Natural contamination of world groundwater supplies with arsenic of volcanic origin has become a complicated and growing problem given current shortage of water. Maintenance cost of treatments that are based on ion exchange and reverse osmosis is considered high, in addition to the high production of sludge with such methods. On the other hand, efficiency of treatments employing coagulation/filtration is usually relative, depending on the method of application. Currently, emerging treatments that use nanotechnology are gaining relevance, due to their high efficiency and low cost. These methods are highly selective, with minimum generation of toxic wastes, as long as particle release into the environment is kept under control to avoid health risks. The present study developed filters with magnetic nanoparticles of Fe 3O 4 (magnetite) supported on porous silica (Fe 3O 4@SiO 2) at a mass ratio of 2:1. The nanoparticles were synthetized by co-precipitation of Fe(II) and Fe(III) using NH 4OH (ac) under inert atmosphere. Average sizes of 15 nm were obtained, measured by means of Transmission Electronic Microscopy (TEM) and characterized by X-ray Powder Diffraction (XRD); the magnetic power was qualitatively determined. The efficiency of the composite material (Fe 3O 4@SiO 2) was determined in a prototype laboratory with a height of 60 cm and a diameter of 5 cm, assembled with five filters of the composite material, with 1 g each filter. The filters were wrapped in resistant water-porous fabric to favor continuous flow at a ratio of 0.015 L/min. The test was performed with arsenic solutions at (43.7 ± 2.1 μg/L), similar to the amount present in water supplies currently treated in Costa Rica. The removal was completed in 7 minutes with 0 N.T.U and less than 10 μg/L arsenic concentration (maximum limit allowed in Costa Rica), quantified by Atomic Absorption Spectrometry with Hydride Generation. After the reaction filters, the prototype was assembled with cleaning filters at a ratio of 1:8. The final way out was through a magnetized tube to ensure that no nanoparticles were released outside with the water, thus contributing to nanotoxicology safety for people and the environment.
Arsenic is an element that has attracted people’s attention since ancient times. It used to be considered as a powerful poison, and it is now in the news as a result of a largest environmental calamity in Asia. This has led to the rediscovery of arsenic despite it always exists in the environment as a “silent” toxic agent in the world. Every year, new areas with arsenic in environments exceeding the maximal contamination levels set by international organizations are identified. Arsenic is a natural or anthropogenic contaminant in areas where human subsistence is a risk. It comprises a large number of chemical species with a wide variation in toxicity [
At least, four million people in several countries in Latin America?Argentina, Chile, El Salvador, Nicaragua, Mexico, Peru and Bolivia among them?drink water having levels of arsenic that put their health at risk [
Arsenic effects in population worldwide go from slight changes in pigmentation on face, neck and back, to cutaneous lesions and hyperkeratosis. Effects appear after five years minimum exposure and may evolve into skin cancer. Later on, or because of ingesting high concentrations of arsenic, other problems may occur, such as digestive, hepatic, renal, cardiovascular, neurological, haematological, reproductive and learning problems, and diabetes [
Combined exposures to lead, cadmium and arsenic are common in both occupational and environmental situations [
The clinical manifestations of such arsenic exposures on the kidney are consistent across studies and may involve effects on the blood vasculature [
In view of the toxic effects of As to human health, it becomes important to remove it from the environment. Some of the most common technologies for arsenic removal include oxidation, coagulation/precipitation, adsorption, ion exchange, electrocoagulation, and membranes [
In recent years, there has been an increasing use of engineered magnetic nanoparticles for remediation and water treatments, leading to elevated public concerns. To this end, it is necessary to enhance the understanding of how these magnetic nanoparticles react with contaminants and interact with the surrounding environment during applications.
The large contaminants removal capacity and fast reaction rate of the magnetic nanoparticles are the major advantages. The total surface area of particles with the same mass increases tremendously (can add up to a thousand times), when the particle size decreases to nano-scale [
Using magnetic nanoparticles for contaminant removal has proven to be a highly efficient technology. Desorption is desirable for controlled applications; but this can lead to a disaster of pollutant migration and spreading out if desorption occurs when the spent magnetic nanoparticles are released into the environment in an uncontrolled manner [
One of the most important characteristics of magnetic nanoparticles, showing advantage over other nanoparticles, is their magnetism. Abundant evidence showed that magnetic properties of particles alter when particle size reaches nanoscale [
When considering the applicability of magnetic nanoparticles for treatment technologies, another major consideration is the reusability of magnetic nanoparticles. To maintain reactivity, physical and chemical properties of the nanoparticle products, the synthesis and manufacturing process of nanoparticles require meticulous control of conditions. The treatment cost of applying nanoparticles is relatively high, compared with traditional treatments. For instance, the Price of 1 kg of γ-Fe2O3 nanoparticles is ranging from USD 180 to 380, depending on the particle size, purity and methods of synthesis [
The rapid expansion of nanotechnology promises to have great benefits for society, yet there is increasing concern that human and environmental exposure to engineered nanomaterials may result in significant adverse effects. That is why the field of nanotoxicology-dealing with effects and potential risks of particulate structures <100 nm in size-has emerged, growing significantly over the past decade from long-standing foundations of well es- tablished knowledge on the toxicology of fibrous and non-fibrous particles and the interactions of viruses with cells.
Discoveries of nanoparticle-specific concepts of toxicology related to their small size and large specific surface area go back to the early parts of the past century, although the distinctive biological effects and kinetics of nanoparticles were not recognized until the last decade of the past century [
Studies also illustrated that nanoparticles have the ability to enter organisms during ingestion or inhalation [
Adsorption of magnetic nanoparticles on the bacteria membrane surface, and the reactions internally in cytoplasm of bacteria were reported to be the causes of bactericidal effect [
The specific gene alteration and hierarchical clustering revealed that SPIONs-COOH altered genes associated with cell proliferative responses due to their reactive oxygen species (ROS) properties. It was also found that the cell type can have quite a significant role in the definition of suitable pathways for detoxification of NPs, which has deep implications for the safe and high yield design of NPs for biomedical applications and will require serious consideration in the future [
The small size facilitates uptake into cells and transcytosis across epithelial and endothelial cells into the blood and lymph circulation to reach potentially sensitive target sites such as bone marrow, lymph nodes, spleen, and heart. Access to the central nervous system and ganglia via translocation along axons and dendrites of neurons has also been observed. The greater surface area per mass compared with larger-sized particles of the same chemistry renders nanoparticles more active biologically. This activity includes a potential for inflammatory and pro-oxidant, but also antioxidant, activity, which can explain early findings showing mixed results in terms of toxicity of nanoparticles, to environmentally relevant species [
The research findings on the toxic effects of magnetic nanoparticles have generally focused on “clean” particles. However, during environmental applications of magnetic nanoparticles, various contaminants could interact with the particles and alter their physiochemical properties. Magnetic nanoparticles may act as contaminant carriers, if the “used” magnetic nanoparticles are internalized by cells. A synergistic toxic effect could be a consequence in this ternary system, cells-contaminants-magnetic nanoparticles, where the bioavailability of loaded magnetic nanoparticles and its affinity towards bacterial cells have yet to be studied. One should also note that the type of bacteria plays a critical role on bactericidal effects, since different bacteria have a different tolerance on oxidative stress and exposure to nanoparticles [
For instance, autotrophic bacteria can utilize chemical energy which can probably withstand the high reactivity of nanoparticles [
The research data on the environmental effects and bioavailability of magnetic nanoparticles is still limited, especially on phytotoxicity, although the toxicological effects of several other types of nanoparticles, such as fullerenes, carbon nanotubes, titanium dioxide and silver, have been widely studied [
Various experimental methods including in vitro study with isolated plant cells, a whole plant, or seeds as well as various experimental setups such as water, soft agar medium, and nature soil have been applied [
Although diverging results of the phytotoxicology of the magnetic nanoparticles were reported, a comparatively conclusive finding showed that the presence of soil or sand reduced the impacts of magnetic nanoparticles on plants. The magnetic nanoparticles tend to attach or deposit on soil or sand grains, leading to a reduction of availability of magnetic nanoparticles [
The magnetic nanoparticles can also lead to little growth of leaves and death of older leaves (grown before dosing of nanoparticles). On the contrary, It was also reported that the magnetic nanoparticles could be taken up and translocated in plants, without any apparent visual impact, and could even enhanced the plant growth at low concentration [
Taken together with the toxicology effects on bacteria, surface modifiers can reduce degree of toxicity on both plants and bacteria, probably due to reduction of attachment, and thus bioavailability. Moreover, the attachment of magnetic nanoparticles to soil medium resulted in lower the toxic impacts, suggesting that magnetic nanoparticles at low concentration could be used for environmental engineering applications without pernicious effects on plants [
The aim of the research was to develop a nature-friendly selective treatment, applying updated technology and at a reasonable cost, intended to be employed in the way out of medium flow wells.
A Fe3O4@SiO2 composite was used as remover of arsenic species. This composite material was prepared using co-precipitation of Fe(II) and Fe(III) with NH4OH(ac) onto SiO2, using a method similar to the one proposed by Petcharoen and Sirivat [
XRD data of single Fe3O4 nanoparticles and Fe3O4@SiO2 were acquired with a PANalytical Empyrean diffractometer with Cokα1 radiation. Each pattern was obtained in the 2θ range of 15.0091˚ - 84.9881˚ with steps of 0.0130˚. The scan step times were 13.7700 s for the single Fe3O4 nanoparticles sample and 37.9950 s for the Fe3O4@SiO2 composite. TEM micrographs were obtained for the single Fe3O4 nanoparticles using a JEOL JEM-2100 microscope with an accelerating voltage of 100 kV.
A scalable lab system using filtering down through porous materials Fe3O4@SiO2 was implemented in order to study the performance of the removers using continuous flow. Filters with Fe3O4@SiO2 composite material were produced, wrapped in semipermeable fabric allowing water flow, containing 1 g of composite material each filter. Several tests were needed to determine the appropriate number of filters per tested arsenic solution volume.
Then, activated carbon bed filters were assembled to the system, in order to reduce turbidity of filtered water coming through the composite material filters. The activated carbon bed filters were placed in the system at a ratio of 8:1 with respect to the composite material filters. Following, the water flows through a 0.45 µm filter, to finally come out through a magnetized tube that can remove all magnetic nanoparticles that may have been liberated.
A solution prepared in the laboratory with arsenic reagent grade with a concentration of (43.7 ± 2.1 µg/L) was used to carry out performance measurements of the filters mentioned above. Following this trial, the performance of the filtration system was tested using the water entering the treatment system at Bebedero, Cañas, Guanacaste in Costa Rica.
Total As in water samples was analyzed using Perkin Elmer AAnalyst-800 atomic absorption spectrometer with a FIAS-100 hydride generation system. All measurements were carried out using a method with a detection limit of 0.71 μg/L and a quantification limit of 2.38 μg/L. Alternatively, simple field test measurements were done using a test kit Lovibond®, previously validated using the Atomic Absorption Spectroscopy analysis method.
Obtaining the smallest particle size possible is essential for a successful synthesis of nanoparticles. Once prepared for visualization through the electronic transmission microscope, the samples were analyzed to determine average size. The Fe3O4 magnetite nanoparticles obtained showed irregular shape with an average size of 15 nm, calculated by means of TEM.
In order to quantify the efficiency of the nanoparticles on the support material and to scale up the results to a field device, the determination of the efficiency of the composite material (Fe3O4@SiO2) was carried out in a prototype laboratory consisting of a continuous flow system. Filter testing was performed starting with 25 filters per time, down to a minimum of 5 filters, concluding that this last number of filters of the composite material may have acted efficiently in the prototype. Work was carried out with continuous flow at a ratio of 0.015 L/min, tested with a laboratory solution of arsenic at 43.7 ± 2.1 mg/L. The resulting concentrations of arsenic in each
volume of sample filtered through the composite material were found to be lower than the detection limit of the atomic absorption equipment (pointed green line).The graphics presented on
It was found that the filters could treat an important amount of water with arsenic. In view of their high performance, it was decided to estimate the projected quantity of water that could be treated with the same filters. The yield volume of the composite material of the prototype was calculated, continuing the trend line. A straight line equation was used for calculation.
Once filter efficiency was determined under laboratory conditions, the filtration system was tested using raw untreated water from the Northern zone of the country, contaminated with arsenic at a concentration of 13.3 µg/L. This area, called Bebedero de Cañas, is characterized by having high pH of 8.1 and total hardness of 83 mg/L, which is considered as medium hardness. It is important to determine the performance of the nano-parti- cles under such conditions, since a previous treatment may be necessary in order to pass water through the filters and these accomplishing the task of selective arsenic absorption. Performance of the filters is shown in
As can be observed, while the water presents high pH and high hardness, there is interaction with the nano- particle charges of the composite material, which causes that after being adsorbed, the arsenic is released, which can be observed in the ascending behaviour of the graphics. In addition, cleaning filters play an important role in arsenic retention by the system; however, the filters become rapidly saturated with interaction of the charges, as shown in
For the above reasons, three tests were performed: test 1-water pH in Bebedero was changed from 8.1 to 5.6; test 2-pH was modified and the sample was put through a resin for cationic exchange; and test 3-the sample received the resin treatment to reduce hardness only. All this was performed to determine the influence of high water pH, high water hardness or both, on the efficiency and arsenic removal capability of the filtration system.
As shown in
Synthesis and characterization of magnetic nanoparticles of Fe3O4 were obtained. The advantages of these materials are known: efficiency and high performance, high specificity, low cost since they were synthesized in our
laboratory from common reagents and minimal waste release into the environment after their reaction in the water. Because of their intrinsic magnetism, the nanoparticles can be separated and recovered with an external magnetic field, which in this case is a magnetized exit tube in the filtration system.
Due to the close relationship surface-area-volume, active reaction sites increase, and the amount required for the treatment processes can be much less than in other similar treatments, since removal capacity and reactivity of nanoparticles are highly size dependent. In this case, the nanoparticles obtained had an average size of 15 nm, therefore it was possible to find particles of 10 nm or less in the material, which is the reason for the high efficiency found.
High performance material was obtained, with average nanoparticle sizes of 15 nm; proven high efficiency; low cost and easily reproducible, because of the type of materials used. Appropriate material characterization was achieved; its magnetic nature was identified and nanoparticles were collected in the magnetized tube at the end, thus avoiding nanoparticle release into the environment in order to respect basic concepts of nanotoxicology.
By depositing nanoparticles on a support of porous silica (Fe3O4@SiO2), an important stability of this composite material is obtained, thus increasing the yield of the reaction of adsorption of arsenic in the treated water.
Added to the above advantages is the possibility of recovery of the material, which allows substantial reduction of the overall cost of treatment. Regeneration of the composite material and capacity of adsorbent removal is made possible when using absorption-based treatments.
Performance of the composite material using arsenic solutions, in both laboratory solutions and in water for use in populations currently affected was validated by means of the filtration system assembled as a prototype laboratory. Although the maximum amount of admissible arsenic in water is surpassed by only 3 µg/L in the population under study, the cost of treatment is very high.
With the proposed system, the number of filters used can be increased, depending on the amount of arsenic to be treated in each particular case, and the volume of water in each system, and its parts may be changed independently, depending on the specific wear.
It was found that the impact of the pH is very high on the performance and water treatment under this system. According to the specific nature of each type of water to be treated it is essential?as is the case of the Bebedero System in Cañas?to lower the pH from 8.1 to 5.6. The results showed that when passing through the cleaning filters, the pH increases again.
The addition to the filtration system of an end tube to collect magnetized nanoparticles makes this kind of treatment an environmentally friendly option because it prevents the intrinsic nanotoxicity of these particles. Because of their small size, nanoparticles can enter directly into the cell, causing undetermined damage.
While in Costa Rica water sources are not highly contaminated with arsenic, as is the case of many countries worldwide, the National Water Institute has been concerned about giving effective treatment to water sources for massive consumption, where the amount of arsenic exceeds the maximum allowed (10 µg/L), although the treatments currently used in this country are costly.
The filtration system using downward continuous flow through magnetic composite material (Fe3O4@SiO2) is currently in the process of registration at the University, awaiting for funds for the construction of field systems.
The present work offers a highly efficient technological and low cost system that can be placed at the water outlet of wells prior to water disinfection. This method also prevents release of nanoparticles, taking into account basic principles of nanotoxicology and respect for the environment. Once treated and chlorinated afterwards, the water may be safely consumed by the population.
We would like to thank Vicerrectoría de Investigación y Extensión from Tecnológico de Costa Rica for their financial support. The researchers Dr Ricardo Starbird Pérez and MSc.Jorge Calvo Gutierrez from Escuela de Química and Ing. Luis Fernando Alvarado from Microscopy Laboratory, for their contributions to research. We are also grateful to the students Ana Victoria Cubero, José Pablo Cerdas, Ana Lucía Moya, Kalet Hernández and Marit Möller for their assistance.
The authors declare that there is no conflict of interest.
Virginia Montero-Campos,Allen Puente-Urbina, (2016) Continuous-Flow Removal of Arsenic in Drinking Water by Filtering down through Fe3O4@SiO2 Magnetic Composite. Journal of Water Resource and Protection,08,619-630. doi: 10.4236/jwarp.2016.85051