Composites were obtained in the in SiC-SiAlON and Al 2O 3-SiAlON system. Physical-chemical processes going on at the obtaining of SiALON within the range of 800 °C - 1500 °C were studied. Charge compositions and sintering regime were selected. It was proved that X-SiALON was obtained at the sintering of kaolin-aluminum powder at 1500 °C, while β-SiALON was formed at the sintering of SiC-Aluminum powder, silicium and Al 2O 3-aluminum powder, silicium at 1500 °C. Corrosion properties of the materials were studied. Investigations were performed by the methods of X-Ray structural and microscopical analysis.
Intense progress of science and technology demands perfection of various branches of industry, which in its turn is connected with the necessity of creation of new materials characterized by hetero modular properties. Taking into consideration practical experience in materials science, an advantage of carbides, borides, nitrides and silicides over other type materials were proved, since hardly melted materials are distinguished by precious properties such as: high refraction, corrosion resistance to a number of aggressive media, high mechanical characteristics, specific electro and heat-physical properties and others [
Among the oxygen-free hardly melted materials silicium carbide- and silicium nitride-based materials are distinguished, which by their unique physical-technical and chemical properties are widely used in modern technology: machine-building, chemical, atomic energy, petroleum refining industries et al. [
Intense work is in progress in recent years in the sphere of obtaining types of ceramics in which properties of oxygen-free substances and oxygen substances will be fused and SiALON are namely such materials [
Our work pursued to obtain SiALON-containing composites by reactive sintering on the basis of silicium carbide and corundum. This method enables us to obtain desirable phase composition material and such materials possess properties of the hot-pressed objects. In the process of obtaining SiALONs by reaction sintering, sintering temperature is sharply decreased at the application of active materials.
In our case we had to select materials which would enable us to use newly formed components obtained by the method of reactive sintering, since at the obtaining of solid solution of SiALON, inculcation of a-Al2O3 and AlN in β-Si3N4 is especially simplified when its crystalline lattice is still in the process of formation. Therefore we gave preference to silica-alumina materials―kaolin, aluminium powder and elemental silicium.
Kaolin, aluminium powder, silicium, silicium carbide, aluminium oxide were used as starting materials, and manganese and yttrium oxides, pearlite and refractory clay were used as additives. Blend compositions are given in
Specimens were made of cylindrical form, size d-15 mm, by semi-dry molding method, molding pressure was 20 MPa. After drying, it was sintered in a furnace by one hour standing at the final temperature. Device for sintering for the specimens consisted of a furnace equipped with silicium carbide heaters, mark TK 30/200.
A device for silicium specimens sintering (
We have studied physical-chemical properties of specimens sintered at 1500˚C (
To investigate physical-chemical processes taking place at SiALONs obtaining, the specimens were sintered in 800˚C - 1500˚C temperature interval and the investigation was carried out by X-Ray diffraction analysis. X-Ray patterns are given on
X-Ray diffraction analysis of sintered SN-1 specimens was carried out at 800˚C - 1500˚C by 100˚C interval.
Composite index | Initial component composition, mass. % | ||||||||
---|---|---|---|---|---|---|---|---|---|
kaolin | Al | Al2O3 | SiC | Si | Pearlite, Armenia | Y2O3 | MgO | Polog clay, Ukraine | |
SN-1 | 80.00 | 20.00 | |||||||
SN-2 | 20.00 | 10.00 | 70.00 | ||||||
SN-3 | 20.00 | 10.00 | 70.00 | ||||||
SN-6 | 18.52 | 18.52 | 18.52 | 18.52 | 20.37 | 2.78 | 1.85 | 0.92 | |
SN-7 | 13.89 | 23.15 | 27.78 | 25.00 | 2.78 | 1.85 | 0.92 | 4.63 | |
SN-8 | 13.89 | 23.15 | 27.78 | 25.00 | 2.78 | 1.85 | 0.92 | 4.63 |
Composite index | Open porosity w, % | Hardness limit at compaction, MPa | Density, ρ, g/sm3 | Chemical resistance, % | |
---|---|---|---|---|---|
Water | Sulfuric acid, ρ = 1.84 | ||||
SN-1 | 16.2 | 230 | 2.28 | 99.41 | 99.15 |
SN-2 | 15.0 | 245 | 2.8 | 99,41 | 99.16 |
SN-3 | 16.0 | 240 | 3.2 | 99.36 | 99.15 |
SN-6 | 15.0 | 256 | 2.25 | 99.82 | 99.20 |
SN-7 | 15.2 | 258 | 2.31 | 99.79 | 99.25 |
SN-8 | 15.4 | 254 | 2.78 | 99.80 | 99.30 |
X-Ray pattern at 800˚C shows clearly cut diffraction maximums characteristic to aluminium, silicium and quartz. dhkl: aluminium-2.338; 2.025; 1.62; 1.432 Å. silicium-3.53; 3.13; 2.45; 1.817 Å. quartz-3.34; 4.25; 2.454; 1.817 Å. As it was expected SiO2 was isolated as a result of destruction of kaolin while silicium was formed as a result of alumothermal reaction via the following reaction:
At 900˚C - 1000˚C temperature interval peaks characteristic to aluminium and SiO2 are sharply decreased, new phases are formed as a result of interaction of ALN and ALON nitrogen and aluminium. dhkl: aluminium- 2.34; 2.025; 1.438 Å. Quartz-3.34; 4.25; 2.454; 1.817 Å. ALN-2.714 Å. ALON-1.985; 1.397 Å. 1000˚C dhkl: SiO2-4.25; 3.34; 2.280; 2.546 Å. Si-3.13; 3.53; 1.817 Å. ALN-2.714; 2.437; 1.402; 1.397 Å. ALON-2.383; 1.985; 1.385 Å.
At 1100˚C - 1200˚C interval, intensity of aluminium diminishes and intensity of ALN and ALON increases. Intensity of SiO2. sharply decreases. At 1200˚C, there are no peaks of Si and SiO2. Peaks characteristic to mullite appear. 1100˚C dhkl: aluminium-2.38 Å; SiO2-4.25; 3.335; 1.824 Å; Si-3.13; 1.824 Å; ALON-1.983; 1.39 Å. ALN-2.704; 2.48; 2.39; 1.56; 1.406; 1.411; 1.32 Å; mullite-5.33; 3.44; 3.395 Å. 1200˚C dhkl: ALN-2.734; 2.700; 2.46; 2.383; 1.548; 1.435; 1.418; 1.334 Å; mullite-5.45; 3.43; 3.395; 2.885; 2.546; 2.295; 2.208; 1.899; 1.990; 1.824; 1.705; 1.530 Å; ALON-1.993 Å.
At 1300˚C - 1400˚C (
and peak characteristic to Si3N4 is not observed. The same picture is seen at 1500˚C, which refers to the fact that at 1300˚C X-SiALON of mullite structure was formed [
At 1000˚C - 1100˚C new phases were formed: ALN and ALON, while at 1100˚C-mullite. At all other temperatures phase formation proceeded by the scheme similar to that of SN-1, but with less intensity, depending on the composition. Thus silicium carbide composite with X-SiAlON binder is obtained (
On the grounds of the obtained results, to obtain SiC and a-AL2O3-containing SiALON composites, we introduced into charge composition, metallic silicium, silicium carbide in smaller amount and a-AL2O3 (
The main phase at the SN-7 X-ray pattern is β-SiALON. The composite alongside with B-SiALON consists of silicium varbode; it contains X-SiALON in trace quantity.
SN-8 composite, similar to the above referred composites consists of β-SiAlON and the introduced a-AL2O3.
Results of microstructure analysis (
SN-1 composite is presented mainly by X-SiALON phase, in which particles of Si3N4 are inserted as inclusions. Lattice of SN-6 composite is β-SiALON with silicium carbide and corundum grains spread in it. SN-7 composite lattice is analogous to that of SN-6, in which silicium carbide grains of the size exceeding that of new- formed silicium nitride are clearly visualized. Lattice of SN-8 composite contains of the very β-SiALON with a-AL2O3 crystals. This figure shows pores which are presented in quantity in this composite.
Chemical and phase compositions of the materials are also reflected in their electric characteristics. If we compare the results obtained by investigation of four various composition materials we’ll observe clearly the difference between them. Material obtained on the base of kaolin (80 mass%) and aluminum powder (20 mass%) (SN-1), in which SiALON and mullite were fixed as leading phases, are distinguished by the highest specific electrical resistance (in wide temperature interval), conduction activation energy (ΔΕ) and electrical resistance temperature coefficient (Δ) (
The above stated can be explained by phase compositions of these two materials, since together with SiALON they contain a-SiC that is characterized by semiconductor (silicon) properties.
At sintering of kaolin and aluminium powder blend in 800˚C - 1500˚C interval, temperatures of formation of
Specimen № | Conduction activation energy, ΔΕ, ev | Electroconductivity temperature coefficient, Δ a.10−2, Ω∙m/K |
---|---|---|
SN-1 | 1.72 | 3.7 |
SN-6 | 1.29 | 2.7 |
SN-7 | 1.08 | 2.3 |
SN-8 | 1.51 | 3.3 |
aluminium and silicium nitrides and on their base mullite structure X-SiALONs was fixed and proved. While at sintering of SiC-aluminium powder, silicium and a-AL2O3-aluminium powder, silicium blend, the SiC-SiAlON and AL2O3-SiAlON composites on β-SiALON lattice were obtained. The obtained results are confirmed by X-Ray diffraction and microscopic analyses.