Green synthesis of metal oxide nanoparticles using plant extract is a promising alternative to traditional method of chemical synthesis. In this paper, we report the synthesis of nanostructured zinc oxide particles by biological method. Highly stable and spherical zinc oxide nanoparticles are produced by using zinc acetate and Ixora coccinea leaf extract. Formation of zinc oxide nanoparticles has been confirmed by UV-Vis absorption spectroscopy, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Dynamic light scattering analysis (DLS), zetapotential study and Scanning Electron Microscope with the Energy Dispersive X-ray studies (EDX). Dynamic light scattering analysis shows average particle size of 145.1 nm whereas high zeta potential value confirms the stability of formed zinc oxide nanoparticles. The Scanning Electron Microscope reveals spherical morphology of nanoparticles and Energy Dispersive X-ray analysis confirms the formation of highly pure zinc oxide nanoparticles. The zinc oxide nanoparticles from Ixora coccinea leaves are expected to have applications in biomedical, cosmetic industries, biotechnology, sensors, medical, catalysis, optical device, coatings, drug delivery and water remediation, and also may be applied for electronic and magneto-electric devices. This new eco-friendly approach of synthesis is a novel, cheap, and convenient technique suitable for large scale commercial production.
Nanoparticles are of great interest due to their extremely small size and large surface area to volume ratio, which lead to both chemical and physical differences in their properties (e.g. mechanical properties, biological and sterical properties, catalytic activity, thermal and electrical conductivity, optical absorption and melting point) compared to bulk of the same chemical composition. Therefore, design and production of materials with novel applications can be achieved by controlling shape and size at nanometre scale. Nanoparticles exhibit size and shape-dependent properties which are of interest for applications ranging from biosensing and catalysts to optics, antimicrobial activity, computer transistors, electrometers, chemical sensors, and wireless electronic logic and memory schemes. These particles also have many applications in different fields such as medical imaging, nanocomposites, filters, drug delivery, and hyperthermia of tumors [
Over the past few decades, inorganic nanoparticles, whose structures exhibit significantly novel and improved physical, chemical, and biological properties and functionality due to their nano-scale size, have elicited much interest. Recent studies have shown that nanoparticles of some materials including metal oxides, can induce cell death in eukaryotic cells [
Among the metal oxide nanoparticles, zinc oxide nanoparticles have drawn attention of many researchers for their unique optical and chemical behaviors which can be easily tuned by changing the morphology. Within the large family of metal oxide nanoparticles, zinc oxide nanoparticles have been used in various cutting edge applications like electronics, communication, sensor, cosmetics, environmental protection, biology and medicinal industry [
Different physical and chemical processes are currently widely used to synthesize metal nanoparticles, which allow one to obtain particles with the desired characteristics. However, these production methods are usually expensive, labor-intensive, and are potentially hazardous to the environment and living organisms. Thus, there is an obvious need for an alternative, cost-effective and at the same time safe and environmentally sound method of nanoparticle production [
Several conventional methods have been used for synthesis of zinc oxide nanoparticles like chemical vapor synthesis [
Few papers reported the biosynthesis of zinc oxide nanoparticles using plant extracts such as Aloe barbadensis miller [
Ixora coccinea leaves were collected from Institute of Chemical Technology campus, Matunga, Mumbai, India. The important compounds in the plant extract are hydroxyl and carbonyl groups. Both functional groups allowed plant extract to act as reducing agent. Functional groups present in the leaves extract of Ixora coccinea such as phenolics and alkaloids are responsible for capping thereby stabilization of nanoparticles reduced. Zinc acetate dihydrate (Zn(O2CCH3)2 as metal ion precursor which act as zinc source and sodium hydroxide (NaOH ) as precipitating agent were purchased from Merck, India Pvt. Ltd. Distilled water was used throughout the reaction process.
Fresh leaves of Ixora coccinea were thoroughly cleaned with running tap water to remove debris and other contaminations, followed by distilled water and air dried at room temperature. Leaves were finely chopped into small pieces. The aqueous extract of sample was prepared by boiling the freshly collected cut leaves (10 g), with 100 cm3 of distilled water, at 60˚C for about 20 minutes, until the color of the aqueous solution changes from watery to light brown. Then the extract was cooled to room temperature and filtered using whatman filter paper. The extract was stored in a refrigerator in order to be used for further experiments.
For the synthesis of zinc oxide nanoparticles, 50 cm3 of 0.5 M zinc acetate dihydrate solution was prepared using distilled water. 1 cm3 aqueous leaf extract of Ixora coccinea was introduced into the above solution after 10 minutes of stirring. In order to maintain the pH 12, 2.0 mol・dm−3 sodium hydroxide was used which resulted in a pale white aqueous solution. This was then placed in a magnetic stirrer for 2 hrs. The pale white precipitate was then taken out and washed over and over again with distilled water followed by ethanol to get free of the impurities. Then a pale white powder of zinc oxide nanoparticles was obtained after drying at 60˚C in oven over night to give yield of 96.7%. Graphical representation of the procedure is shown in
The obtained zinc oxide nanoparticles were measured for its maximum absorbance using UV-Vis spectrophotometry. The optical property of zinc oxide nanoparticles was determined via ultraviolet and visible absorption spectroscopy in the range of 280 - 420 nm. Structure of zinc oxide nanoparticles was analyzed by using X-Ray Diffraction (XRD) analysis. Particle size of synthesized nanoparticles was obtained by Dynamic light scattering analysis (DLS) and stability of the nanoparticles was checked by zeta potential measurement. External morphology i.e. shape of the nanoparticles were characterized by Scanning Electron Microscope (SEM). Elemental analysis was obtained from energy dispersive X-ray diffraction (EDX), which was attached with SEM.
The optical absorption spectra of zinc oxide nanoparticles were recorded using UV/VIS 3000+ Double Beam UV Visible Ratio-Recording Scanning Spectrophotometer from Lab India (SKU: 174-0020) with dimensions of (W × D × H)/Weight = 540 × 440 × 390 mm/36kg. Spectral bandwidth of Spectrophotometer is 0.5, 1, 2, 5 nm and wavelength is in the range of 190 to 1100 nm.
The X-Ray diffraction (XRD) pattern of synthesized zinc oxide nanoparticles is shown in
30 kV and 15 mA was used with scan rate of 3˚/min. The data recorded in the range 5θ - 80θ and analyzed using Jade 6.0 software. X-Ray diffraction pattern shows 2θ values at 31.84˚, 34.52˚, 36.38˚, 47.64˚, 56.7˚, 63.06˚, 68.1˚ and 69.18˚. All evident peaks could be indexed as the Zinc oxidewurtzite structure (JCPDS Data Card No: 36-1451). Zinc oxide crystallizes in two main forms, hexagonal wurtzite and cubic zincblende. The wurtzite structure is most stable at ambient conditions and thus most common. It also confirms the synthesized nanopowder was free of impurities as it does not contain any characteristics XRD peaks other than zinc oxide peaks [
Particle size was determined by dynamic light scattering technique using Nano plus (Micromeritics, USA).The instrument can measure the particle size of samples suspended in liquids in the range of 0.1 nm to 12.3 µm with sample suspension concentrations from 0.00001% to 40%, plus a sensitivity for molecular weight to as low as 250 Da. Dynamic light scattering is a widely used technique for the determination of particle size in colloidal solution. The average size of the particles, size distribution, and polydispersity index (PDI) of the synthesized zinc oxide nanoparticles were determined by this technique and the results are shown in
Zeta potential analysis was carried out to detect the surface charges acquired by zinc oxide nanoparticles, which can be used to gain further insights into the stability of the obtained colloidal zinc oxide nanoparticles. Zeta potential of zinc oxide nanoparticle
was measured using instrument provided by Nanoplus-Micromeritics, USA. This instrument has the ability to perform highly accurate zeta potential measurements of sample suspensions in the −500 mV to +500 mV range. Patented FST technology utilizes a transparent electrode to minimize path length and reduce multiple scattering effects. The magnitude of zeta potential gives an insinuation of potential stability of colloid. If the particles in a suspension have large negative or positive zeta potential values, particles will repel each other and there will be no aggregation of nanoparticles. On the other hand, if particles have small zeta potential values there is no force to prevent particle coming together and their aggregation. It is generally considered that the zeta potential values greater than +30 mV or smaller than −30 mV, result in stable suspensions [
FT-IR is an effective method to reveal the composition of products.
The morphology of the prepared nanoparticles was examined using scanning electron microscopy.
The Energy Dispersive X-ray Diffractive (EDX) study was carried out for the synthesized
zinc oxide nanoparticles to know about the elemental composition. EDX confirms the presence of zinc and oxygen signals of zinc oxide nanoparticle as shown in
Frequency (cm)−1 | Possible Assignment |
---|---|
3398.56 cm−1 | OH stretching vibrations |
2912.09 cm−1 | The C-H stretch in alkanes |
2845.74 cm−1 | O-H stretch in carboxylic acid |
1561.06 cm−1 | C=C stretch in aromatic ring and C=O stretch in polyphenols |
1461.45 cm−1 | C-N stretch of amide-I in protein |
1018.12 cm−1 | C-O stretching in amino acid |
533.71 cm−1 | hexagonal phase ZnO |
The rapid biological synthesis of zinc oxide nanoparticles using leaf extract of Ixora coccinea provides an environmental friendly, simple and efficient route for synthesis of nanoparticles. Zinc oxide nanoparticles have been successfully synthesized by using this method. The prepared zinc oxide nanoparticles were spherical in shape and were characterized using XRD, FTIR, EDX, DLS, UV-Vis absorption and SEM techniques. The SEM image showed that most of the nanoparticles are spherical in shape formed within diameter range of 80 - 130 nm. FTIR shows that peak at 533.71 cm−1 is the characteristic absorption of zinc oxide bond which confirms formation of zinc oxide nanoparticles. X-ray diffraction confirms the formation of a hexagonal wurtzite phase which is the most stable form of zinc oxide at ambient conditions. Particle size of 145.1 nm and polydispersity index of 0.189 were found, which indicates there is uniform size distribution of nanoparticles. The zeta potential was found to be −49.19 mV. The high value confirms the stability of zinc oxide nanoparticles. Zinc oxide nanoparticles prepared from above mentioned route are expected to have more extensive application in biotechnology, sensors, medical, catalysis, optical device, coatings, drug delivery and water remediation. Also, they may be applied for electronic and magneto-electric devices. This process is an economical method for the preparation of nanocrystalline zinc oxide with respect to energy, time and simplicity as well as it has high yield of 96.7% and can be used for large scale synthesis of zinc oxide nanoparticles.
Yedurkar, S., Maurya, C. and Mahanwar, P. (2016) Biosynthesis of Zinc Oxide Nanoparticles Using Ixora Coccinea Leaf Extract―A Green Approach. Open Journal of Synthesis Theo- ry and Applications, 5, 1-14. http://dx.doi.org/10.4236/ojsta.2016.51001