as a control (directly from fungal filtered) and in 37˚C and pH 6.0 as an optimum conditions for the AgNPs biosynthesis process (Figure 2). The direct electron microscopic visualization allows measuring the size and shape of the silver nanoparticles formed. The micrograph showed nanoparticles with spherical in shape and measured 12.7 nm in size.

Silver nanoparticles from the all used fungal extracts have been characterized using XRD by various investigators. The size of silver nanoparticles can also be determined by laser diffraction. Selected area electron diffraction (SAED) spots that corresponded to the (from inside to outside of the central ring) planes of the face- centered cubic (FCC) structure of elemental silver are clearly seen in Figure 3(a). The silver particles formed can be achieved by measuring the XRD-spectrum of the samples. X-ray diffraction occurred to confirm the crystalline nature of the nano-particle and the XRD pattern obtained has been represented in Figure 3(b). The XRD pattern showed intense peaks in the whole spectrum of 20 values ranging from 20 to 80.

Currently, FTIR measurements of AgNPs were carried out after 24 h of incubation with the fungus to identify the possible biomolecules responsible for the reduction of the Ag+ Ions and capping of the bio-reduced AgNPs synthesized by fungal filtrate. Representative spectra of obtaining nanoparticles manifests absorption peaks located at about 1045, 1245, 1299, 1361, 1377, 1488, 1550, and 1631 in the region 1000 - 1800 cm−1. The FTIR spectra reveal the presence of different functional groups like C?N, C?O?C, amide linkages, 1400 to 1700 cm−1 region provides information about the presence of “C=O“ and “N?H“ groups, these may be between amino acid residues in polypeptides and protein in synthesized silver nanoparticles and give rise to well-known signatures in the infrared region of the electromagnetic spectrum (Figure 4(a)).

Energy dispersive X-ray spectrum (EDX) analysis shows the peak in the silver region confirming presence of elemental silver. The optical absorption peak is observed approximately at 3 KeV, which is typical for the absorption of metallic silver nanocrystalline due to surface plasmon resonance, from this we confirmed the presence of nanocrystalline elemental silver (Figure 4(b)).

3.2. Mycosynthesized AgNPs Induced Dose Dependant Cytotoxicity

In the present investigation the cytotoxicity of the biologically synthesized sliver NPs using Penicillium aurantiogresium (IMI 89372) was evaluated under in vitro conditions in MCF-7, HCT and Vero cell lines. This was assessed in term of cell viability by crystal violet assay for 24 hour in human cancer cells MCF-7 and HCT as well as in the normal Vero cell lines using concentrations ranging from 0.44 µg/ml to14 µg/ml. Depending on AgNPs concentration, a significant differential cytotoxic effect was testified towards the examined cells. The results showed that the synthesized AgNPs was found to be potentially cytotoxic against MCF-7 and MCT cell lines. However, MCF-7 viability were significantly inhibited by AgNPs agent with IC50 value 10.5 µg/ml of the concentration and MCT cells with IC50 12.3 µg/ml of the concentration. The results also demonstrated that the sensitivity of the two cancer cell lines examined in the current work was higher than that of Vero cell lines (IC50 77.4 µg/ml) (Figure 5).

Figure 2. TEM micrograph of synthesized silver nanoparticles (scale bar: 50 nm) from tested fungal extracts measured 12.7 nm.

(a) (b)

Figure 3. (a) & (b) Selected area electron diffraction (XRD) showing the characteristic crystal planes of elemental silver from all fungal extracts used in the present study.


Figure 4. (a) FT-IR spectrum and (b) Energy-dispersive X-ray spectrum (EDX).

Figure 5. Cytotoxic activity of AgNPs on MCF-7, HCT and Vero cell lines as assayed by crystal violet method. The values are the mean of three separate trials ± SE.

3.3. Cellular Morphology Analysis

The morphological changes of MCF-7, HCT and Vero cell lines were analyzed using inverted microscope after incubation with the highest concentration of AgNPs (14 µg/l) used in the current investigation for 24 hr. Both MCF-7 and HCT cancer cells showed profound morphological changes characteristic of cytotoxicity. The cells appeared aggregated, irregular in shape, detached from the substratum and floating in their culture media. Moreover, the cells showed typical apoptotic features characterized by chromatin condensation close to the nuclear envelope, associated with cytoplasmic vacuolization. These morphological changes are less pronounced in Vero cells (Figure 6).

3.4. Silver Nanoparticles (AgNPs) Mediated Radiosensitivity of MCF-7 Cancer Cells

To determine whether AgNPs enhanced the therapeutic effect of radiotherapy and resulted in better cytotoxic effect than radiotherapy alone, the cytotoxic effect of combined treatment with γ-irradiation and AgNPs was evaluated in comparison with the cytotoxic effect of irradiation treatment alone. The cells were treated with AgNPs of 10.55 µg/ml concentration for 24 hr then irradiated with 6 Gy. The radiosensitizing effect of AgNPs in MCF-7 cells was demonstrated 24 hours post irradiation exposure through a demonstration of its antiproliferating effect (MTT assay), cell membrane integrity (via LDH release) and DNA damage as well as apoptotic gene expression (caspase-3, Bax and Bcl-2) as well as caspase activity.

3.5. MTT Assay

The MTT assay implies that incubation of MCF-7 cell lines with AgNPs (10 µg/ml) caused significant (P < 0.01) inhibition of cell proliferation (65.5 ± 2.6) and to (65.2 ± 5.7) when irradiation treatment applied alone (P < 0.01), Mean while, combination of AgNPs with IR increased the inhibition of cell proliferation (P < 0.001) compared to control set. It is worth of mentioning that the combined treatment caused a pronounced increase in inhibition of cell proliferation compared to irradiation treatment alone (P < 0.05) (Figure 7).

3.6. LDH Assay

3.7. DNA Fragmentation in MCF-7 Cell Lines

3.8. Caspase-3 Activity in MCF-7 Cell Lines

Figure 6. In vitro cytotoxicity of AgNPs. Microscopic photographs of the tested cell lines: cells were treated with or without AgNPs (14 µg/ml) for 24 hours using an inverted microscope at ×40 magnification.

Figure 7. Radiosensitizing effect of AgNPs on cell proliferation in MCF-7 cells. The results represent the means of three separate experiments ± the mean of standard error. Treated groups showed statistically significant differences from the control group at ***P < 0.001, **P < 0.01.AgNPs+IR showedstatistically significant differences from the IR group at aP < 0.05.

Figure 8. Radiosensitizing effect of AgNPs in MCF-7 cells as indicated by LDH activity. The results represent the means of three separate experiments ± the mean of standard error. Treated groups showed statistically significant differences from the control group at ***P < 0 .0 01, **P < 0. 01. AgNPs +IR showedstatistically significant difference from the IR group at aP < 0. 05.

M 1 2 3 4

Figure 9. An agarose gel electrophoresis show the DNA fragmentation pattern which was monitored in different studied groups. Apoptotic strand breaks/streaking DNA was observed in the treated groups (2, 3 & 4) and minimal apoptotic breaks in group 1 (cancer untreated cells).

Figure 10. Radiosensitizing effect of AgNPs on caspase-3 activity in MCF-7 cells. The results represent the means of three separate experiments ± the mean of standard error. Treated groups showed statistically significant differences from the control group at ***P< 0 .0 01, **P< 0. 01. AgNPs+IRR showedstatistically significant differences from the IR group at aP< 0. 01.

3.9. Expression of Apoptotic Genes in MCF-7Cell Lines

3.10. Radiosensitizing Effect of AgNPs and Cellular Morphology Analysis

Furthermore, the radio sensitizing effect of AgNPs on cellular morphology was also demonstrated upon treatment with IC50 of silver NPs (10.5 µg/ml) alone, IR treatment (6 Gy) alone and the combination of both. The photographs (Figure 12) showed that control (without treatment with AgNPs or radiation), the tumor cell was composed of sheets or cords of irregularly sized and shaped cells with no tendency to keratinization. Mitotic figures were commonly encountered and the tumor cells were clearly surrounded by the stroma (Figure 12(a)).

Figure 11.Radiosensitizing effect of AgNPs on the expression of the apoptotic gene Bax and anti apoptotic gene Bcl-2 in MCF-7 cell lines. The results represent the means of three separate experiments ± the mean of standard error. Treated groups showed statistically significant differences from the control group at ***P < 0 .001.AgNPs+IR showedstatistically significant differences from the IR group at aP< 0. 01.

(a) (b)(c) (d)

Figure 12. Radio sensitizing effect of AgNPs on cellular morphology. Microscopic photographs of (a): untreated MCF-7 cell lines and (b): cells treated with AgNPs (10.5µg/ml) for 24 hour alone; (c) cells treated with 6 Gy irradiation alone and (d) cells treated with the combination of both, using inverted microscope at ×40 magnifications.

The cells were gradually keratinized after treatment with AgNPs occasionally showing malignant squamous pearls (Figure 12(b)). The individual cell keratinization and cancer pearls were more prominent after treatment with either AgNPs or radiation (Figure 12(b) and Figure 12(c)).

After treatment with both, almost all the tumor cells were degenerated to necrosis, with only a pearl-like structure and very few cellular elements remaining remarkable nuclear hypochromasia were enmeshed within the fibrous stroma (Figure 12(d)).

4. Discussion

Lactate dehydrogenase (LDH) is a soluble cytosolic enzyme, which is released into the extracellular medium due to membrane damage consequently lead to apoptosis. Thus the content of AgNPs induced cytotoxicity was determined quantitatively by measuring measuring the activity of LDH in the supernatant as an indirect method [19] . LDH leakage into culture supernatant was measured in MCF-7 cells treated with AgNPs and/or irradiation to determine cell membrane damage. Moreover, we examined whether AgNPs enhanced irradiation induced MCF cell death through augmenting of irradiation?induced the membrane leakage. In this study, the LDH activity in the medium was significantly higher in cells treated with the sole AgNPs or IR treatment alone compared to the untreated control cells. In close relationship with our results, other investigators reported that AgNPs significantly affect the cell membrane integrity and caused LDH leakage in a concentration dependent manner and after 24 hour of AgNPs exposure in liver rat cells and in L929 fibroblasts [32] [33] . Furthermore it has been evidenced that IR-induced apoptotic cell death was most likely associated release of LDH [34] .

It is worth mentioning that, in combined treatment AgNPs enhanced the cytotoxicity of MCF-7 cells to the radiation dose and caused more killing of cells than that observed in the sole AgNPs and irradiation treatments. In line with our results, other studies emphasized that PEG-GNPs could enhance the therapeutic sensitivity in breast cancer EMT-6 cells [34] . Also, Zhang et al. [35] evidenced the radiosensitizing effect GSH- and BSA- GNPs in HeLa cells. They attributed this effect to the enhanced DNA damaging effect induced by the photoelectric effect and Compton scattering of the heavy metal.

Apoptosis is a well-recognized cell death mechanism in cancer treatment, through which cytotoxic agents kill tumor cells [31] . DNA considered as one of the important characteristics of cell death. Radiotherapy and chemotherapy are important integral parts of breast cancer treatment which result in DNA damage and can lead to apoptotic death [36] . In the present investigation, the MCF-7 cell lines were treated with the sole treatments of AgNPs (10.5 µg/ml), irradiation (6 Gy) and their combination (AgNPs + IRR) for 24 hr. DNA was then extracted from cell lysate followed by detection by agaros gel.

The laddering pattern showed DNA fragments in MCF-7 cells treated with AgNPs alone or irradiation by itself. Adding strengthen to the fact, more pronounced fragmented DNA ladders was observed after applying the AgNPs combined with irradiation (IR) therapy, suggesting that AgNPs enhanced IR induced apoptotic cell death. In close relationship with our findings, other studies have been reported that when cancerous cell lines treated with AgNPs exhibited formation of DNA ladder [37] and resulted in DNA damage [38] caused induction of oxidative stress [39] .

These results were further confirmed by the morphological analysis of the treated cells (Figure 12) which revealed that the cells were shrunken, irregular in size, detached from the substratum and became floated in the culture media which appeared greater after exposure to the combined therapy. All these observation of the cell morphology emphasized induction of apoptosis and appeared in a good correlation with our results evidenced by MTT assay, LDH leakage assay and DNA laddering pattern. The results could be explained as a result of the production of ROS and the subsequent induction of oxidative stress which play an important role in cell injury which lead to DNA damage and consequently apoptotic cell death [7] [18] [40] See comment in PubMed Commons below.

In the same line with these results, many investigators demonstrated that AgNPs resulted in DNA oxidative damage suggesting AgNPs mediate ROS-induced genotoxicity and play important role in AgNPs-induced toxicity [41] . Moreover, Zhang and colleagues reported that γ-radiation can be absorbed directly by DNA, leading to ionization of both the nucleobases and sugars, directly generating DNA damage [35] .

Caspase-3 is known to be the major effector of the apoptotic machinery and plays an important role in the apoptotic pathway [20] . To investigate whether apoptosis is mediated by caspase-3, was demonstrated its mRNA level and caspase-3 activity at the biochemical level after treatment with the sole AgNPs (10.5 µg/ml), irradiation alone (6 Gy) or in combination.

Regulation of caspases as well as Bax, and Bcl-2 gene expression considered to be of the important regulatory mechanisms of cell apoptosis [46] . In the current study, an inverse relationship between the Bax and Bcl-2 gene expression was noticed under the effect of each of the sole treatments of AgNPs (10.5 µg) and irradiation (6 Gy) and the combined treatment with AgNPs plus irradiation. However, the Pro-apoptotic Bax gene expression was significantly increased and showed that Bax and Bcl-2 gene expression are regulated differently with AgNPs alone and irradiation alone. More pronounced alteration of these genes expression was noticed after the combined treatment. The results suggest the radiosensitizing effect of AgNPs enhanced radiation induced up regulation of Bax and down regulation of Bcl-2 cell, thereby increasing the cell killing effect beyond either of the sole treatments alone. The results also, pointed to that the expression of these genes might be responsible for the control of the apoptotic cell death.

Our observations are in consistent with studies demonstrated that AgNPs have been reported to possess radiation dose-enhancement effects on different human cancer cell, including MGC-803 [31] , U-231 breast cancer cells [47] and A549 lung cancer cells [48] . Liu and co-workers found that AgNPs treatment followed by radiotherapy resulted in antiproliferative and proapoptotic effect [30] . Colasanti and Co workers explained the enhancing effect of AgNPs to the radiation dose. They evidenced that combination of cytotoxic agent could enhance the dose of ionizing radiation to generate an additive effect that could be more useful in reduction of the therapeutic dose of radiation to obtain the same therapeutic effect [51] .

5. Conclusion

In the present study, we have successfully synthesized and prepared stable, spherical AgNPs of 12.7 nm in size using the fungus Penicillium aurantiogresium (IMI 89372) which is green, environmentally friendly, cost effective, and rapid method for synthesis of AgNPs. The prepared AgNPs showed cell type specific cytotoxicity and could reduce cell viability in a dose dependent manner with significant morphological changes in MCF-7 and HCT cancer cells. AgNPs were more cytotoxic towards MCF-7 than MCT cell lines. These observations are less prominent in Vero cell lines. Based on our results, the combination of AgNPs and irradiation treatment could enhance gamma irradiation induced killing of MCF-7 cancer cells by inhibiting proliferation of the cells, increasing of LDH and caspase-3 activity and alteration of caspase-3, Bax and Bcl-2 genes expression. The radiosensitizing effect could be endorsed to the synergistic effect of free radicals induced by the combination of irradiation and AgNPs that increased the oxidative stress and induced apoptotic cell death. Further systemic and comparative studies are required to achieve the best in vivo radiosensitizing effect with a focus on the exact underlying molecular mechanisms.

Cite this paper

Omama E. Elshawy,Eman A. Helmy,Laila A. Rashed, (2016) Preparation, Characterization and in Vitro Evaluation of the Antitumor Activity of the Biologically Synthesized Silver Nanoparticles. Advances in Nanoparticles,05,149-166. doi: 10.4236/anp.2016.52017


  1. 1. Yu, M.K., Park, J. and Jon, S. (2012) Targeting Strategies for Multifunctional Nanoparticles in Cancer Imaging and Therapy. Theranostics, 2, 3-44.

  2. 2. Chen, X. and Schluesener, H.J. (2008) Nanosilver: A Nanoproduct in Medical Application. Toxicology Letters, 176, 1-12.

  3. 3. Thakkar, K.N., Mhatre, S.S. and Parikh, R.Y. (2010) Biological Synthesis of Metallic Nanoparticles. Nanomedicine, 6, 257-262.

  4. 4. Parikh, R.Y., Singh, S., Prasad, B.L., Patole, M.S., Sastry, M. and Shouche, Y.S. (2008) Extracellular Synthesis of Crystalline Silver Nanoparticles and Molecular Evidence of Silver Resistance from Morganella sp.: Towards Understanding Biochemical Synthesis Mechanism. ChemBioChem, 9, 1415-1422.

  5. 5. Kilin, D.S., Prezhdo O.V. and Xia, Y. (2008) Shape-Controlled Synthesis of Silver Nanoparticles: Ab Initio Study of Preferential Surface Coordination with Citric Acid. Chemical Physics Letters, 6, 113-116.

  6. 6. Sriram, M.I., Kanth, S.B., Kalishwaralal, K. and Gurunathan, S. (2010) Antitumor Activity of Silver Nanoparticles in Dalton’s Lymphoma Ascites Tumor Model. International Journal of Nanomedicine, 5, 753-762.

  7. 7. AshaRani, P.V., Hande, M.P. and Valiyaveettil, S. (2009) Anti-Proliferative Activity of Silver Nanoparticles. BMC Cell Biology, 10, 65.

  8. 8. Zhang, X.F., Choi, Y.J., Han, J.W., Kim, E., Park, J.H., Gurunathan, S. and Kim, J.H. (2015) Differential Nanoreprotoxicity of Silver Nanoparticles in Male Somatic Cells and Spermatogonial Stem Cells. International Journal of Nanomedicine, 10, 1335-1357.

  9. 9. Kathiresan, K., Manivannan, M.A. and Nabeel, B. (2009) Studies on Silver Nanoparticles Synthesized by a Marine Fungus, Penicillium fellutanum Isolated from Coastal Mangrove Sediment. Colloids and Surfaces B: Biointerfaces, 71, 133-137.

  10. 10. Mosmann, T. (1983) Rapid Colorimetric Assay for Cellular Growth and Survival: Application to Proliferation and Cytotoxicity Assays. Journal of Immunological Methods, 65, 55-63.

  11. 11. Siu, P.M. and Always, S.E. (2005) Mitochondria-Associated Apoptotic Signalling in Denervated Rat Skeletal Muscle. The Journal of Physiology, 565, 309-323.

  12. 12. Ahmad, A, Mukherjee, P., Senapati, P., Mandal, D., Khan, M.I. and Kumar, R. (2003) Extracellular Biosynthesis of Silver Nanoparticles Using the Fungus Fusarium oxysporum. Colloids and Surfaces B: Biointerfaces, 28, 313-318.

  13. 13. Bharde, A., Rautaray, D., Bansal, V., Sanyal, M. and Sastry, M. (2006) Extracellular Biosynthesis of Magnetite Using Fungi. Small, 2, 135-141.

  14. 14. Ahmad, A., Senapati, M. and Sastry, M. (2003) Extracellular Biosynthesis of Monodispersed Gold Nanoparticles by a Novel Extermophillic Actinomycete, Thermonospora sp. Langmuir, 19, 3550-3553.

  15. 15. Swathi, G., Sridevi, A., Sandya, A., Praveen, B. and Narasimha, G. (2014) Biosynthesis, Characterization and Antibacterial Activity of Silver Nanoparticles by Soil Fungi Pencillium sps. International Journal of Drug Delivery, 6, 165-171.

  16. 16. Sukirtha, R., Priyanka, K.M., Antony, J.J., et al. (2012) Cytotoxic Effect of Green Synthesized Silver Nanoparticles Using Melia azedarach against in Vitro HeLa Cell Lines and Lymphoma Mice Model. Process Biochemistry, 47, 273- 279.

  17. 17. Dziedzic, A., Kubina, R., Buldak, R.J., Skonieczna, M. and Cholewa, K. (2016) Silver Nanoparticles Exhibit the Dose-Dependent Anti-Proliferative Effect against Human Squamous Carcinoma Cells Attenuated in the Presence of Berberine. Molecules, 21, 365.

  18. 18. Franco-Molina, M.A., Mendoza-Gamboa, E., Sierra-Rivera, C.A., Gómez-Flores, R.A., Zapata-Benavides, P., Castillo-Tello, P., Alcocer-González, J.M., Miranda-Hernández, D.F., Tamez-Guerra, R.S. and Rodríguez-Padilla, C. (2010) Antitumor Activity of Colloidal Silver on MCF-7 Human Breast Cancer Cells. Journal of Experimental & Clinical Cancer Research, 29, 148.

  19. 19. Gurunathan, S., Han, J.W., Eppakayala, V., Jeyaraj, M. and Kim, J.H. (2013) Cytotoxicity of Biologically Synthesized Silver Nanoparticles in MDA-MB-231 Human Breast Cancer Cells. BioMed Research International, 2013, Article ID: 535796.

  20. 20. Jeyaraj, M., Sathishkumar, G., Sivanandhan, G., MubarakAli, D., Rajesh, M., Arun, R., Kapildev, G., Manickavasagam, M., Thajuddin, N., Premkumar, K. and Ganapathi, A. (2013) Biogenic Silver Nanoparticles for Cancer Treatment: An Experimental Report. Colloids and Surfaces B: Biointerfaces, 106, 86-92.

  21. 21. Park, S., Lee, Y.K., Jung, M., Kim, K.H., Chung, N., et al. (2007) Cellular Toxicity of Various Inhalable Metal Nano- particles on Human Alveolar Epithelial Cells. Inhalation Toxicology: International Forum for Respiratory, 19, 59-65.

  22. 22. Hess, L.K., Jones, L., Schlager, J.J., et al. (2008) Unique Cellular Interaction of Silver Nanoparticles: Size-Dependent Generation of Reactive Oxygen Species. Journal of Physical Chemistry B, 112, 13608-13619.

  23. 23. Kulandaivelu, B. and Gothandam, K.M. (2016) Cytotoxic Effect on Cancerous Cell Lines by Biologically Synthesized Silver Nanoparticles. Brazilian Archives of Biology and Technology, 59, e16150529.

  24. 24. Liu, W., Wu, Y., Wang, C., Li, H.C., Wang, T., Liao, C.Y., Cui, L., Zhou, Q.F., Yan, B. and Jiang, G.B. (2010) Impact of Silver Nanoparticles on Human Cells Effect of Particle Size. Nanotoxicology, 4, 319-330.

  25. 25. Foldbjerg, R., Olesen. P., Hougaard, M., Dang, D.A., Hoffmann, H.J. and Autrup, H. (2009) PVP-Coated Silver Nanoparticles and Silver Ions Induce Reactive Oxygen Species, Apoptosis and Necrosis in THP-1 Monocytes. Toxicology Letters, 190, 156-162.

  26. 26. Lee, I.J. and Seong, J.S. (2011) Radiosensitizers in Hepatocellular Carcinoma. Seminars in Radiation Oncology, 21, 303-311.

  27. 27. McGinn, C.G., Shewach, D.S. and Lawrence, T.S. (1996) Radiosensitizing Nucleotides. Journal of the National Cancer Institute, 88, 1193-1203.

  28. 28. Swanner, J., Mims, J., Carroll, D.L., Akman, S.A., Furdui, C.M., Torti, S.V. and Singh, R.N. (2015) Differential Cytotoxic and Radiosensitizing Effects of Silver Nanoparticles on Triple-Negative Breast Cancer and Non-Triple-Negative Breast Cells. International Journal of Nanomedicine, 10, 3937-3953.

  29. 29. Maeda, K., Chung, Y.S., Takatsuka, S., Ogawa, Y., Sawada, T., Yamashita, Y., Onoda, N., Kato, Y., Nitta, A. and Arimoto, Y. (1995) Tumor Angiogenesis as a Predictor of Recurrence in Gastric Carcinoma. Journal of Clinical Oncology, 13, 477-481.

  30. 30. Liu, P.D., Huang, Z.H., Chen, Z., Xu, R., Wu, H., Zang, F., Wang, C. and Gu, N. (2013) Silver Nanoparticles: A Novel Radiation Sensitizer for Glioma? Nanoscale, 5, 11829-11836.

  31. 31. Huang, P., Yang, D.P., Zhang, C., Lin, J., He, M., Bao, L. and Cui, D. (2011) Protein-Directed One-Pot Synthesis of Ag Microspheres with Good Biocompatibility and Enhancement of Radiation Effects on Gastric Cancer Cells. Nanoscale, 3, 3623-3626.

  32. 32. Hussain, S.M., Hess, K.L., Gearhart, J.M., Geiss, K.T. and Schlager, J.J. (2005) In Vitro Toxicity of Nanoparticles in BRL 3A Rat Liver Cells. Toxicology in Vitro, 19, 975-983.

  33. 33. Park, M.V., Neigh, A.M., Vermeulen, J.P., de la Fonteyne, L.J., Verharen, H.W., Briedé, J.J., van Loveren, H. and de Jong, W.H. (2011) The Effect of Particle Size on the Cytotoxicity, Inflammation, Developmental Toxicity and Genotoxicity of Silver Nanoparticles. Biomaterials, 32, 9810-9817.

  34. 34. Sohn, D., Essmann, F., Schulze-Osthoff, K. and Janicke, R.U. (2006) P21 Blocks Irradiation-Induced Apoptosis Downstream of Mitochondria by Inhibition of Cyclin-Dependent Kinase-Mediated Caspase-9 Activation. Cancer Research, 66, 11254-11262.

  35. 35. Zhang, X.D., Chen, J., Luo, Z., Wu, D., Shen, X., Song, S.S., et al. (2014) Enhanced Tumor Accumulation of Sub-2 Nm Gold nanoclusters for Cancer Radiation Therapy. Advanced Healthcare Materials, 3, 133-141.

  36. 36. Elmore, S. (2007) Apoptosis: A Review of Programmed Cell Death. Toxicology Pathology, 35, 495-516.

  37. 37. Kalishwaralal, K., Deepak, V., Pandian, S.R.K., et al. (2010) Biosynthesis of Silver and Gold Nanoparticles Using Brevibacterium casei. Colloids and Surfaces B: Biointerfaces, 77, 257-262.

  38. 38. Hsin, Y.H., Chen, C.F., Huang, S., Shih, T.S., Lai, P.S. and Chueh, P.J. (2008) The Apoptotic Effect of Nanosilver Is Mediated by a ROS- and JNK-Dependent Mechanism Involving the Mitochondrial Pathway in NIH3T3 Cells. Toxicology Letters, 179, 130-139.

  39. 39. Lim, D.H., Jang, J., Kim, S., Kang, T., Lee, K. and Choi, I.H. (2012) The Effects of Sub-Lethal Concentrations of Silver Nanoparticles on Inflammatory and Stress Genes in Human Macrophages Using cDNA Microarray Analysis. Biomaterials, 33, 4690-4699.

  40. 40. Kim, S. and Ryu, D.Y. (2013) Silver Nanoparticle-Induced Oxidative Stress, Genotoxicity and Apoptosis in Cultured Cells and Animal Tissues. Journal of Applied Toxicology, 33, 78-89.

  41. 41. Kim, J.S., Sung, J.H., Ji, J.H., Song, K.S., Lee, J.H., Kang, C.S., et al. (2011) In Vivo Genotoxicity of Silver Nanoparticles after 90-Day Silver Nanoparticle Inhalation Exposure. Safety and Health at Work, 2, 34-38.

  42. 42. Satyavani, K., Gurudeeban, S., Ramanathan, T. and Balasubramanian, T. (2011) Biomedical Potential of Silver Nanoparticles Synthesized from Calli Cells of Citrullus colocynthis (L.) Schrad. Journal of Nanobiotechnology, 9, 43.

  43. 43. Zhang, Y., Guo, J., Qi, Y., Shao, Q. and Liang, J. (2014) The Prevention of Radiation-Induced DNA Damage and Apoptosis in Human Intestinal Epithelial Cells by Salvianic Acid A. Journal of Radiation Research and Applied Sciences, 7, 274-285.

  44. 44. Taylor, R.C., Cullen, S.P. and Martin, S.J. (2008) Apoptosis Controlled Demolition at the Cellular Level. Nature Reviews Molecular Cell Biology, 9, 231-241.

  45. 45. Reed, J.C. (1999) Bcl-2 Family Proteins. In: Hickman, J.A. and Dive, C., Eds., Apoptosis and Cancer Chemotherapy, Humana Press, Totowa, 99-116.

  46. 46. Koike, T., Yang, Y., Suzuki, K. and Zheng, X. (2008) Axon and Dendrite Degeneration: Its Mechanisms and Protective Experimental Paradigms. Neurochemistry International, 52, 751-760.

  47. 47. Lu, R., Yang, D., Cui, D., Wang, Z. and Guo, L. (2012) Egg White-Mediated Green Synthesis of Silver Nanoparticles with Excellent Biocompatibility and Enhanced Radiation Effects on Cancer Cells. International Journal of Nanomedicine, 7, 2101-2107.

  48. 48. Ma, J., Xu, R., Sun, J., Zhao, D., Tong, J. and Sun, X. (2013) Nanoparticle Surface and Nanocore Properties Determine the Effect on Radiosensitivity of Cancer Cells upon Ionizing Radiation Treatment. Journal of Nanoscience and Nano- technology, 13, 1472-1475.

  49. 49. Sanpui, P., Chattopadhyay, A. and Ghosh, S.S. (2011) Induction of Apoptosis in Cancer Cells at Low Silver Nanoparticle Concentrations Using Chitosan Nanocarrier. ACS Applied Materials and Interfaces, 3, 218-228.

  50. 50. Su, X.Y., Liu, P.D., Wu, H. and Gu, N. (2014) Enhancement of Radiosensitization by Metal-Based Nanoparticles in Cancer Radiation Therapy. Cancer Biology & Medicine, 11, 86-91.

  51. 51. Azarova, A.M., Lyu, Y.L., Lin, C.P., Tsai, Y.C., Lau, J.Y.N., Wang, J.C. and Liu, L.F. (2007) From the Cover Roles of DNA Topoisomerase II Isozymes in Chemotherapy and Secondary malignancies. Proceedings of the National Academy of Sciences of the United States of America, 104, 11014-11019.


*Corresponding author.