Bauxite deposits for production of alumina are lacking in Nigeria and there is an aluminium smelter plant in the country which requires alumina for its operation. Development of alternative alumina resource using clays that are abundant in the country is the focus of this paper. The thermal activation of Ibere clay from southeastern Nigeria for optimal leaching of alumina was investigated. The clay assayed 28.52% Al 2O 3 and 51.6% SiO 2, comprising mainly kaolinite mineral and quartz or free silica. The alumina locked up in the clay structure was rendered acid-soluble by thermal activation which transformed the clay from its crystalline nature to an amorphous, anhydrous phase or metakaolinite. The clay samples were heated at calcination temperatures of 500°C, 600°C, 700°C, 800°C, and 900°C at holding times of 30, 60, and 90 minutes. Uncalcined clay samples and samples calcined at 1000°C (holding for 60 minutes) were used in the control experiments. The result of leaching the clay calcines in 1 M hydrochloric acid solution at room temperature, showed that the clay calcines produced at 600°C (holding for 60 minutes) responded most to leaching. Samples calcined for 60 minutes also responded better than those held for 30 or 90 minutes. Based on activation energy studies, it was observed that calcines produced at 600°C (for 60 minutes) had both the highest leaching response (50.27% after 1 hour at leaching temperature of 100°C) and the lowest activation energy of 24.26 kJ/mol. It is concluded therefore that Ibere kaolinite clay should be best calcined for alumina dissolution by heating up to 600°C and holding for 60 minutes at that temperature. The clay deposit has potential for use as alternative resource for alumina production in Nigeria where bauxite is scarce.
Aluminium is the second most-produced and consumed metal after iron and steel. It is produced by the electrolytic reduction of alumina (Al2O3) in the Hall-Héroult process [
The high-volume consumption of aluminium in Nigeria and the establishment of an aluminium smelter plant at Ikot-Abasi [
Kaolinite clay has the structural formula in which the silica tetrahedral layer, represented by ( Si 2 O 5 ) 2 − is made electrically neutral by an adjacent aluminium octahedral layer, Al 2 ( OH ) 4 2 + [
However, the alumina content of kaolinite (and other clay minerals) is locked up in the clay structure. Proper thermal treatment or activation is usually necessary to render the alumina soluble under atmospheric leaching conditions [
As illustrated in
For example, kaolinite is reported to change from hydroplastic condition to leather hard, then stone hard and finally to anhydrous condition or metakaolinite as it is heated between room temperature and about 600˚C because of drying, dehydration and dehydroxylation [
1) Drying or loss of wetness or physically adsorbed water by evaporation occurs at temperatures below 120˚C. The loss of physically attached water is endothermic and results in measurable weight loss. The weight loss is usually minor, and the changes due to loss of physical water do not alter the crystalline structure of the clay [
2) Dehydration or further loss of any remaining physically held water occurs between 120˚C and about 550˚C. The resulting material after this transformation is referred to as bone-dry or stone hard clay. Throughout the drying and dehydration temperature range (where physical water is removed), the expulsion of water is reversible as shown in
3) De-hydroxylation is the loss of constitutional or chemically combined water (the OH water). Around 550˚C, the chemically combined water in clays begins to be released. This transformation continues until all chemically combined water is expelled resulting in the formation of metakaolinite, an anhydrous form of kaolinite [
and does not spontaneously rehydrate when it is exposed to water and it remains stable up to approximately 980˚C [
The thermal changes of kaolinite heated above 600˚C can be outlined in accordance with the following sequential reactions [
Al 2 O 3 ⋅ 2 SiO 2 ⋅ 2 H 2 O ︸ Kaolinite → Dehydration above 600 ˚ C Al 2 O 3 ⋅ 2 SiO 2 ︸ Metakaolinite + 2 H 2 O ︸ Constitutional WaterRemoved (1)
4 ( Al 2 O 3 ⋅ 2 SiO 2 ) ︸ Metakaolinite → 950 ˚ C - 980 ˚ C 3 Al 2 O 3 ⋅ 2 SiO 2 ︸ Primary Mullite + γ -Al 2 O 3 ︸ Gamma-Alumina ( fcc ) + 6 SiO 2 ︸ Amorphous Silica (2)
γ -Al 2 O 3 ︸ Gamma-Alumina ( fcc ) + 3SiO 2 ︸ Amorphous Silica → 1000 ˚ C - 1400 ˚ C 3 Al 2 O 3 ⋅ 2 SiO 2 ︸ SecondaryMullite + SiO 2 ︸ Tridymite (3)
3 Al 2 O 3 ⋅ 2 SiO 2 ︸ SecondaryMullite + SiO 2 ︸ Tridymite → 1400 ˚ C - 1580 ˚ C 3 Al 2 O 3 ⋅ 2 SiO 2 ︸ Mullite + SiO 2 ︸ Cristobalite (4)
Thus, the thermal changes of kaolinite heated above 600˚C progress in four major steps, namely: endothermic dehydration by de-hydroxylation of kaolinite (Al2O3∙2SiO2∙2H2O) to metakaolinite (Al2O3∙2SiO2); sudden exothermic crystallization at about 980˚C resulting to the formation of primary mullite (3Al2O3∙2SiO2), γ-alumina and amorphous silica; further recrystallization to secondary mullite and tridymite; and then transformation of tridymite to cristobalite. Whereas reaction (1) or the first transformation is associated with loss in weight (due to LOI); all four transformations are accompanied by considerable volume and enthalpy changes [
The temperatures at which these transformations (phase changes) begin and end depends on: 1) degree of crystallinity of the kaolinite, 2) its impurity oxides contents, 3) particle sizes, rate of heating, and duration of heating at a given temperature. Therefore, clays from different localities vary considerably not just in mineralogy and chemical composition, but in degree of crystallinity and purity [
Raw clay sample obtained from Ibere clay deposit (Lat. 5˚25'36''N, Long. 7˚33'48''E) in Ikwuano Council of Abia state, Nigeria was sun-dried, crushed and ground. The ground clay sample was placed on a 300 μm ASTM sieve and shaken for 5 minutes. The oversize was further ground and sieved on the same sieve. The procedure was repeated until the entire clay sample passed through the 300 μm sieve (50 standard Tyler mesh).
Representative sample of the sieved clay was analysed using Pananalytical XRD (Empyrean model) to determine the constituent minerals. Optimally calcined sample of the clay was also analysed with XRD to determine the effect of thermal transformation on the clay. Similarly, the chemical composition (amounts of Al2O3, SiO2, TiO2, etc.) was determined by means of Buckscientific AAS (model 210 VGP). The loss on ignition (LOI) was determined by placing one gramme of dry clay sample (dried at 105˚C for 12 hours in an oven) into a platinum crucible of known weight ( W d ). This was subsequently fired at 1000˚C for 1 hour in a muffle furnace. At lapse of time, the crucible was brought out of the furnace and reweighed ( W f ) after cooling down to room temperature. The LOI was calculated in percentage as ( W d − W f / W d ) × 100 .
Ground and sieved clay samples passing 300 μm sieve were subjected to thermal treatments in a muffle furnace at a heating rate of 15˚C per minute up to the holding temperature (500˚C, 600˚C, 700˚C, 800˚C or 900˚C) and held for 30, 60 or 90 minutes before furnace-cooling to room temperature. For the control experiment; a sample of the clay was reserved in the uncalcined condition (room temperature) and used as control 1, while another sample was heated up to 1000˚C and held for 60 minutes and used as control 2.
Analytical grade HCl acid and pure deionized water were used to prepare the leaching reagent. 1 molar standard solution of hydrochloric acid was prepared using deionized water. This was used as the leaching reagent for the leaching studies to determine the leaching response of the various clay calcines and the controls. The leaching was done under moderate leaching conditions, i.e. hydrochloric acid concentration of 1 M, leaching temperature at ambient (~25˚C), shaking speed of 100 rpm, and solid/liquid ratio or clay weight to acid volume ratio of 0.02 g/ml, using clay particles passing 300 μm (−50 mesh).
The leach contact time or duration ranged from 0 to 120 minutes at intervals of 30 minutes. The flask or reaction bottle was shaken at a constant rate of 100 rpm during the contact time (duration of leaching) to facilitate the reaction. This was achieved by means of a KOMA orbital shaker (model KED11). By the end of leaching, the resulting slurry was filtered to separate undissolved materials (residue) from the filtrate (leachate or pregnant solution). The leachate was analysed for aluminium ion concentration.
This procedure was repeated for all the clay calcines and the control samples, which were prepared at different temperatures and duration of calcination. The optimum condition for calcining the clay was determined using solubility data (concentration and fraction of aluminium ion solubilized).
After examination of the extent of aluminium extraction or solubilization from the clay calcines, the calcine with the best leaching response for each calcination temperature was subjected to activation energy studies to establish the thermodynamic basis for their better leaching kinetics. This was in accordance with the Arrhenius rate law, viz:
k = A e − ( E a R T ) or ln k = − ( E a R ) ⋅ 1 T + ln A (5)
where, k is the leaching rate constant, A is the Arrhenius frequency factor, Ea is the activation energy for the leaching reaction, R is the universal gas constant (= 8.314 J∙mol−1∙K−1), and T is the leaching temperature on the absolute scale [
Thus, samples held for 60 minutes at different temperatures of calcination were leached in 1 M HCl at 25˚C, 50˚C, 75˚C and 100˚C for a reaction contact time of 60 minutes. All other variables such as clay particle size, shaking speed, and solid/liquid ratio were kept constant at less than 300 µm (−50 mesh), 100 rpm and 0.02 g/ml, respectively. The natural logarithm of rate constants (lnk) as deduced from the solubility data (based on second-order reaction kinetics which appeared to fit the data) and the reciprocal of absolute temperature (1/T) were used for Arrhenius plots to determine the activation energy (Ea) in the case of each clay calcine [
Ibere clay is dominated by kaolinite mineral, with free silica or quartz and anatase as accessory minerals (
The peaks for constituent mineral phases are clearly identified in the X-ray diffraction pattern of the uncalcined clay (
Chemical Composition (%) | ||||||||
---|---|---|---|---|---|---|---|---|
SiO2 | Al2O3 | Fe2O3 | TiO2 | CaO | MgO | Na2O | K2O | LOI |
51.6 | 28.52 | 1.21 | 1.72 | 0.98 | 0.91 | 0.38 | 1.34 | 1148 |
The presence of Al3+ ions in the leach solutions shows that a dissolution reaction occurred between the alumina in the clay calcine and the leaching reagent. It is proposed that hydrochloric acid ionized in water to produce protons or hydrogen ions (H+) in the hydrated form known as hydronium (H3O+) in accordance with reaction (6) [
HCl + H 2 O ⇌ H 3 O + aq + Cl − aq or HCl aq ⇌ H + aq + Cl − aq (6)
The dissolution of alumina (Al2O3) from the clay is therefore the result of interaction between hydrogen ions (H+) and aluminium atoms of the alumina in accordance with reaction (7):
Al 2 O 3 ⋅ 2SiO 2 ︸ Metakaolinite ( Claycalcine ) + 6 ( H + Cl − ) ︸ Hydrochloricacid solution → ( 2 Al 3 + 6 Cl − ) + 3 H 2 O ︸ LeachSolution ( Tobeinfiltrate ) + 2SiO 2 ︸ Residue (7)
The extent of dissolution was expressed in percentage or as a fraction where the fraction of Al ions (XAl) leached out of the clay into the solution was given as X Al = concentration of Al ions in the solution concentration of Al ions in the original clay sample while the percent Al ions (%Al) leached out of the clay into the solution was expressed as % Al = 100 ⋅ X Al .
The results showed that thermal treatment (calcination temperature and holding time) has significant effect on the amount of Al ions taken into solution. The effect of calcination temperatures at different durations of heating (30, 60 or 90 minutes) is illustrated in Figures 4-6. As shown, response to leaching is lowest for the uncalcined clay sample (control 1) followed by that calcined at 1000˚C (control 2). The ability of the acid (1 M HCl) to extract alumina from the clay (and enrich the leach solution with aluminium ions) varied as calcination temperature increased from 500˚C to 900˚C. However, at 1000˚C (control 2), the ability of the acid to attack the clay and remove alumina dropped drastically. Under 30, 60 and 90 minutes holding times (Figures 4-6); the peak leaching response occurred in the case of samples calcined at 600˚C. As shown, between 500˚C and 900˚C; the response of Ibere clay to leaching by acid attack increased and dropped, reaching its peak at 600˚C. This behaviour is probably due to the transformation of the clay from its room temperature crystalline form (kaolinitic) to various degrees of amorphous state (metakaolinitic) and back to high temperature crystalline form at 1000˚C and beyond, as the clay steadily lost physically combined water (through drying and dehydration) and chemically combined water (de-hydroxylation) as temperature increased. In other words, the clay was completely de-hydrolyzed and transformed to metakaolinite (amorphous phase) when it was heated to 600˚C. Consequently, the kaolinite clay was completely crystalline or had various degrees of crystallinity below and above 600˚C.
Another interesting observation is that samples held for 60 minutes in the furnace responded better on leaching than those held for 30 or 90 minutes at all calcination temperatures investigated (
was just beginning, at 60 minutes, the transformation to amorphous metakaolinitewas completed, but holding up to 90 minutes resulted to the reappearance of some crystallinity. Prolonged heating can therefore make the silica and alumina contents of clay to react, resulting in reduction of solubility. Furthermore, prolonged heating may also bring about the sintering of particles or phases leading to reduction in leaching response [
These observations are in conformity with XRD patterns shown in
As observed previously (
is because high temperatures enhance diffusion or mobility and hence collision frequency of reacting species in addition to providing extra thermal energy for overcoming the energy barrier or activation energy for the process. Similar observations were made by other researchers [
The effect of thermal activation on leaching of clay calcines at different leaching temperatures is also shown in
The activation energy of leaching was found to depend on the thermal treatment given to the clay, specifically the temperature and duration of calcination (
reaction is made thermodynamically or energetically easier, thus enhancing reaction rates or kinetics. This explains why clay calcine produced at 600˚C (holding for 60 minutes) yielded the highest solubility of alumina from the clay as shown by the %Al in leach solution. It was also observed that the uncalcined sample of the clay required the highest activation energy of leaching (34.84 kJ/mol); explaining why it was very difficult to leach alumina from such sample, as seen in its very low solubility data. Thus, the alumina in uncalcined or unactivated clay is locked up in the clay chemistry, responding very sluggishly to acid attack. Similarly, clay sample calcined at 1000˚C for 60 minutes recorded the next highest activation energy (31.05 kJ/mol) after the uncalcined clay. Leaching of alumina was also difficult in this case because at 1000˚C, crystalline phases had formed. Thus, the alumina is again locked up in the mullite network, making it difficult for acid attack. Similar findings were reported in literature [
The effect of thermal treatment on the transformation of Ibere kaolinite clay and subsequent leaching of alumina was investigated under atmospheric pressure1. Different thermal treatments produced different degrees of leaching response from the clay based on the nature and extent of phase transformation. X-ray diffraction studies confirmed that the optimal leaching response corresponded with the thermal treatment that transformed the clay to an amorphous phase or metakaolinite. The clay was transformed from its low-temperature crystalline form to an amorphous form at 600˚C and then back to high-temperature crystalline phases. Prolonged heating (above 90 minutes) under isothermal conditions also caused the appearance of crystalline phases and loss of solubility. Best results were achieved under 60 minutes heating duration at 600˚C. Thermal treatment also affected the activation energy of leaching such that high solubility (high leaching response) corresponded with low activation energy. Thermally activated Ibere clay can be used as alternative resource for alumina in Nigeria where bauxite is scarce or non-existent.
The present work has established the optimal calcination conditions for Ibere clay. Further work is recommended to investigate the effects of the leaching variables such as clay particle size, acid concentration, leaching temperature, solid/liquid ratio of clay weight to acid volume, and shaking rate. This will establish the optimal leaching conditions for solubilizing the alumina in the clay. Methods of recovering alumina from the leach solution should also be investigated.
This work was financially supported by a research fellowship of the Federal University of Technology, Owerri (REG/EST/SPMU/SP.2318). The authors would like to thank the unknown reviewers for their helpful comments and suggestions.
The authors declare no conflicts of interest regarding the publication of this paper.
1The authors acknowledge that pressure hydrometallurgy as proposed by Habashi [
Mark, U., Anyakwo, C.N., Onyemaobi, O.O. and Nwobodo, C.S. (2019) Effect of Calcination Condition on Thermal Activation of Ibere Clay and Dissolution of Alumina. International Journal of Nonferrous Metallurgy, 8, 9-24. https://doi.org/10.4236/ijnm.2019.82002