Nano size lithium ferrite was prepared through aerosol route and characterized using TEM, XRD, magnetic measurements and Mössbauer spectroscopy. The particle size of as obtained samples were found to be ~10 nm through TEM, that increases upto ~80 nm on annealing at 1200 oC. The unit cell parameter ‘a’ calculated using XRD, confirms the formation of ?-LiFe5O8. Room temperature Mössbauer spectra of as obtained sample of all the ferrites exhibited broad doublet suggesting super paramagnetic nature. This doublet further resolved into two doublets and assigned to the surface region atoms and internal region atoms of the particles. The annealed samples (1200 oC) show broad sextets, which were fitted with two sextets indicating different local environment of both tetrahedrally and octahedrally coordinated Fe-cation. Cation distribution obtained from the X-ray, magnetic and Mössbauer data confirms that the three fifth of the iron atom goes in to the octahedral site.
Lithium iron oxides LiFe5O8 are of increasing scientific interest and are also promising candidates for cathode materials in rechargeable lithium batteries [1,2]. Its high curie temperature, high saturation magnetization and hysterisis loop properties after performance advantages over other spinel ferrites used in microwave frequency and magnetic core applications [1–4]. Two separate crystallographic ordered and disordered forms of LiFe5O8 have been isolated. A super structured form in which lithium and iron atoms are ordered is called aLiFe5O8 and has a subgroup of Fd-3m with a primitive cubic unit cell (space group P433 or P413, a = 8.3372 Å) [
The present work deals with the synthesis of nano particles of lithium ferrite via aerosol route at a temperature ~600 oC. This avoids the precipitation of a-Fe2O3 or Fe3O4. On the other hand in aerosol method particle size, degree of agglomeration, chemical homogeneity can be controlled with relative ease. Aerosol method has the potential of producing multicomponent materials and production of powder by this method is commercially viable [10,11].
The sample so prepared was characterized using transmission electron microscope (TEM), X-ray diffractometer (XRD), magnetic and Mössbauer spectrometer. This work is an attempt to investigate the cation distribution using XRD, magnetic and Mössbauer measurements.
Nano particles of lithium ferrite (LiFe5O8) were prepared via aerosol route using a setup described in our earlier papers [12–14]. The desired proportions of lithium and iron nitrates were weighed and dissolved in water to prepare 5 x 10-2 M solutions. Air pressure, sample uptake and furnace temperature were maintained at 40 psi, 3-4 ml/min and ~600 oC respectively during preparation. The ferrite powder was deposited on the teflon coated pan.
The elemental analysis was carried out on an electron probe micro analyzer (EPMA) (JEOL, 8600 M) and atomic absorption spectrophotometer (AAS) (GBC, Avanta),
while the particle morphology was examined by transmission electron microscope (TEM) (Philips, EM400). The X-ray diffraction (XRD) studies were carried on Xray spectrometer (Bruker AXS, D8 Advance) with FeKa radiation and magnetic measurements were made on a vibrating sample magnetometer (VSM) (155, PAR). Mössbauer spectra were recorded on a constant acceleration transducer driven Mössbauer spectrometer using 57Co(Rh) source of 25 mCi initial activity. The spectrometer was calibrated using a natural iron foil as well as recrystallized sodium nitroprusside dihydrate (SNP) as standards.
Elemental analytical data for Li and Fe were obtained by EPMA. About 2 mm thick pellet was prepared, fixed on the sample holder and coated with the carbon to make them conducting. Elemental analysis was carried out at eight different points on each pellet with spot size of ~10 mm dia and results were found to be consistent. The results were further verified by atomic absorption spectrophotometer.
The TEM micrograph of a very small amount of as obtained samples placed on the carbon grid shows spherical particles of ~100-300 nm size as reported in our earlier papers [13,14]. However, after agitating ultrasonically and taking the suspended particles on the carbon grid shows well separated particles of size ~10 nm. The micrographs for sample annealed at 1200 oC shows that the particle size increases with annealing temperature. It is widely believed that the net decrease in free energy of solid-solid and solid-vapour interface provides the necessary driving force for particle growth during annealing process [
The powder X-ray diffractographs of as obtained sample and that of annealed at various temperatures is given in
X-ray diffraction intensity calculations were carried out using the formula suggested by Buerger [
Ihkl = │Fhkl│2PLp
where, notations have their usual meanings. It is well known that, the intensity ratio of planes I(220)/I(400), I(220)/I(440) and I(400)/I(440) are considered to be sensitive to the cation distribution, therefore, these ratios were used in estimating cation distribution. Finally, the cation distribution is estimated from X-ray intensity calculations for the best fit cation distribution and found to be [Fe2]A[LiFe3]BO8.
Magnetic hysteresis loops, at room temperature were recorded for the as obtained as well as annealed sample. Typical loops for as obtained LiFe5O8 and after annealing at 1200 oC are shown in
ple exhibits no hysteresis, which may be attributed to superparamagnetic relaxation as confirmed by XRD. The values of saturation magnetization and magnetron nB (the saturation magnetization per formula unit in Bohr magnetron) at 300 K for the annealed sample were obtained from the hysterisis loop and found to be 66.92 emu/g and 4.99 respectively. According to Neel’s two sublattice model of ferrimagnetism, the magnetic moment per formula unit (mB), nBN(x) is expressed as:
nBN(x) = MB(x) – MA(x)
where MB and MA are the Band Asublattice magnetic moment in mB respectively. The nBN(x) value was calculated using the ionic magnetic moments of Fe3+ and Li+ which are 5 mB and 0 mB respectively. The calculated value (5 mB) clearly indicates the inverse spinel structure with lithium and three fifth of the total Fe3+ occupying octahedral sites and two fifth occupying tetrahedral site.
bution of surface region atoms is 42 % of total area of the experiment spectrum. This is in agreement with the percentage (44 %) of the volume of surface region atoms to the total volume of the particle with an average grain size (8 nm) by Ma et al. [
The Mössbauer spectra recorded at 300 K after annealing at 1200 oC (
Lithium ferrite has been prepared successfully with particle size ~10 nm by aerosol route with high yield. After annealing the sample at 1200 oC confirms the formation of single phase a-LiFe5O8. The cation distribution obtained from the X-ray, magnetic and Mössbauer data confirms that the three fifth of the iron atom goes in to the octahedral site.
Since Lithium ferrite and mixed lithium ferrites have very high potential for cathode materials in rechargeable lithium batteries, microwave applications and, especially as replacements for garnets, due to their low cost. The squareness of the hysteresis loop and superior temperature performance are other prominent advantages that have made them very promising candidates for application in microwave devices. In this communication we report our studies on the synthesis of lithium ferrite and their magnetic properties and the work is going on with the mixed lithium ferrites to improve their magnetic properties and their applications in different fields.