The Dye Sensitized Solar Cell (DSSC) plays an important role because of low material cost, ease of production and high conversion efficiency as compared to other thin-film solar cell technologies. The main objective is to create and find the best configuration of the solar cell based on materials that are inexpensive and highly efficient in solar energy conversion and subsequently test the efficiency of dye sensitized titanium dioxide solar cell. We begin the process with two glass plates coated with Fluorine tin oxide (FTO). Titanium dioxide is applied to the conductive side of one plate and the other plate is coated with graphite. A dye is adsorbed on to the TiO 2 layer and then the plates are sandwiched together. A drop of iodide electrolyte is then added between the plates. The tests carried out indoors under a lamp emitting all wavelengths in the visible spectrum were not found to provide consistent data due to substantial heating of the cell. The outdoor tests carried out in natural sunlight exhibited steady voltage at much higher level. Future research will involve the incorporation of quantum dots instead of the organic dye as a sensitizer. Quantum dots have the advantages of providing tunable band gaps and the ability to absorb specific wavelength.
The Dye sensitized solar cell (DSSC) is one of the huge and economic challenges in the 21st century. The main objective is to create and find the best configuration of the solar cell based on materials that are inexpensive and highly efficient in solar energy conversion and subsequently test the efficiency of dye sensitized titanium dioxide solar cell. The DSSC has reported high efficiency cells based on Titanium dioxide (TiO2) Nanoparticles and transparent conducting glass, natural dyes and iodine electrolyte solutions. The DSSC separates the two requirements as the charge generation is done at the semiconductor dye interface and the charge transport is done by the semiconductor and the electrolyte that is spectral properties optimization can be done by modifying the dye alone, while carries transport properties can be improved by optimizing the semiconductor and the electrolyte composition. Solar cell with high efficiency and low cost is necessary for sunlight capture and the conversion of light to energy [
There are a set of five different layers of components stacked in serial, including glass substrate, transparent conducting glass, Titanium dioxide TiO2 nanoparticles, organic dyes, electrolyte solution, and counter electrode is presented in
A typical cell structure is explained. In five different components:
1) Transparent Conducting Glass:
2) Titanium Dioxide (TiO2) Nanoparticles:
3) Dyes:
4) Electrolyte:
5) Counter Electrode:
First there is a layer In the front of the cell of glass substrate, this layer allows sunlight penetrating into the cell while conducting electron carriers to outer circuit is called Transparent conducting oxide. Second a layer of negatively doped TiO2 nanoparticles is used. The beneficial of TiO2 include high photosensitivity, high structure stability under solar irradiation and low cost [
The main idea and the mechanism of DSSC is quite obvious, photon of different energy in sunlight strike on the cell.
We begin the process of creating the solar cells with two glass plates coated with Fluorine Tin Oxide (FTO). This thin semiconducting layer allows charge to flow since glass in itself is nonconductive. The plates are first tested to find the conductive side of the glass. This conductive side will be covered with the other materials. Titanium Dioxide is applied to the conductive side of one plate by using a glass rod and rolling it on the plate until a neat coating is achieved. (Note: to keep the cells in place, it is important to place a piece of tape on the left and right sides of the plate so that the plate will not be moving around as shown in
This plate is then placed above a Bunsen burner for about 30 minutes so that the TiO2 is bonded to the plate. This process is called sintering and allows a three dimensional network to be achieved so that electron flow may occur. Following the sintering process, the plate is allowed to cool and is then placed in a bath of the dye Strawberries solution for 30 minutes as shown in
ticles comes into play. The increased surface area allows for a greater amount of dye molecules to be absorbed, which will be of great importance during the test. The amounts of electrons allowed to flow through the system are dependent upon the number of dye molecules present in the cells themselves. The greater surface area translates to an increased flow of electricity.
After absorbing the dye, the plates are placed to dry and bond. The bottom plate is placed in a hood (conductive side up) so that the counter electrode in the form of the thin carbon soot or platinum paste may be applied. The cells are sprayed so that an even coating is achieved. This process is repeated until the total number of desired cells is obtained. The individual pieces of glass are now ready to be combined. The electrolyte solution is then placed on the dyed side of the plate, enough to saturate the surface. The two plates are sandwiched together (conductive sides touching) and secured with binder clips. The cells are now ready to be tested and is presented in
The electrolyte solution consist of three different materials that we used in our research which is pure Iodine, Potassium Iodide and Ethylene glycol. We got about 0.1269 g of pure Iodine and 0.83 g of Potassium Iodide and we put both in 10 ml of Ethylene glycol.
Once preparation of the positive and negative electrodes is completed, 1 - 2 drops of electrolyte are placed on
the negative electrode and the two FTO plates are sandwiched together. The sandwiching of the two plates is offset so that each one has a small portion exposed so that an alligator clamp can be attached; the negative clamp goes on the TiO2 positive Sensitizer plate and the positive clamp goes on the counter electrode plate as shown in
Thus far in the research, the variables examined have been the sensitizing dye and the size of the conductive glass. The conductive glass used in all the cells is Fluorine Tin Oxide (FTO) glass. Moreover the Nano crystalline matrix has been Titanium dioxide (TiO2) throughout. An outline of our variables is displayed in
Our most efficient reproducible data was achieved in the second trial. The cell produced a potential of ~140 mV. The highest potential and current readings have been recorded while using Fluorine Tin Oxide (FTO) as the negative and positive plates. The readings carried out indoors under a lamp emitting all wavelengths in the visible spectrum were not found to provide steady/consistent data due to substantial heating of the cell. Test results from different cells varied greatly, even within a series. This makes it very obvious that variability exists in one of the factors, most likely the electrolyte mediator. The most probable reason for this observation is that the electrolyte is evaporating out from between the two plates due to the high temperatures under the lamp. Using a filter helps greatly with the heat, but the electrolyte still seems to undergo degradation over time with the exposure to the light.
One of the emerging problems in durability of the solar cells is the nature of the electrolyte. The liquid electrolyte can undergo evaporation, leaking, charge separation/recombination at the TiO2/electrolyte interface or degradation. There may be a back-reaction that takes place between the conduction-band electrons from the ex-
cited sensitizer and the oxidized dye molecules themselves, or with the oxidized electrolyte species
latter recombination process is:
These processes have been a concern for other researchers producing TiO2 based solar cells. Literature reviews would have to be conducted to examine how this recombination process could be stopped or lessened. The use of a filter has also proven to lend a significant hand in decreasing the heat reaching the cell. It is also
S. No. | Size of Glass | Dye | Voltage obtain |
---|---|---|---|
1 | 4 (inches) | Strawberry | ~80 (mv) |
2 | 2 (inches) | Strawberry | ~140 (mv) |
3 | 2 (inches) | Turmeric powder | ~40 (mv) |
4 | 1 (inches) | Strawberry jam | ~30 (mv) |
very clear that we must obtain a more realistic lamp for the environment to mimic the true full solar spectrum. Only then will we be able to see the real life practicality of the cells.
Incorporating what we have seen with our plans for the future, we feel that there are many things we may try in order to improve our results and provide insight into their nature. We are also looking into the use of quantum dots to replace our dye. Quantum dots may be manipulated to absorb a specific wavelength of light. Their absorption exists in a direct relationship with their size. If able to make set wavelengths for absorption, the cells could be arranged in series to collect energy from a variety of areas in the spectrum. Future research will involve the incorporation of quantum dots instead of the organic dye as a sensitizer. Quantum dots have the advantages of providing tunable band gaps and the ability to absorb specific wavelength, including UV light, from the solar spectrum. We also intend to explore different sealants and solid electrolytes such as conductive polymers to prevent the electrolyte evaporation.
Ari A.Mohammed,Alan S. SaidAhmad,Wafaa A.Azeez, (2015) Fabrication of Dye Sensitized Solar Cell Based on Titanium Dioxide (TiO2). Advances in Materials Physics and Chemistry,05,361-367. doi: 10.4236/ampc.2015.59036