In claim of developing ecologically-friendly and low cost polymeric materials, some polymer scientists and engineers have focused on improving the properties of polymer composites with natural fibers. One typical example of these natural fibers currently used as reinforcements in low load-bearing polymer composites is bovine fiber which is traditionally a waste from slaughterhouse. However, nature has designed natural fibers with anisotropic properties which may not augur well for the development of polymer composites with guaranteed field-proven reliability. Nonetheless, unlike vegetal fibers, most animal fibers can be alternatively exploited for keratinous applications. In the present study, the tensile properties, crude protein contents and variations in elemental distribution of hair fibers obtained from three breeds of bovine found in Nigeria were investigated. The hair fibers were characterized by ultimate testing machine, proximate analysis and scanning electron microscopy with energy dispersive X-ray spectroscopy. Superlative Young’s modulus and tensile strength among the fibers were found to be 0.98989 GPa and 0.56158 MPa, respectively. The determined crude protein contents of the fibers ranged between 35% and 40%. Also, single hair fibers from each bovine breed showed significant variations in elemental distribution along their longitudinal sections which translates to anisotropic chemical and mechanical properties. However, the mean spectral values of the principal elements that constitute amino acids in the fibers are in the same range with that of human hair fibers with a successful record of keratinous applications.
Critical reviews on the idea of radically replacing synthetic fibers (SFs) with Natural Fibers (NFs) in Polymer Composites (PCs) have revealed that this approach is defective and equally impracticable [
This intellectual dispute subsequently resulted in a complicated confusion that prominent materials scientists have painstakingly tried to clarify since the invasion of NFs in PCs development [
The foregoing clarification eventually culminated in a lot of researchers with keen interest in NFs trying assiduously to strike a balance between NFRPCs and SFRPCs. The consequent approaches to upgrade the properties of NFRPCs include fiber surface modification by chemical treatments, polymer matrix modification and the deployment of coupling agents [
Nonetheless, these approaches still failed to be NFRPCs’ saving grace despite reducing the economic viability of developing them. According to some researchers, the economic viability of developing NFRPCs is another major claim that led to the express switch from SFRPCs to NFRPCs [
During the advent of NFRPCs, the vegetal fibers (VFs) were the most exploited NFs. However, due to their associated drawbacks such as hydrophilic nature, dimensional instability at high temperatures and poor adhesive strength (wettability) [
At first, the diversion into AFRPCs showed some great prospects; however, the problem of great anisotropy in their properties makes it difficult to develop AFRPCs with desired engineering properties [
However, unlike VFs, most AFs are biological wastes such as avian feathers and mammalian hairs which are generated across the globe by agro-industrial industries in billions tons per year [
On the bright side, most of these AFs are keratinous materials; that is, they are potential bio-resources for keratin extraction [
Keratins and their derivatives are extensively used for biomedical, cosmetic, industrial and agricultural applications. Keratin films and keratin-based films are used in ocular surface reconstruction, drug delivery systems and treatment of acute myocardial infarction. Keratin hydrogels are used in peripheral nerve repair and as homeostatic agents. Keratin powders are used in wound healing and bone regeneration [
Hitherto, chicken feathers, animal wools and human hairs have been the major bio-resources exploited for keratin extraction with little attention on bovine hair, hooves and horns [
Of interest to the present study is whether Bovine Hair Fiber (BHF) should remain an emerging engineering material for AFRPCs development or should be considered a keratinous bio-resource.
The present study investigated the tensile properties, proximate compositions and variations in elemental distribution (along longitudinal sections) of BHFs obtained from three different breeds of bovines found in Nigeria.
The materials used in this research were basically White Bovine Hair Fiber (WHBHF), Black Bovine Hair Fiber (BLBHF) and Brown Bovine Hair Fiber (BRBHF) obtained from healthy White Fulani, Forest Muturu and Ankole-Wa- tusi bovine breeds, respectively. The BHFs were obtained from the tail sections of each bovine breed. In order to have full knowledge of the BHFs, they were collected from a cattle ranch in the Federal University of Technology, Akure (FUTA), Ondo State, Nigeria. Ages of the bovines were 5 years ± 6 months at the time of collection; the diameters of the collected BHFs ranged between 65 and 67 µm and their lengths ranged between 50 and 60 mm. The bovines are allowed to graze under free-range system. The average temperature across the year in this part of Nigeria varies between 23.55˚C ± 0.423˚C and 37.54˚C ± 0.23˚C in the wet and dry seasons, respectively.
The as-obtained BHFs from FUTA cattle ranch were thoroughly washed and rinsed with detergent and warm distilled water to render them free from impurities such as dust, oil and grease. Thereafter, the cleaned BHFs were dried for 21 days at 25˚C ± 2˚C to prepare them for tensile test, proximate analysis and Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy (SEM-EDS).
Till date, perfect methods of evaluating the actual tensile properties of a single NF are still non-existent. Most researchers invariably use the longitudinal tensile modulus (which is always higher than the transverse modulus) of NFs to predict the mechanical behavior of NFRPCs. However, some researchers who considered this approach defective resorted to using the Young’s modulus from a bundle of NFs for predicting the performance of NFRPCs [
The tensile properties of the BHFs were evaluated in compliance with ASTM D3822-07 standard [
The proximate compositions of the BHFs were manually determined by proximate analysis in accordance with AOAC 2003 standard [
A single BHF was placed within the vacuum chamber located at the bottom of the scanning electron microscope column (German brand AURIGA, Carl Zeiss 2010 model). An electron source, located at the top of the column, produced electrons that passed through the column and were incident upon the BHF. The electron beam was directed and focused by magnets and lens inside of the scanning electron microscope column as it approached the BHF. The beam swung across the sample causing some of the electrons to be reflected by the BHF and some to be absorbed. Specialized X-ray detectors received these electrons and processed the signal into a usable format. The SEM-EDS was carried out on eight different spectra on a single BHF from each bovine breed, however, the closest four spectral details were selected for discussion in the present study.
Figures 1-6 show the SEM-EDS results for the BHFs. Form the results, it was observed that for each bovine breed, elemental distributions differ significantly per spectrum in a single fiber. This is a general phenomenon observed with most NFs, and hitherto, there are no conclusive explanations for this incongruity. Many great attempts by researchers to explain this occurrence were implicit and tainted by many pitfalls. However, some researchers claimed that this occur-
rence might be as a result of diametric inconsistency in a single NF, which in turn allows an inconsistent distribution of elements across the fiber’s longitudinal and transverse sections [
Likewise, the elemental distributions of the BHFs vary with respect to bovine breeds. 13 elements were found in the BRBHF, 9 elements were found in the WHBHF and 7 elements were found in the BLBHF. However, 7 elements present in all the BHFs with different wt% are Carbon, (C), Oxygen (O), Nitrogen (N), Sulfur (S), Silicon (S), Calcium (Ca) and Aluminum (Al).
For the WHBHF and the BLBHF, C, N, O and S are present in significant amounts. Mean spectra values (MSVs) for C, N, O and S for the WHBHF are 45.56, 20.88, 25.22 and 4.85 wt%, respectively. For the BLBHF, the MSVs for C, N, O and S are 50.28, 20.84, 22.92 and 5.47 wt%, respectively. However, for the BRBHF, a different trend in the amount of significant elements present was observed. This fiber has very low N and S contents but has C, O, Fe, Si and Phosphorus (P) present in significant amounts. The MSVs for the C, O, Fe, Si and P present in this fiber are, 17.89, 36.20, 27.43, 7.21 and 3.59 wt%, respectively.
The occurrence of variations in elemental distributions of hair fibers from different breeds of the same animal has explained by some trichologists is dependent on some specific factors. These factors include geographical location, environmental conditions, type of nutrition, health status, age and gender of the animal [
From these observations, it can be said that BHF is not excluded from the blacklist of critical reviewers who have associated the limitations of NFs in NFRPCs development with their anisotropic properties. These researchers believe that glass fibers would still continue to dominate the fiber market as far as the development of FRPCs for load-bearing applications is concerned [
In
The superlative tensile modulus exhibited by the BLBHF is 0.98089 GPa which is considerably lower that of wool fiber (presumably the least stiff animal fiber known so far) with a tensile modulus of 3.4 ± 0.1 GPa [
In addition to the poor tensile properties, other shortcomings of BHFs are their short fiber length and high susceptibility to mechanical degradation if they are chemically modified. For most of the BHFs, the maximum fiber length attainable is 60 mm which in turn would limit the choices of fiber orientation in developing BHFRPCs. In terms of chemical modification of BHFs, the hydrophobic epithelial cuticle may be disrupted and expose the hydrophilic cortex of
the BHFs and this is likely to result in a swollen fiber [
Despite these exposed shortcomings of BHFs as an engineering material, the general claim used to support their emergent applications in AFRPCs development is their hydrophobic epithelial cuticle containing a lipid layer that includes 18-methyl eicosanoic acid (18 MEA) [
Judging by these limitations, the present study considered it commendable for researchers with keen interest in exploiting BHFs for significantly useful purposes to seek alternative applications for this presently under-utilized bio-re- source.
Of interest to the present study is the CPC% of the BHFs, therefore their MC% and AC% would not be discussed. Prior exploiting AFs for keratin extraction, it is paramount to know the CPC% present in the fibers as this gives an insight as to whether the exploitation would be worthwhile or not.
This result is expected as some key elements such as C, N, O and S which are the building blocks of amino acids were detected in significant amounts by the spectroscopic analysis of the BHFs. The WHBHF and BRBHF have very close CPC% which are 39.66% and 39.51%, respectively. A slight drop in CPC% was observed with the BLBHF having 35.77 CPC%. A similar finding was reported by Oladele et al. when they investigated the effect of chemical treatments on CPC% of Zebu breed bovine fiber [
According to Moore et al., the proximate composition may not give the exact protein content in a fiber [
Presently, there exist many methods to extract keratin from BHF and other mammalian hair fibers. In a study conducted by Souza et al. on the feasibility of extracting keratin from BHF through hydrolysis, they were able to extract keratins with molecular weight of 20 kDa [
Any of the abovementioned methods can be adopted by researchers interested in the exploitation of BHFs for keratinous applications. A flowchart of possible extraction routes of keratins from BHFs and their potential areas of applications is presented in
The present study concluded from the observations from its experimental results, supporting research findings and theoretical facts that the exploitation of BHFs as reinforcements in PCs is an under-utilization of this bio-resource. This is dependent on the fact that their application is invariably limited to low load- bearing PCs. Furthermore, the field-proven reliability of BHFRPCs is still deeply rooted in the experimental phase.
Based on the foregoing revelations, a proper utilization of BHFs would be their exploitation for keratinous applications. This is basically because BHFs from different sources can be exploited simultaneously for keratin extraction, which may not be suitable for developing BHFRPCs due to the anisotropic properties of these fibers.
However, in the absence of limited research facilities to exploit BHFs for keratinous application, the fibers still remain as good candidates for reinforcing low load-bearing polymer composites.
Oladele, I.O., Olajide, J.L., Daramola, O.O. and Siaw, K.B. (2017) Re-Evaluation of Bovine Fiber Biomass as Exploitable Keratinous Bio-Re- source for Biomedical and Industrial Applications. Journal of Minerals and Materials Characterization and Engineering, 5, 1-17 http://dx.doi.org/10.4236/jmmce.2017.51001