The present paper deals with gelatin nanofibres functionalized with silver nanoparticles, prepared by electrospinning using solutions of gelatin mixed with silver nitrate (AgNO3). As a common solvent for gelatin and silver nitrate (AgNO3), a mixture of acetic acid and water (70:30 v/v) was selected. In this system, acetic acid was used as a solvent for gelatin, and at the same time reducing agent for silver ions in solution. Silver nanoparticles (nAg) were stabilized through a mechanism that involves an interaction of the oxygen atoms of the carbonyl groups of gelatin. The viscosity and the conductivity of the gelatinous solutions were found to increase with the solution concentration. There is an observed decrease in the viscosity of the nAg containing gelatin solutions with the aging time increasing, whereas the conductiity of the AgNO3—containing gelatin solutions was greater than that of the base gelatin solution. The gelatin nanofibres functionalized with silver nanoparticles were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and antimicrobial test. The results of investigations by TEM and XRD confirmed the presence of silver nanoparticles with diameters in the range of (2 - 10 nm), uniformly distributed over the surface of smooth nanofibres with an average diameter of 70 nm. The release of silver ions from both the 2- and 4-hrs crosslinked nAg containing gelatin fiber mats by a total immersion method in buffer and distilled water occurred rapidly during the first 60 minutes, and increased gradually afterwards. Lastly, the tests demonstrated that gelatin/Ag nanofibers have a good antimicrobial activity against some common bacteria found on burned wounds. The anti-bacterial activity of these materials was greatest against Staphylococcus aureus, followed by Escherichia coli, and Pseudomonas aeroginosa ≈ Candida albicans.
One of the very important tissues for human health is the skin, which plays the role of an interface between body and environment, and acts as a protective barrier against physical, chemical and biological aggressions. Skin is actually a complex systems involved in the processes of absorption and excretion, showing a selective permeability for some important substances in human metabolism [
The currently increasing incidence of skin diseases caused a significant demand for skin replacement materials which in many cases cannot be assured from natural sources. It also increased the demand for skin regrowth substrates used in treating skin lesions, which stimulated tissue engineering to develop new biodegradable materials. These materials can promote adhesion, development and migration of fibroblasts which are necessary for a good quality reepithelization. Skin substitutes used today are expensive and have limitations concerning the biocompatibility, making their use sometimes risky. Various technologies have been developed to produce biomaterials used for skin lesions treatment of wound dressings. One of the very interesting nanotechnologies investigated now is polymer solutions spinning in an electrostatic field (electrospinning), which can be applied to solutions of various natural and synthetic polymers, such as gelatin, collagen, chitosan, fibrinogen, silk, polylactic acid, hyaluronic acid, obtaining non-woven nanofibres membrane with thicknesses in a range that goes from a few tens of nanometers to over one thousands of nanometers [
Natural biopolymers have high viscosity and very low solubility in common organic solvents, which makes them difficult to process by solution spinning in an electrostatic field. Natural polymers dissolve well in 1,1,1,3,3,3-hexafluoro-2-propanol and trifluoroacetic acid [4-7], which are toxic and expensive solvents, features that limit their use in applications on an industrial scale.
Due to its natural abundance and inherent biodegradability in physiological environments, gelatin is widely used in food, cosmetic, pharmaceutical and medical applications [
Because of the inherent properties of gelatin and the unique characteristics of the e-spun fibers, e-spun gelatin fibers are ideal materials to be used as scaffolds for cell and tissue culture, carriers for topical/transdermal delivery of drugs, and wound dressings.
Bacterial colonization and subsequent infection can interfere with the wound healing process by producing various substances (e.g., toxins, proteases and proinflammatory molecules) which may cause an excessive and prolonged inflammatory response of the host tissues [16-19].
Idealantimicrobial dressings should have a number of key attributes, including provision of a moist environment to enhance healing [
Silver nanoparticles (nAg) are well known for strong antibacterial properties and no harm on human cells [
Some polymers have been successfully used for the synthesis of metal nanoparticles. The binding interaction between polymer and the metal nanoparticles, polymer stabilizes the metal nanoparticles—polymer composite, and hence, the nanoparticles attached to the polymer chains will be dispersed in the solution when the composite dissolves. Therefore, it is possible to prepare the metal nanoparticles containing nanofibers via electrospinningthe solution of the metal nanoparticle—polymer composite, if the size of nanoparticles is small enough.
In the present study, mats of gelatin fibers containing nAg were prepared by electrospinning. The proposed use of these e-spun fiber mats is as wound dressing pads. Glutraldhyde (GTA) vapor was used to improve the stability of the fiber mats in a moist environment. The nAg-containing gelatin fiber mats were characterized for their release characteristics of the as-loaded silver, as well as for their antibacterial activity against some common bacteria found on burn wounds.
Gelatin (from porcine skin, type A) was purchased from Sigma Aldrich.Silver nitrate (AgNO3; 99.9% purity) with a molecular weight of 169.87 was purchased from Sisco Research Laboratories PVT.LTD (SRL). Acetic acid (96%) (C2H4O2) with a molecular weight of 60.05 was purchased from (Adwic) El-Nasr Pharmaceutical Chemicals Co. Glutaraldehyde, (GTA; 25 wt% solution in water) [HCO(CH2)3CHO] was purchased from Sigma Aldrich. Glycinepure lab. Chemical (99%) with a molecular weight of 75.07 was purchased from (Adwic) El-Nasr Pharmaceutical Chemicals Co. All chemicals were of analytical reagent grade and used without further purification.
AgNO3 was first dissolved in a quantity of 70:30 v/v glacial aceticacid/distilled water. A metered weight of gelatin powder was then added into the as-prepared AgNO3 solution. Slight stirring was used to expedite the dissolution and homogenize the solution. The concentration of the base gelatin solution was 50% w/v (based on the volume of the mixed solvent), and the amount of AgNO3 was 2.5% w/w (based on the weight of the gelatin powder). To investigate the effect of aging time on the formation of nAg, the AgNO3-containing gelatin solution was aged in a brown bottle while being stirred for varying periods of time. Some of the aged AgNO3-containing gelatin solutions were characterized for shear viscosity and conductivity using a Brookfield DV-III ultra-programmable rheometer and a professional portable conductivity meter HC3010, trans-instruments. The presence of silver only in the form of crystallized metal nanoparticles is certified by the X-ray diffractogramme. The morphology of the electrospun fibers was observed under a Quanta FEG 250 FEI, Holanda scanning electron microscope (SEM) after gold coating by an Ion sputtering with 15 mA for 3.5 minutes each sample. The diametets of the as formed nAg was observed under Jeol Jem-1230 transmission electron microscope (TEM).
The base gelatin solution and the AgNO3-containing gelatin solution that had been aged for 12 h were fabricated into fiber mats by e-spinning. Firstly, each of the as-prepared solutions was loaded into a standard 3-mL plastic syringe, the open end of which was attached to a needle, which was used as the nozzle. Apiece of aluminum (Al) sheet was placed below the capillary tip as the ground collector. Capillary was connected with a high voltage power supply (Model Glassman high voltage, NJ08829), which could generate positive DC voltages. A High-Voltage DC powersupply was used to charge the solution by attaching the emitting electrode of positive polarity to the nozzle, and the grounding one to the collecting device. An electrical potential of 20 kV was applied across a distance of 18 cm between the tip of the needle and the outer surface of the collection device (i.e., collection distance).
Crosslinking of both the neat and the nAg-containing gelatin fiber mats was carried out by soaking the fiber mat samples in 2 wt% glutaricdialdehyde (GTA/ethanol) for different time intervals. After exposure, the samples were washed with 0.2M glycine in order to remove the unreacted GTA.
The neat and the nAg-containing gelatin fiber mats were examined either qualitatively or quantitatively for the size and/or the amount of both the individual fibers and the as-formed nAg using a Quanta FEG 250 FEI, Holandascanning electron microscope (SEM) and an energy dispersive X-ray (EDX), a Jeol Jem-1230 transmission electron microscope (TEM). The average diameters of both the fibers and the as-formed nAg were determined from SEM and TEM images, respectively. FT-IR measurements were performed in a FT-IR Spectrometer 1760× (Perkin-Elmer) to verify the composition of fibers from functional groups.
Prior to the release assay, the actual amount of silver in the uncrosslinked nAg-containing gelatin fiber mat specimens (2 cm × 2 cm) and the form of silver that was released from the specimens were needed to be determined. The in-vitro release of silver was carried out by the addition of a releasing medium (buffer, and distilled water) to attain a total volume of 5 ml.
The release characteristics of silver from the nAgcontaining gelatin fiber mats that had been soaked in the GTA solution for 2 hrs or 4 hrs was assessed in buffer, and distilled water as the releasing medium. The specimens cut from the fiber mat samples (2 cm × 2 cm) were immersed in 5 ml of the releasing medium at room temperature.
At a specified immersion periods ranging between 0 and 7 d, the releasing medium was quantified for the amount of released silver, using Inductively Coupled Plasma (ICP). At each time point, the measurements were carried out in triplicates. The obtained data were carefully calculated to obtain the cumulative amount of released silver. The cumulative release profiles of silver were expressed based on either the unitweight of the specimens or the unit weight of the actual amount of silver in the specimens. The results were presented in term of cumulative release as a function of release time.
Where Mt was the amount of silver released at time t, the amount of silver added to electrospinning solution was regarded as M∞.
The antibacterial activity of the e-spun fiber mats, both from the base solution and the 12 h-aged AgNO3-containing gelatin solution were tested against aerobic bacteria commonly found on burn wounds: e.g., E. coli (Gramnegative), Pseudomonas aeroginosa (Gram-negative), S. aureus (Gram-positive), and Candida albicans. The assessment was conducted based on the disc diffusion method. If inhibitory concentrations were reached, there would be no growth of the microbes, which could be seen as a clear zone around the disc specimens. Those were photographed for further evaluation.
Prior to e-spinning, some of the AgNO3-containing gelatin solutions that had been aged for different time intervals were measured for their viscosity and conductivity. The observed decrease in the shear viscosity of the solutions with increasing the aging time could be a result of a considerable hydrolytic degradation of gelatin molecules. While the conductivity of the AgNO3-containing gelatin solutions was greater than that of the base gelatin solution. This could be as a result of the presence of Ag+ and NO3− ions in the solution as shown in figure 1 [
In order to determine electrospun gelatin fiber structure before and after crosslinking, FT-IR was carried out on the electrospun fibers before and after crosslinking.
FTIR measurements were conducted on uncrosslinked gelatin and crosslinked gelatin in order to determine whether crosslinking of the electrospun gelatin affected the gelatin structure or not (figure 2).
The uncrosslinked electrospun gelatin had an amide I peak (C=O stretch) at 1636 - 1640 cm−1, amide II peak (N-H bend and C-H stretch) at 1542 - 1544 cm−1, amide III peak (C-N stretch plus N-H in phase bending) at 1240 cm−1 and amide A peak (N-H stretching vibration) at 3316 cm−1, which are the distinguishing features of gelatin.
The spectrum of the crosslinked gelatin is shown in detail in figure 2. In addition to the previously mentioned peaks, a strong peak at 1450 cm−1 was observed in the crosslinked gelatin due to aldimine absorption [
The characteristic absorption of the aldimine groups
occurred at 1450 cm−1. Furthermore, additional peaks were observed at 1470 - 1570 cm−1, which increased as the crosslinking reaction was proceeded (figure 2). To more conclusively determine if crosslinked gelatin was successfully fabricated, we expanded the FT-IR spectra from 1100 - 1750 cm−1 (figure 2). In this region of the FT-IR spectra, the amount of CH=N groups increased [
This technique proved crosslinking of gelatin using glutaraldehyde during the crosslinking process, which is an essential condition to limit the insolubility and increase the biocompatibility of gelatin for applications in the biomedical field [
XRD was used to confirm the success of silver nanoparticles incorporation into the electrospun gelatin. The patterns of electrospun gelatin are not crystalline and appear amorphous (not shown).The XRD pattern of electrospun gelatin fiber mats was shown in
This is implies the presence of the Ag nanoparticles which are embedded in the gelatin fibers.
emphasized that, at 12 h of aging, silver was present both as Ag ions and as elemental Ag; but for convenience, nAg was used loosely to denote both forms of silver that were present in the e-spun fiber. Quantitative assessment by EDX for the amount of the elemental Ag in the e-spun fiber mat from the 12 hrs aged AgNO3-containing gelatin solution indicated a value of 0.25 wt%.
Here, the formation of the nAg nuclei was postulated in order to originate due to ionic interactions between the Ag+ ions and either -NH2 or -COOH groups, or both, on the gelatin chains, according the following schemes:
or due to simple binding between Ag+ ions and lone pair electrons of N and O atoms in the -NH2 and -COOH groups [
Since gelatin is water-soluble, an e-spun gelatin fiber mat can easily dissolve either partially or completely, losing its fibrous structure when coming into contact with an aqueous medium. It may partially dissolve and loose its fibrous structure upon an amount of exposure to
a high ambient humidity (e.g., 80% - 90%) for a certain period of time. To extend the use of e-spun gelatin fiber mats in applications that require exposure to an aqueous medium or high humidity, further crosslinking is necessary. Among the various chemical systems used to crosslink an e-spun gelatin fiber mat.
GTA is seemingly the most suitable, as it is economical and does not compromise the fibrous structure of the e-spun membrane. Here, the neat and the nAg-containing e-spun gelatin fiber mats were further crosslinked by GTA aqueous solution for either 2 or 4 hrs. Crosslinking treatment did not affect the amount of nAg in the crosslinked e-spun gelatin fiber mats [
for 2 hrs) and finally to brown (for the fiber mats that had been crosslinked for 4hrs). They also shrunk slightly from their original dimensions. The change in color of the gelatin upon crosslinking with GTA is caused by the formation of aldimine linkages (-CH=N-) between the free amino groups of lysine or hydroxylysine amino acid residues of the protein and the aldehyde groups of GTA [25,30].
Moreover, the shrinkage of the fiber mats is responsible for the observed decrease in the size of inter-fibrouspores as well as the observed decrease in the thickness of the fiber mats and the observed increase in the diameters of the individual fibers.
Here, it is postulated that the as-formed nAg dissolved readily upon contact with the releasing medium, and that both the remnant and the dissolved Ag+ ions were released into the medium during the release studies.
The release characteristics of Ag+ ions from either 2 hrs or the 4 hrscrosslinkednAg-containing electrospun gelatin fiber mats samples, was investigated by the total immersion method in one of the releasing media (i.e., the buffer, and distilled water). The cumulative amount of Ag+ ions released from these materials is reported in
Concerning the 2 hrs crosslinked nAg-containing espun gelatin fiber mat specimens, the cumulative amount of Ag+ ions released from the specimens in distilled water was the same as that released in the buffer during the first 60 min of submersion, while that released from specimens in the buffer was increasingly greater afterwards. A similar trend was observed for the 4 hrs crosslinked nAg-containing e-spun gelatin fiber mat specimens, in which the cumulative amount of Ag+ ionsreleased from these specimens in distilled water was approximately the same as that amount released in the buffer during the first 60 min of submersion.
Between the two sample types, the cumulative amount of Ag+ ions released from the 2 hrs crossinked nAg-containing e-spun gelatin fiber mat specimens in any type of releasing medium was systematically greater than the amount released from the 4 hrs crosslinked ones. This is possibly a result of the observed lower weight loss and water retention of the 4 hrs crosslinked nAg-containing e-spun gelatin fiber mat specimens in comparison with those of their 2 hrscrosslinked counterparts.
Quantitatively, the cumulative amount of Ag+ ions released from the 2 hrscrosslinkednAg-containing e-spun gelatin fiber mat specimens in the buffer increased from ~13.9 mg/g of the specimens at 60 min, to attain a final value of ~26.9 mg/g of the specimens at day 7. For the 4 hrs crosslinked nAg-containing e-spun gelatin fiber mat specimens, the amount of Ag+ ions increased from ~ 12.9 mg/g of the specimens at 60 min to ~22.1 mg/g of the specimens at day 7. In distilled water, the cumulative amount of Ag+ ions released from the 2 hrs crosslinked nAg-containing e-spun gelatin fiber mat specimens increased from ~14.5 mg/g of the specimens at 60 min to ~ 22.2 mg/g of the specimens at day 7. For the 4 hrs crosslinked nAg-containing e-spun gelatin fiber mat specimens, it increased from ~12.5 mg/g of the specimens at 60 min to ~20.1 mg/g of the specimens at day 7.
The possible reason for the observed greater release of Ag+ ions from both types of samples in buffer than in distilled water could be due to the protonation of the amino groups of gelatin. The pH value of the buffer medium was supposedly less than the isoelectric point (PI) of the type-A gelatin (i.e., PI ≈ 7 - 9) used in this work [
The potential use of nAg-containing e-spun gelatin fiber mats as functional wound dressings was assessed by observing their antibacterial activity (based on the disc diffusion method) against some common bacteria found on burn wounds: Escherichia coli, Pseudomonas aeroginosa, Staphylococcus aureus and Candida albicans. The activity of the neat e-spun gelatin fiber mats against these bacteria was used as a control. Since both the neat and the nAg-containing e-spun gelatin fiber mat specimens were crosslinked with GTA vapor to enhance their stability in an aqueous medium, the effect of glycine treatment on the neat e-spun gelatin fiber mats, and then Ag-containing e-spun gelatin fiber mat specimens to neutralize unreacted aldehyde groups of GTA [
It should be noted that the initial diameter of all the specimens was the same. However, in a wet condition, the specimens swelled, resulting in the observed dimensional change.
According to the results obtained, all of the crosslinked neat e-spun gelatin fiber mat specimens, with glycine treatment, showed no activity against the tested bacteria. For the nAg-containing specimens, inhibitory zones were evident.
Specifically, the antibacterial activity of the nAg-containing specimens, regardless of the sample type, was greatest against Staphylococcus aureus, followed by Escherichia coli, and Pseudomonas aeroginosa ≈ Candida albicans respectively figure 8.
Feng et al. [
with Ag+ ions, both Escherichia coli and Staphylococcus aureus underwent a series of events that led to their demise. Specifically, they postulated that the bactericidal mechanism was based on the ability of Agions to bind with certain chemical functionalities of the cell wall, the cytoplasm and the nucleus. This causes DNA molecules to condense, the cytoplasmic membrane to detach from the cell wall, and the cell wall to become severely damaged [
Silver ions (Ag ions), known for their broad-spectrum antimicrobial activity, were reduced into silver nanoparticles (nAg) in a base gelatin (type A, porcine skin) solution (50% w/v in 70 vol% acetic acid) containing 2.5 wt% AgNO3 (based on the weight of the gelatin powder). The presence of nAg in the AgNO3-containing gelatin solution was first realized after it had been aged for at least 12 hours. The average diameters of the as-formed nAg ranged between ~2 and ~10 nm. Both the neat gelatin and the 12 hours aged AgNO3-containing gelatin solutions were fabricated into ultrafine fibers by electrospinning (20 kV/18 cm). The average diameters of these fibers were in the range of 98 - 345 and 154 - 390 nm respectively. Both the neat and the nAg-containing gelatin fiber mats were further crosslinked in order to improve their stability in an aqueous medium or a high humidity atmosphere by 2% glutaraldehyde (GTA) aqueous solution. Crosslinking not only caused the color of the cross-linked gelatinfibers to change, but also was responsible for the fusing and shrinking of the crosslinked fiber mats. The release characteristics of Ag ions from either the 2 or the 4 hrs-crosslinked nAg-containing e-spun gelatin fiber mats was investigated by the total immersion method in acetate buffer, and distilled water at room temperature. The cumulative release of Ag ions from the samples in the acetate buffer and distilled water occurred rather rapidly during the first 60 minutes after submersion in the releasing medium, and increased gradually afterwards. Lastly, the antibacterial activity of these materials (with glycinewashing) was greatest against S. aureus, followed by E. coli, P. aeroginosa ≈ Candida albicans respectively. The results confirmed the structure of silver nanoparticles containing nanofibers which could find important application in the biomedical field, e.g., as the wound dressings, due to the advantages of gelatin, and silver nanoparticles.