Journal of Materials Science and Chemical Engineering
Vol.1 No.3(2013), Article ID:35297,6 pages DOI:10.4236/msce.2013.13001
Study of Sodium-Chromium-Iron-Phosphate Glass by XRD, IR, Chemical Durability and SEM
1Hassan II University of Casablanca, Faculty of Science, High Energy and Condensed Matter Lab, Casablanca, Morocco
2Hassan II University of Casablanca, Faculty of Science, Mineral chemistry Lab, Casablanca, Morocco
Email: *youssefmakhkhas@gmail.com, *hassayout@yahoo.fr, said_aq@yahoo.fr
Copyright © 2013 Youssef Makhkhas et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Received May 13, 2013; revised June 19, 2013; accepted June 30, 2013
Keywords: Chemical Durability; IR Spectroscopy; Scanning Electron Microscopy; Phosphate Glasses; XRD
ABSTRACT
Chromium iron phosphate glass was investigated for use as waste form because of its improved chemical durability. The introduction of chromium in sodium-iron-phosphate glass is used to compare its effect with iron in inhibition of corrosion. The sodium-chromium-iron phosphate glass of composition 10Na2O-30Fe2O3-5Cr2O3-55P2O5 (mol%) was produced by melting batches of (99, 98% pure) Cr2O3, Fe2O3, Na2CO3, and (NH4)2HPO4 at 1080˚C for one hour and pouring the liquid into steel mold. The sample was annealed at 680˚C for 48 h. We have performed the measurement of X-Ray Diffraction (XRD), Scanning Electronic Microscopy (SEM), Infra-Red spectroscopy (IR), and the chemical durability. The IR of the glass studied, contains two dominant bands, which were characteristic of pyrophosphate groups, (P-O) stretching mode of P-O non bridging oxygen at 1055 cm−1 and sym stretching mode of bridging oxygen at 444 cm−1 respectively. There is also a band at 603 cm−1 attributed to isolated tetrahedral units (PO4)3−. The chemical durability of the glass was investigated by measuring the weight loss in distilled water at 90˚C for 22 days.
1. Introduction
Phosphate glasses are of particular interest in both technological and scientifical fields because they generally have lower processing temperatures less than 1000˚C, lower glass transition temperatures (Tg) [1-6], and higher thermal expansion coefficients (α) than silicate glasses in the range of 90 to 250 × 10−7/˚C [4-6]. These properties makes them a good candidates in many applications such as glass to metal seals, thick film paste, the molding of optical elements, low temperature enamels for metals [2-4]. However, their relatively poor chemical durability makes them unsuitable for practical applications [7-9]. It was reported [9-15] that the introduction of oxides such as SnO, PbO, ZnO, Cr2O3 and Fe2O3, results in the formation of Sn-O-P, Pb-O-P, Zn-O-P, P-O-Cr and P-O-Fe bonds, and leads to improvement in the chemical durability of the modified phosphate glasses.
The iron phosphate glasses have generally both excellent chemical durability and low melting temperature typical between 950 and 1100˚C, [16]. Chromium phosphate glasses for the immobilisation and disposal of nuclear waste were reported in 1984 [17]. The combination of chromium phosphate glass with various types of simulated nuclear waste showed that it is possible to have a waste form with a corrosion rate more slowly than that one of a comparable borosilicate glass. Therefore it has been suggested that the chemical durability of sodiumchromium-iron phosphate glasses is attributed to the replacement of P-O-P bonds by P-O-Cr and P-O-Fe bonds. The presence of P-O-Fe bands in higher concentrations, makes the glass more hydration resistant [16,18-21]. The P-O-Cr bands seem to play the same role than P-O-Fe bands [22].
In this paper we present a study of sodium chromium iron phosphate glass 10Na2O-30Fe2O3-5Cr2O3-55P2O5 which is prepared by the melt quenching technique, and characterized by X-Ray Diffraction, Infra-Red spectroscopy, and Scanning Electronic Microscopy. The chemical durability was investigated in distilled water solution.
2. Experimental
The glass of composition 10Na2O-30Fe2O3-5Cr2O3-55 P2O5 (mol %) is obtained by the melting quench method in 1080˚C. Appropriate mixture of mixing compounds Na2CO3, ferric oxides, Cr2O3 and (NH4)2HPO4 were initially tempered at various temperatures between 300˚C - 500˚C to achieve a preparation before the glass preparation.
The melt was achieved in alumina crucibles for about 30 mn at 1080˚C ± 10˚C. The isolated glasses samples have an approximate of size 10 mm diameter and 3 mm in thickness. The vitreous state was first evidenced from the shiny aspect and then confirmed from XRD patterns. Annealing of this glass was realized at 680˚C for 48 hours. The first structural approach was made using X-rays diffraction which allowed to following. The density of the glass was measured at room temperature using the helium pycnometry method. The chemical durability sample of the size 0.9 × 0.9 × 0.9 × 0.3 cm was used sample were first polished to a 400 grit finished with SiC paper, then they were immersed in a flask filled with 100 ml of distilled water at 90˚C for a time of 22 days. The dissolution rate (DR) was then determined from the weight loss during the aqueous treatment at 90˚C. The infrared (IR) spectra for each glass were measured between 400 and 1600 cm−1 using mX−1 and NIC-3600 FTIR spectrometers. The sample was prepared by pressing a mixture of about 2 mg of glass powder and 100 mg of anhydrous KBr powder. The chemical of composition of the analysed glass is given in Table 1.
2.1. X-Ray Diffraction, and Density
No crystalline phase was detected by X-ray in the glass composition 10Na2O-30Fe2O3-5Cr2O3-55P2O5, whereas we notice that there is the existence of crystalline micro domain which means that the crystallization of the glass had just started, this observation comes from apearence of some peaks related to the crystalline phase NaFeP2O7 (Figure 1(a)). The XRD pattern of annealed glass (Figure 1(b)) shows more crystallization peaks of the same phase, this result might confirm that the glass structure could be composed by NaFeP2O7 pyrophosphates groups.
2.2. Infrared Spectroscopy Study
The infrared spectra shown in Figure 2, for the glass of composition 10Na2O-30Fe2O3-5Cr2O3-55P2O5 include two dominant bands. These bands are characteristics of pyrophosphate groups: the band at 1099 and 760 cm−1 are attributed to (PO3)1 − asymmetric stretching mode of non bridging oxygen (P-O-P) sym stretching mode of bridging oxygen, respectively [22-25]. The band at 992 cm−1 seems to be assigned to the isolated tetrahedral units (PO4)3− [26-28].
2.3. SEM Microscopy Study
We noticed that the SEM plots (Figures 3(a) and (b)) for both glasses before and after aqueous dissolution confirms the presence of all the elements forming the glass. The proportions of the constituents seem as well to be in accordance with the theoretical composition.
The microscopic photograph was made at the nanometrical scale (as shown in Figures 4(a) and (b)).
The surface of the glass before the aqueous attack
Table 1. bench composition, calculated (O/P) ratio, DR and density of the glass studied.
(a)(b)
Figure 1. (a) X-ray diffraction spectra for the sample 10Na2O-30Fe2O3-5Cr2O3-55P2O5; (b) X-Ray diffraction pattern for 10Na2O-30Fe2O3-5Cr2O3-55P2O5 glass partially crystallized at 650˚C for 48 h.
appears to be homogeneous in comparision with the attacked one which shows a deteriorated zone on its surface. Taking in consideration the dimension of the photographs, the etched surface remains very small.
3. Dissolution Rate
The dissolution rate (DR) for sodium-lead-iron-phosphate glass is a function of time (see Figure 5). The dotted line indicates the dissolution rate of the glass which is included for comparison. Experimental dissolution rate for lead-iron-phosphate glass were reported by Day and et al. [29]. In the present work the dissolution rate for 10Na2O- 30Fe2O3-5Cr2O3-55P2O5 glass decreases as the time of immersion in water increases. This decrease is observed in this type of glass because in the early stage the solution is still dilute, and the increase of glass leaching product has a relatively minor effect upon the rate of reaction.
4. Discussion-Correlation between the Structure and the High Durability of Iron Phosphate Glasses
Both XRD and IR techniques have confirmed the structural evolution of the glass network towards the pyrophosphate. So the structure of sodium-chromium-iron phosphate glass can be considered as pyrophosphate units connected with ferric and ferrous ions in octahedral or distorted octahedral coordination [30]. The chemical durability of sodium-chromium-iron phosphate glass of composition 10Na2O-30Fe2O3-5Cr2O3-55P2O5 (regarding aqueous attack at 90˚C) is attributed to the increasing number of Fe-O-P bonds in the glass [30,31]. Such bonds are expected to be more water resistant than the P-O-P and Na-O-P bands [32]. This glass have a (DR) 50 times less than the DR of window glass and ~150 times less than the DR for BABAL glass which have been considered as alternative materials for the immobilization of nuclear waste substance [32,33].
5. Conclusion
The structure and the chemical durability of sodiumchromium-iron phosphate glass of composition 10Na2O- 30Fe2O3-5Cr2O3-55P2O5 (mol%) have been investigated using various techniques such IR, XRD, SEM....
The structure of the 10Na2O-30Fe2O3-5Cr2O3-55P2O5 (mol%) glass can be considered as pyrophosphate units
Figure 2. The IR spectra of sodium-chromium-iron-phosphate glass.
(a)(b)
Figure 3. (a) The SEM plot for the sample glass 10Na2O-30Fe2O3-5Cr2O3-55P2O5 (before aqueous attack); (b) The SEM plot for the sample glass 10Na2O-30Fe2O3-5Cr2O3-55P2O5 (after aqueous attack).
(a)(b)
Figure 4. (a) Microscopic photograph of the surface of the glass 10Na2O-30Fe2O3-5Cr2O3-55P2O5, before aqueous attack (Resolution of 50 µm); (b) Microscopic photograph of the surface of the glass 10Na2O-30Fe2O3-5Cr2O3-55P2O5, after 22 days of aqueous attack.
Figure 5. Dissolution rate for sodium chromium iron phosphate glassas a function of immersion time in aqueous solution at 90˚C.
connected with chromium. This glass have a (DR) ~200 times less than the DR for BABAL glass which have been considered as alternative materials for the immobilization of nuclear waste substance. This result is very important for applications in the nuclear waste management. The improved chemical durability is attributed to the replacement of the easily hydrated Na-O-P and P-O-P bonds by corrosion resistant Fe-O-P and Pb-O-P bands. The recorded IR spectra indicate that these glasses are dominated by (P2O7)4− dimmer units, and contain a large number of Fe-O-P bonds.
The studied glass possesses a strong chemical durability. This can be used in many domains, especially in the vitrification of nuclear wastes which represents a clean alternative to the traditional way of burying hazardous wastes in isolated lands.
6. Acknowledgements
The authors wish to thank National Center for Scientific and Technical Research [Division of Technical Support Unit for Scientific Research (TSUSR) Rabat, Morocco] for helpful discussions. The present work is supported by the Laboratory of Physics of High Energy and Condensed Matter, and Laboratory of Inorganic Chemistry (University Hassan II, Faculty of Sciences Ain Chock).
REFERENCES
- L. M. Sanford and P. A. Tick, US Patent 4.314.031, 1982.
- P. Y. Shih, S. W. Yung and T. S. Chin, “Thermal and Corrosion Behavior of P2O5-Na2O-CuO Glasses,” Journal of Non-Crystalline Solids, Vol. 224, No. 2, 1998, pp. 143- 152. doi:10.1016/S0022-3093(97)00460-2
- P. Y. Shih, S. W. Yung, C. Y. Chen, H. S. Liu and T. S. Chin, “The Effect of SnO and PbCl2 on Properties of Stannous Chlorophosphate Glasses,” Materials Chemistry and Physics, Vol. 50, No. 1, 1997, pp. 63-69. doi:10.1016/S0254-0584(97)80185-X
- T. Y. Wei, Y. Hu and L. G. Hwa, “Structure and Elastic Properties of Low-Temperature Sealing Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 288, No. 1-3, 2001, pp. 140-147. doi:10.1016/S0022-3093(01)00612-3
- H. Niida, M. Takahashi, T. Uchino and T. Yoko, “Preparation and Structure of Organic-Inorganic Hybrid Precursors for New Type Low-Melting Glasses,” Journal of Non-Crystalline Solids, Vol. 306, No. 3, 2002, pp. 292- 299. doi:10.1016/S0022-3093(02)01188-2
- H. S. Liu, P. Y. Shih and T. S. Chin, “Thermal, Chemical and Structural Characteristics of Erbium-Doped Sodium Phosphate Glasses,” Physics and Chemistry of Glasses, Vol. 37, 1996, p. 227.
- M. R. Reidmeyer, M. Rajaram and D. E. Day, “Preparation of Phosphorus Oxynitride Glasses,” Journal of NonCrystalline Solids, Vol. 85, No. 1-2, 1986, pp. 186-203. doi:10.1016/0022-3093(86)90090-6
- H. Yung, P. Y. Shih, H. S. Liu and T. S. Chin, “Nitridation Effect on Properties of Stannous-Lead Phosphate Glasses,” Journal of the American Ceramic Society, Vol. 80, No. 9, 1997, pp. 2213-2220. doi:10.1111/j.1151-2916.1997.tb03110.x
- J. L. Rygel and C. G. Pantano, “Synthesis and Properties of Cerium Aluminosilicophosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 355, No. 52-54, 2009, pp. 2622-2629. doi:10.1016/j.jnoncrysol.2009.09.004
- P. A. Bingham and R. J. Hand, “Sulphate Incorporation and Glass Formation in Phosphate Systems for Nuclear and Toxic Waste Immobilization,” Materials Research Bulletin, Vol. 43, No. 7, 2008, pp. 1679-1693. doi:10.1016/j.materresbull.2007.07.024
- S. Ray, X. Fang, M. Karabulut, G. K. Marasinghe and D. E. Day, “Effect of Melting Temperature and Time on Iron Valence and Crystallization of Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 249, No. 1, pp. 1- 16. doi:10.1016/S0022-3093(99)00304-X
- P. Y. Shih and T. S. Chin, “Preparation of Lead-Free Phosphate Glasses with Low Tg and Excellent Chemical Durability,” Journal of Materials Science Letters, Vol. 20, No. 19, 2001, pp. 1811-1813. doi:10.1023/A:1012551603964
- C. M. Shaw and J. E. Shelby, “Effect of Lead Compounds on the Properties of Stannous Fluorophosphate Glasses,” Journal of the American Ceramic Society, Vol. 71, No. 5, 1988, pp. C252-C253. doi:10.1111/j.1151-2916.1988.tb05071.x
- I. W. Donald, “Preparation, Properties and Chemistry of Glassand Glass-Ceramic-To-Metal Seals and Coatings,” Journal of Materials Science, Vol. 28, No. 11, 1993, pp. 2841-2886. doi:10.1007/BF00354689
- A. Šantić and A. Moguš-Milanković, “Charge Carrier Dynamics in Materials with Disordered Structures: A Case Study of Iron Phosphate Glasses,” Croatica Chemica Acta, Vol. 85, No. 3, 2012. doi:10.5562/cca1989
- S. Aqdim, H. El Sayouty, B. Elouad and J. M. Greneche, “Chemical Durability and Structural Approach of the Glass Series (40-y) Na2O-yFe2O3-5Al2O3-55P2O5-by IR, X-Ray Diffraction and Mössbauer Spectroscopy,” IOP Conference Series: Materials Science and Engineering, Vol. 28, 2012, Article ID:012003.
- B. C. Sales and L. A Batner, “Lead-Iron Phosphate Glass: A Stable Storage Medium for High-Level Nuclear Waste,” Sciences, Vol. 226, No. 4670, 1984, pp. 45-48. doi:10.1126/science.226.4670.45
- B. Kumar and S. Lin, “Redox State of Iron and Its Related Effects in the CaO-P2O5-Fe2O3 Glasses,” Journal of the American Ceramic Society, Vol. 74, No. 1, 1991, pp. 226-228. doi:10.1111/j.1151-2916.1991.tb07322.x
- S. T. Reis, M. Karabulut and D. E. Day, “Chemical Durability and Structure of Zinc-Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 292, No. 1-3, 2001, pp. 150-157. doi:10.1016/S0022-3093(01)00880-8
- T. Jermoumi, M. Hafid and N. Toreis “Density, Thermal and FTIR Analysis of (50-x)BaO.xFe2O2·50P2O5 Glasses,” Physics and Chemistry of Glasses—European Journal of Glass Science and Technology Part B, Vol. 43, No. 3, pp. 129-132.
- S. Aqdim, “Identification et Etudes Thermique et Electrique des Phases vitreuses des Systèmes Ternaires Li2OM2O3-P2O5 (M= Cr, Fe),” 1990.
- S. T. Reis, D. L. Faria, J. R. Martinelli, W. M. Pontuschka, D. E. Day and G. S. M. Partiti, “Structural Features of Lead Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 304, No. 1-3, 2002, pp. 188-194. doi:10.1016/S0022-3093(02)01021-9
- S. Cai, W. J. Zhang, G. H. Xu, J. Y. Li, D. M. Wang and W. Jiang, “Microstructural Characteristics and Crystallization of CaO-P2O5-Na2O-ZnO Glass Ceramics Prepared by Sol-Gel Method,” Journal of Non-Crystalline Solids, Vol. 355, No. 4-5, 2009, pp. 273-279. doi:10.1016/j.jnoncrysol.2008.11.008
- R. K. Brow, D. R. Tallant, S. T. Myers and C. C. Phifer, “The Short-Range Structure of Zinc Polyphosphate Glass,” Journal of Non-Crystalline Solids, Vol. 191, No. 1-2, 1995, pp. 45-55. doi:10.1016/0022-3093(95)00289-8
- S. T. Reis, M. Karabulut and D. E. Day, “Structural Features and Properties of Lead-Iron-Phosphate Nuclear Wasteforms,” Journal of Nuclear Materials, Vol. 304, No. 2-3, 2002, pp. 87-95. doi:10.1016/S0022-3115(02)00904-2
- C. R. Rambo, L. Ghussn, F. F. Senc and J. R. Martinelle, “Manufacturing of Porous Niobium Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 352, No. 32-35, 2006, pp. 3739-3743. doi:10.1016/j.jnoncrysol.2006.03.104
- H. Doweidar, Y. M, Moustafa, K. EL-Egili and I. Abbas, “Infrared Spectra of Fe2O3-PbO-P2O5 Glasses,” Vibrational Spectroscopy, Vol. 37, No. 1. 2005, pp. 91-96. doi:10.1016/j.vibspec.2004.07.002
- C. S. Ray, X. Fang, M. Karabulut, G. K. Marasinghe and D. E, Day, “Effect of Melting Temperature and Time on Iron Valence and Crystallization of Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 249, No. 1, 1999, pp. 1-16. doi:10.1016/S0022-3093(99)00304-X
- A. Mogus-Milankovic, A. Santic, S. T. Reis, K. Furic and D. E. Day, “Mixed Ion-Polaron Transport in Na2O-PbOFe2O3-P2O5 Glasses,” Journal of Non-Crystalline Solids, Vol. 342, No. 1-3, 2004, pp. 97-109. doi:10.1016/j.jnoncrysol.2004.07.012
- J.S. Brooks, G.L. Williams and D.W. Allen; Phys. Chem. Glasses 33 (1992) 171.
- X. Yu, D. E. Day, G. J. Long and R. K. Brow, “Properties and Structure of Sodium-Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 215, No. 1, 1997, pp. 21-31. doi:10.1016/S0022-3093(97)00022-7
- S. T. Reis, M. Karabulut and D. E. Day, “Chemical Durability and Structure of Zinc-Iron Phosphate Glasses,” Journal of Non-Crystalline Solids, Vol. 292, No. 1-3, 2001, pp. 150-157. doi:10.1016/S0022-3093(01)00880-8
- G. Malow, W. Lutze and R. C. Ewing, “Alteration Effects and Leach Rates of Basaltic Glasses: Implications for the Long-Term Stability of Nuclear Waste Form Borosilicate Glasses,” Journal of Non-Crystalline Solids, Vol. 67, No. 1-3, 1984, pp. 193-205. doi:10.1016/0022-3093(84)90156-X
NOTES
*Corresponding authors.