We synthesized Zn0.8Fe2.2O4 ferrite powders by coprecipitation and hydrothermal techniques and analyzed the mor-phology and magnetic properties. The morphology and structure of the Zn ferrite powders were investigated using Scanning Electron Microscopy (SEM) and X-ray Diffraction (XRD) identifying the crystallization planes. Magnetic hysteresis curves were obtained for the Zn ferrites samples.
Ferrite nanopowders have scientific and technological importance in recent years due to their magnetic properties and have a broad range of applications such as magnetic recording, ferrofluids, magnetic resonance imaging, biomedicine, catalyst, etc. [1,2]. They have been used for high-frequency transformers cores, rod antennas, radio frequency coils and more recently as radar-absorbing materials [3,4]. Spinel ferrites are materials with good magnetic and electronic properties, which depend strongly on the cation distribution among the tetrahedral and octahedral sites [
In this work we analyzed the morphological and magnetic properties of Zn0.8Fe2.2O4 powders synthesized by the coprecipitation and hydrothermal techniques.
The Zn0.8Fe2.2O4 ferrite powders were prepared by coprecipitation (sample S1 in
To obtain Zn0.8Fe2.2O4 ferrite powders using the coprecipitation method we have mixed iron nitrate, zinc nitrate and sodium hydroxide with bidistilled water. The solution was heated to 90°C during 5 hours on a Magnetic Agitator at 400 rpm. To obtain the final zinc ferrite powder the solution was then cleaned with bidistilled water and alchool, filtered for 5 hours for neutral pH and calcinated in a Nabertherm Oven at 200°C for 2 hours.
Using the hydrothermal method for synthesing zinc ferrite we combined iron nitrate and zinc nitrate with bidistilled water and sodium hydroxide and introduced it in an autoclave for 5 hours at 200°C in an Heraeus 6060 UT Stove. To obtain the zinc powder the final solution was cleaned and filtered with bidistilled water for 5 hours to obtain neutral pH and then dried.
Performing Scanning Electron Microscopy (SEM) with an FEI Company microscope, type Inspect S we analyzed the structure of Zn0.8Fe2.2O4 powder and show typical micrographs in Figures 1(a),1(b). For the sample S1 shown in
differences in the aggregation of the material for the two synthesis techniques.
The measurements were done in the 2θ range of 20°- 90° for samples of zinc ferrites obtained by the two techniques. The calculated distance between the main crystal planes was 0.2 nm. Well defined diffraction peaks corresponding to the characteristic planes (311), (511) and (440) apear at 35°, 57° and 64°. The intensity of the peaks reveal that the sample S2 obtained by the hydrothemal method has bigger particles then the sample S1 obtained by coprecipitation. Other wide diffraction peaks corresponding to (220), (442), (553) and (731) planes are also present with low relative intensities asumed to arise from an amorphous structure. Using the Scherrer Equation [
We analyzed the magnetic behavior of the zinc ferrite obtained by coprecipitation and hydrothermal methods by measuring the magnetization as a function of an applied 50 Hz, AC magnetic field amplitude up to 160 kA/m [
In Figures 3(a),3(b) the M-H curves of the sample S1 and S2 obtained by the two synthesis methods are given.
In the case of the sample S1 obtained by coprecipitation a superparamagnetic-like behavior was observed, with a maximum magnetization of 200 A/m at 160 kA/m. The maximum magnetization of the sample S2 obtained by the hydrothermal method is 750 A/m for a maximum applied field of 160 kA/m, the magnetic remanence was 70 A/m and coercivity about 6.40 kA/m.
The analysis of the morphology and structure by electron microscopy for zinc ferrites shows that the powders are composed of particles with diameters bellow 100 nm for both S1—coprecipitation and S2—hydrothermal samples. From the x-ray diffraction measurements we observe for both synthesis methods the crystal planes (311), (511)
and (440) though the intensity of the peaks of the zinc ferrite obtained by the hydrothermal method gave bigger particles by about 10% as compared to the coprecipitation method. These diffraction peaks correspond to the main diffraction planes in zinc ferrites although some amorphous material structure is observed also by the wide and small peaks of planes (220), (442), (553) and (731). We also observed that the structure for the sample S2—hydrothermal is more crystalline while for the sample S1—coprecipitation the surface structure is more homogenous.
From the hysteresis measurements the Zn0.8Fe2.2O4 powders obtained in this investigation we obtained a ferromagnetic behavior [
Two synthesis methods were investigated to obtain the zinc ferrites with magnetic properties usable for shielding applications.
The zinc ferrite nanopowder synthesized by the hydrothermal technique shows a higher magnetic behavior as seen from the hysteresis curves. From x-ray diffraction measurements the zinc ferrite particles for sample S2— hydrothermal have bigger sizes compared to the samples S1—coprecipitation. The ferrite nanopowder obtained by both methods show small particles with diameters typically bellow 100 nm resting on a more planar structure.
We conclude that the synthesis method has important influence on the morphology, structure and magnetic behavior of the zinc ferrite nanopowders and in our case the hydrothermal method gave superior magnetic results.