Preparation of Microcapsules Containing Phase Change Material and Silicon Carbide Powder with Interfacial Polycondensation Reaction Method

Ryo Morita, Natsukaze Saito, Yoshinari Taguchi, Masato Tanaka*

Graduate School of Science and Technology, Niigata University, Niigata, Japan

Email: *tanaka@eng.niigata-u.ac.jp

Copyright © 2015 by authors and Scientific Research Publishing Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY).

http://creativecommons.org/licenses/by/4.0/

Received 28 February 2015; accepted 21 March 2015; published 26 March 2015

ABSTRACT

The fundamental experiments were performed to establish the operational conditions required to prepare the microcapsules containing paraffin wax as a phase change material (PCM) and SiC powder with the interfacial polycondensation reaction. It was investigated how SiC powder affected a few characteristics of microcapsules such as the diameters of microcapsules, latent heat storage density, thermal responsibility and supercooling. In the experiment, the concentration of oil soluble surfactant, the revolution speed of impeller for preparing the (O/W) emulsion and the added weight of SiC powder were changed stepwise. The microcapsules containing PCM in which SiC powder was dispersed could be prepared well and characterized. The diameters of microcapsules increased by containing SiC powder and the content of SiC powder could be increased by performing surface modification of SiC powder. Latent heat storage density decreased with the content of SiC powder. Supercooling of PCM and thermal responsibility could be improved to some degree by containing SiC powder.

Keywords:

PCM Microcapsule, Latent Heat Storage, Silicon Carbide, Interfacial Polycondensation Reaction, Paraffin Wax, Thermal Composite

1. Introduction

Hitherto, many kinds of microcapsules have been prepared and applied in the various fields such as thermal energy storage, cosmetics, drugs, information recording materials, paintings and so on [1] -[4] . Among of these microcapsules, the microcapsules containing PCM have attracted great attention from industrial communities [5] -[8] , because the microcapsules containing PCMs can absorb, store and release latent heat according to the PCM species and the amount of microencapsulated PCM [9] -[11] .

The PCM microcapsules have been prepared by using suspension polymerization [12] -[14] , in-situ polymerization [15] [16] , interfacial polycondensation reaction [17] -[19] and miniemulsion polymerization [20] and applied in fabrics, building materials and automobile engine. The PCM microcapsules thus prepared are the fine particles with the core-shell structure which have the PCM core surrounded by a polymer shell. It is necessary that the polymer shell prevents PCM from leaking during the process of phase change and overcome mechanical stress. The bulky PCM is given the extremely large heat transfer area by being microencapsulated. However, supercooling is easy to occur due to the limited smaller hollow. Furthermore, the microcapsules made of a polymer shell and PCMs such as paraffin wax with low thermal conductivity have a less heat conductivity. However, it may be expected that these demerits could be improved by adding solid powder, which plays as a supercooling prevention agent and an improvement agent for heat conductivity. Namely, if solid powder with higher thermal conductivity could be dispersed in PCM, relative thermal conductivity of microcapsules could be improved. Also, if solid powder plays as a nucleating agent, super cooling could be prevented at the same time.

Thus, the microcapsules made of PCM and a filler with higher thermal conductivity, namely, the thermal composites may be prepared with the preparation methods stated above by adding solid powder into PCM. In these preparation processes, first, it is necessary to form the oil droplets (PCM-droplets) of PCM containing solid powder, namely, the stable (S/O)/W dispersion.

In general, the dispersing behaviour such as coalescence and break up of dispersed oil droplets are affected by containing solid powder in the oil droplets, because physical properties such as relative density and relative viscosity of oil phase are changed. In this case, the diameters of oil droplets are necessarily affected. In the case of preparing the microcapsules by using the (S/O)/W dispersion, the diameters of microcapsules are necessarily affected by solid powder in PCM.

So, it is important to investigate how solid powder dispersed in the PCM-droplets affects the dispersing behavior of the PCM-droplets in the turbulent field [21] [22] . However, there are no reports about the dispersing behaviors of PCM-droplets containing solid powder.

In this study, in order to investigate how solid powder affects the dispersing behavior of PCM-droplets and a few characteristics of PCM-microcapsules, it is tried to prepare the microcapsules containing PCM and SiC powder by the interfacial polycondensation reaction method. Here, SiC with higher thermal conductivity may be suitable to the improvement agent for PCM with lower thermal conductivity. The purposes of this study are to obtain the fundamental information about the dispersing behavior of PCM-droplets containing solid powder, to prepare the microcapsules containing PCM and SiC powder and to characterize the microcapsules.

2. Experimental

2.1. Materials

Materials used to prepare the microcapsules containing paraffin wax (PCM) and silicon carbide powder (SiC) were as follows.

Paraffin wax (Wako Pure Chemical Ind. Co., Ltd., Tokyo, Japan) with the melting point of 50˚C was used as PCM. The oil soluble monomer and the water soluble monomer for the interfacial polycondensation reaction were toluen diisocyanate (TDI) and diethylene tetramine (DETA) (Wako Pure Chemical Ind. Co., Ltd, Tokyo, Japan), respectively. The continuous phase dissolving polyvinyl alcohol (PVA: Poly. Degree 500, Sapo. Degree 98 - 99) as a stabilizer was distilled water. Silicon carbide (SiC: thermal conductivity 3.5 w/cm/K) (Sunprite Ind. Co., Ltd., Tokyo, Japan) with the mean diameter of 0.5 µm was added into PCM. Dehydrated toluen (Wako Pure Chemical Ind. Co., Ltd., Tokyo, Japan) was used as the solvent to modify the surface of silicon carbide by triethoxy vinylsilane (Shinetsu Chemical Co., Ltd., Tokyo, Japan).

2.2. Surface Modification of Silicon Carbide

Figure 1 shows the schematic diagram of experimental apparatus used to modifying SiC. The impeller with the diameter of 5.0 cm and the four baffles made of aluminium plate were set as shown in Figure 1. Dehydrate toluene and triethoxyvinylsilane of the given volume and SiC of a given weight were added into the reactor of the separable flask with the effective volume of 500 cm3. The surface modification reaction was continued for 5h at 109˚C. The modification conditions were shown in Table 1.

SiC modified thus was washed twice with ethanol, separated by filtration and then, dried at room temperature.

2.3. Preparation of Microcapsules

Figure 2 shows the schematic diagram of experimental apparatus for preparing the microcapsules. The reactor was set in the thermostatted water bath to keep the reaction temperature constant. The six bladed turbine impellers with the diameter of 5.0 cm were set at one third of liquid depth from the bottom. The four baffles made of aluminium plate were set to prevent air from entraining as shown in Figure 2.

Figure 3 shows the flow chart for preparing the microcapsules together with the microencapsulation mechanism of the model microcapsule tried to prepare. SiC and TDI were added into the melted PCM and stirred to prepare the (S/O) dispersion. The distilled water phase dissolving PVA was prepared as the continuous water phase. The (S/O) dispersion was added into the continuous water phase and stirred to form the (S/O)/W dispersion. After the dispersed oil droplets with the desired mean diameter were formed, the additive water phase dissolving DETA was poured into the (S/O)/W dispersion at the feeding velocity of 0.5 ml/min with the microcyringe and then, the interfacial polycondensation reaction was conducted for 24 h at 50˚C. The experimental conditions for preparing the microcapsules were shown in Table 2.

2.4. Preparation of Microcapsules

2.4.1. Observation of Microcapsules

The surface and inner structure of a microcapsule were observed by scanning electron microscope (JSM-5800: Nihon Denshi Co., Ltd., Tokyo, Japan). The whole of microcapsule was observed by stereo microscope (SE1145TR: Olympus Co., Ltd., Tokyo, Japan). SiC in the microcapsule was analyzed by electron probe microanalyzer (EPMA8705: Shimazu Seisakusho, Co., Ltd., Kyoto, Japan).

Figure 1. Schematic diagram of experimental apparatus for modifying SiC.

Table 1. Experimental conditions for surface modification.

Figure 2. Schematic diagram of experimental apparatus for preparing microcapsules.

Figure 3. Flow chart for preparing microcapsules and microencapsulation mechanism.

Table 2. Experimental conditions for preparing microcapsules.

2.4.2. Diameter Distribution and Mean Diameter

The diameter distributions and mean diameters of microcapsules were directly measured from the photographs of microcapsules taken by stereo microscope according to the method reported in the previous works [21] [22] . Here, the mean diameter was the Sauter mean diameter.

2.4.3. Latent Heat Storage Density

Latent heat storage density of PCM and microcapsule was measured by scanning differential calorimeter (DSC- 50: Shimazu Seisakusho, Co., Ltd., Kyoto, Japan).

2.4.4. Content of SiC

The content of SiC microencapsulated was estimated from difference in the weight measured by thermogravimetry analyzer (DTG-50/50: Shimazu Seisakusho, Co., Ltd., Kyoto, Japan).

3. Results and Discussion

3.1. Effects of Fundamental Experimental Conditions

3.1.1. Effects of PVA Concentration and Revolution Speed

In order to investigate the effect of addition of SiC, first it may be necessary to prepare the microcapsule without SiC and to investigate the effects of fundamental background experimental conditions. So, the effects of both the PVA concentration and the revolution speed of impeller on a few characteristics of microcapsules such as the shape and the diameters were investigated without addition of SiC.

Figure 4 shows the optical microscopic photographs of microcapsules without SiC prepared by changing the PVA concentration (CPVA) at Nr = 300 rpm (a) and by changing the revolution speed (Nr) at CPVA = 0.5 wt% (b). As the microcapsules prepared at CPVA = 0 wt% were larger and irregular, the (O/W) emulsion was found to be unstable. However, with increasing the PVA concentration, the smaller spherical sound microcapsules could be prepared because of the formation of stable (O/W) emulsion. Also, the microcapsules could be prepared even by changing the revolution speed from 300 rpm to 5000 rpm and by forming the stable (O/W) emulsion. As these results are important to control the diameters of microcapsules, the effects of the PVA concentration and the revolution speed were investigated in detail as follows.

Figure 5 shows the dependence of mean diameters (dp) of microcapsules without SiC on the PVA concentration (CPVA) at Nr = 300 rpm and the revolution speed (Nr) at CPVA = 0.5 wt%. The mean diameters decreased from 520 µm at CPVA = 0.1 wt% to 13 µm at CPVA = 1.0 wt% with the PVA concentration, but abruptly increased at the PVA concentration smaller than CPVA = 0.1 wt%. Also, the mean diameters decreased from 320 µm at Nr = 300 rpm to 8.24 µm at Nr = 5000 rpm with the revolution speed. These dependences of mean diameters on the

Figure 4. Photographs of microcapsules. (Effects of PVA concentration and revolution speed) (a) Nr = 300 rpm; (b) CPVA = 0.5wt%.

Figure 5. Dependence of mean diameter of microcapsules on PVA concentration and revolution speed.

PVA concentration and the revolution speed could be expressed by the following equation.

(1)

In the interfacial polycondensation reaction method, the diameters of microcapsules almost become equal to those of the-PCM droplets or slightly larger than them.

The dependence of mean diameters of microcapsules on the revolution speed was found to coincide with that reported in the general oil-in-water emulsion, where the diameters of dispersed oil droplets were determined under breakup domain [23] [24] . Also, the dependence of mean diameters of dispersed oil droplets in the (O/W) emulsion on the stabilizer concentration was reported as dp ~ C-0.3~-1.0 [25] . It is well known that PVA molecules strongly adsorb on the interface between the oil phase and the water phase. Furthermore, on preparing the microcapsules with the interfacial poly condensation reaction method, the higher adsorption concentration of PVA prevents the microcapsule shell from forming, because the denser adsorption layer of PVA formed on the surface of droplets prevents the water soluble monomer and the oil soluble monomer from contacting and reacting at the interface.

Mizuno et al. reported that the growing velocity of the polyurea shell decreased with the PVA concentration [26] .

Also, as the interfacial area per unit volume of reaction mixture should increase with decrease in the mean diameters of oil droplets, the concentrations of oil soluble monomer and water soluble monomer per unit interfacial area should decrease. As a result, the velocity of interfacial polycondensation reaction may decrease and the growing velocity of the shell thickness may become lower [26] . As it is possible that the shell thickness and the adsorption layer of PVA on the PCM-droplets affect the characteristics of microcapsules, it was investigated whether the PVA concentration affects the characteristics of microcapsules or not.

Figure 6 shows the effect of the PVA concentration on the phase change temperature (the melting start temperature (Tm) and the solidifying temperature (Ts)) and latent heat storage density (H). The melting start temperature and the solidifying temperature were not affected by the PVA concentration to the detectable degree at all. Also, latent heat storage density (H) was not affected by the PVA concentration, too.

Taking the results obtained into consideration, the microcapsules were hereafter prepared at CPVA = 0.5 wt% to investigate the addition of SiC, because the spherical sound microcapsules could be prepared as shown in Figure 4.

3.1.2. Effect of Addition of SiC

The effect of addition of SiC on a few characteristics of microcapsules was investigated on the basis of results obtained above.

Figure 7 shows the optical microscopic photographs of microcapsules without and with SiC under the condi-

Figure 6. Effect of PVA concentration on phase change temperature and latent heat storage density.

(a) (b) (c)

Figure 7. Optical microscopic photographs of microcapsules without and with SiC. (a) WSiC = 0wt%-wax; (b) WSiC = 3wt%- wax; (c) WSiC = 10wt%-wax; (Nr = 500 rpm, CPVA = 0.5 wt%).

tions of Nr = 500 rpm and CPVA = 0.5 wt%. From these photographs, SiC contained in the microcapsules could be observed, but SiC coagulated in the microcapsules. Furthermore, the microcapsules containing less SiC were observed, because SiC may break away from the PCM-droplets during the microencapsulation process.

Also, Figure 8 shows the diameter distributions (a) of microcapsules without and with SiC at Nr = 500 rpm and Nr = 5000 rpm and the optical microscopic photographs of microcapsules with SiC at Nr = 500 rpm and Nr = 5000 rpm (b).

From Figure 8(a), it is found that the diameter distributions shifted to the larger diameter side due to addition of SiC. Also, from Figure 8(b), it is found that SiC was contained well in the microcapsules even changing the revolution speed. The diameters of oil droplets containing solid powder may become larger because of increase both in the relative viscosity of oil droplet phase and in the viscous force against destructive force in the turbulent field [23] [24] . Accordingly, the diameters of microcapsules containing SiC may become larger. As it is possible that the amount of contained SiC affects a few characteristics such as the diameter and latent heat storage density of microcapsules, the effect of addition of SiC was investigated in detail.

Figure 9 shows the dependence of mean diameters of microcapsules on the revolution speed (Nr) at WSiC = 0 and 3.0 wt% and the added weight of SiC (WSiC) at Nr = 500 rpm. The mean diameters decreased with the revolution speed, become larger than those of microcapsules without SiC and increased with the added weight of SiC, respectively. These dependencies are expressed as the following Equation (2).

(2)

The dependence (as shown in Figure 5) of mean diameters of the microcapsules without SiC on the revolution speed becomes equal to that for the microcapsules with SiC. From these results, it is found that the PCM-droplets without and with SiC were formed under breakup domain. Thus, the correlating equations as Equations (1) and (2) are valuable to control the diameters of microcapsules without and with SiC.

3.1.3. Effect of Surface Modification

As the microcapsules containing less SiC were observed in Figure 7, the effect of surface modification of SiC

(a) (b)

Figure 8. Diameter distributions and optical microscopic photographs.

Figure 9. Dependence of mean diameters on revolution speed and added weight of SiC.

on the content and the dispersing feature of SiC in the microcapsule were investigated.

Figure 10 shows the dependence of mean diameters of microcapsules on the concentration (Cs) of surface modification agent. It is found that the mean diameters increased with the concentration of surface modification agent. This result may be due to increase in the content of SiC and the relative viscosity of oil droplets as stated above.

Figure 11 shows the effect of surface modification on the content, where the measured contents (W’SiC) are compared with those (WSiC) based on the feed. It is found that the measured contents (W’SiC) for modified SiC were larger than those for unmodified SiC and become close to the contents (WSiC) based on the feed. This result may be due to increase in the hydrophobicity of the surface of SiC and affinity of SiC to PCM.

Figure 12 shows the SEM photographs (A, B) and the x-ray images (C, D) of microcapsules prepared by changing the added weight of unmodified SiC. From Figure 12, it is found that the microcapsules without and

Figure 10. Dependence of mean diameter on concentration of modification agent.

Figure 11. Effect of modification on content.

Figure 12. SEM photographs and x-ray images (with unmodified SiC).

with SiC were spherical [A(a), B(a)] and the amount of SiC contained in the microcapsule could be increased by increasing the added weight of SiC [C(b) D(b)].

Figure 13 shows the effect of surface modification of SiC on the dispersing feature of SiC in the microcapsule. The unmodified SiC dispersed in the circumferential region of microcapsule, however, the modified SiC dispersed in the whole region of microcapsule. This may be due to increase in both hydrophobicity of surface and the stability of SiC. As a result, the content could be increased due to surface modification as shown in Figure 10 and Figure 11.

3.2. Effect of SiC on Thermal Characteristics

Figure 14 shows the DSC curves of PCM (a) and microcapsules with SiC (WSiC = 3 wt%) (b). The endothermic peaks of PCM and microcapsules do not equal to the exothermic peaks of them because of supercooling and the reaction remainder such as DETA. Furthermore, the endothermic and the exothermic peaks of PCM were merely smaller than those of microcapsules because of the reaction remainder such as DETA, the microcapsule shell and SiC. Meanwhile, latent heat storage density of microcapsule was smaller than that of PCM because of increase in the weight of microcapsules due to the shell and SiC contained.

Figure 15 shows the effect of SiC on latent heat storage density (a) and the phase change temperature (b).

Figure 13. Effect of surface modification.

(a) (b)

Figure 14. DSC curves of PCM and microcapsules with SiC.

(a) (b)

Figure 15. Effect of SiC on latent heat storage density and phase change temperature.

From Figure 15(a), the following results were obtained. Namely, latent heat storage density calculated on the basis of the PCM amount in the feed is very smaller than that of PCM. Furthermore, latent heat storage density of microcapsules without SiC and with SiC of 2 wt% and 3 wt% become equal to the calculated values, but latent heat storage density of microcapsules with SiC of 5 wt% and 10 wt% become smaller than the caluculated values.

Also, the reason why the measured values are smaller than the calculated values may be due to the lower content, because PCM should leak during the microencapsulation process.

On the other hand, from Figure 15(b), the following valuable results could be obtained. The melting start temperature (Tm) and the solidifying temperature (Ts) at = 0 become higher than those (TWm, TWs) of PCM. This result may be due to supercooling in the limited smaller hollow of the microcapsules and lower thermal conductivity. However, with increasing the melting start temperature (Tm) and the solidifying temperature (Ts) gradualy become close to those (TWm, TWs) of PCM (especially to TWs at = 1 wt%).

From these results, it may be expected that SiC contained should play as a supercooling prevention agent and improvement agent for thermal conductivity of the microcapsules. Although the thermal characteristics of microcapsules can be improved by microencapsulating SiC at the same time, however, latent heat storage density decrease. For example, at = 10 wt%, latent heat storage density decreases from 165 kJ/kg of PCM to 120 kJ/kg. For overcoming these demerits, it is necessary to increase the content of PCM and to select a filler with smaller density and higher thermal conductivity.

4. Conclusions

It was tried to prepare the microcapsules containing paraffin wax as PCM and SiC with the interfacial polycondensation reaction method and to characterize. The following fundamental valuable results could be obtained.

1) The diameters of microcapsules without and with SiC were determined under break up domain in the turbulent field.

2) The microcapsules containing paraffin wax and SiC could be prepared well.

3) The diameter of microcapsules increased with the weight of SiC contained.

4) The content of SiC could be increased by modifining SiC because of increase in hydrophobicity and affinity of SiC to PCM.

5) Thermal conductivity in the microcapsule could be improved by microencapsulating SiC at the same time.

6) SiC played a supercooling prevention agent in the microcapsules.

References

  1. Kondo, T. and Tanaka, M. (1975) Microcapsules (Preparation, Properties, Application). Sankyo Shuppan, Tokyo.
  2. Kondo, T. (1967) Saishin Maikurokapseruka Gijutsu (Microencapsulation Technique). TES, Tokyo.
  3. Tanaka, M. (2008) Key Point of Preparation of Nano/Microcapsules. Techno System Publishing Co. Ltd., Tokyo.
  4. Koishi, M., Eto, K. and Higure, H. (2005) (Preparation + Utilization) Microcapsules. Kogyo Chosakai, Tokyo.
  5. Yamagishi, Y., Sugeno, T., Takeuchi, H. and Pyatenko, A.T. (1998) Themal Characteristics of Supercooles Phase Change Materials inside Microcapsules. Netsu Bussel, 12, 10-17. http://dx.doi.org/10.2963/jjtp.12.10
  6. Yamagishi, Y., Sugeno, T., Takeuchi, H. and Pyatenko, A.T. (1998) Forced Convection Heat Transfer with Microencapsulated Phase-Change-Material Slurries. Kagaku Kogaku Ronbunshu, 24, 104-110. http://dx.doi.org/10.1252/kakoronbunshu.24.104
  7. Yamagishi, Y., Takeuchi, H. and Pyatenko, A.T. (1999) Pyatenko, Characteristics of Microencapsulated PCM Slurry as a Heat-Transfer Fluid. AIChE Journal, 45, 696-707. http://dx.doi.org/10.1002/aic.690450405
  8. Stritih, U. and Novak, P. (1996) Solar Heat Storage Wall for Building Ventilation. Renewable Energy, 8, 268-271. http://dx.doi.org/10.1016/0960-1481(96)88860-4
  9. Zhaoa, C.Y. and Zhang, G.H. (2011) Review on Microencapsulated Phase Change Materials (MEPCMs): Fabrication, Characterization and Applications. Renewable and Sustainable Energy Reviews, 15, 3813-3832. http://dx.doi.org/10.1016/j.rser.2011.07.019
  10. Yuan, Y., Zhang, N., Tao, W., Cao, X. and He, Y. (2014) Fatty Acids as Phase Change Materials: A Review. Renewa- ble and Sustainable Energy Reviews, 29, 482-498. http://dx.doi.org/10.1016/j.rser.2013.08.107
  11. Jamekhorshid, A., Sadrameli, S.M. and Farid, M. (2014) A Review of Microencapsulation Methods of Phase Change Materials (PCMs) as a Thermal Energy Storage (TES) Medium. Renewable and Sustainable Energy Reviews, 31, 531- 542. http://dx.doi.org/10.1016/j.rser.2013.12.033
  12. Zhang, X.X., Tao, X., Yick, K.I. and Wang, X.C. (2004) Structure and Thermal Stability of Microencapsulated Phase-Change Materials. Colloid and Polymer Science, 282, 330-336. http://dx.doi.org/10.1007/s00396-003-0925-y
  13. Tang, X., Li, W., Shi, H., Wang, X., Wang, J. and Zhang, X. (2013) Fabrication, Characterization, and Supercooling Suppression of Nanoencapsulated n-Octadecane with Methyl Methacrylate-Octadecyl Methacrylate Copolymer Shell. Colloid and Polymer Science, 291, 1705-1712. http://dx.doi.org/10.1007/s00396-013-2905-1
  14. Sánchez, L., Sánchez, P., Carmona, M., Lucas, A. and Rodríguez, J.F. (2008) Influence of Operation Conditions on the Microencapsulation of PCMs by Means of Suspension-Like Polymerization. Colloid and Polymer Science, 286, 1019- 1027. http://dx.doi.org/10.1007/s00396-008-1864-4
  15. Su, J., Ren, L. and Wang, L. (2005) Preparation and Mechanical Properties of Thermal Energy Storage Microcapsules. Colloid and Polymer Science, 284, 224-228. http://dx.doi.org/10.1007/s00396-005-1368-4
  16. Su, J.F., Wang, S.B., Zhang, Y.Y. and Huang, Z. (2011) Physicochemical Properties and Mechanical Characters of Methanol-Modified Melamine-Formaldehyde (MMF) Shell microPCMs Containing Paraffin. Colloid and Polymer Sci- ence, 289, 111-119. http://dx.doi.org/10.1007/s00396-010-2328-1
  17. Cho, J.S., Kwon, A. and Cho, C.G. (2002) Microencapsulation of Octadecane as a Phase-Change Material by Interfacial Polymerization in an Emulsion System. Colloid and Polymer Science, 280, 260-266. http://dx.doi.org/10.1007/s00396-001-0603-x
  18. Cheng, F., Wei, Y., Zhang, Y., Wang, F., Shen, T. and Zong, C. (2013) Preparation and Characterization of Phase- Change Material Nanocapsules with Amphiphilic Polyurethane Synthesized by 3-allyloxy-1,2-propanediol. Journal of Applied Polymer Science, 130, 1879-1889. http://dx.doi.org/10.1002/app.39302
  19. Borreguero, A.M., Rodríguez, J.F., Valverde, J.L., Peijs, T. and Carmona, M. (2013) Characterization of Rigid Polyurethane Foams Containing Microencapsulted Phase Change Materials: Microcapsules Type Effect. Journal of Applied Polymer Science, 128, 582-590. http://dx.doi.org/10.1002/app.38226
  20. Cortazar, M.G. and Rodríguez, R. (2013) Thermal Storage Nanocapsules by Miniemulsion Polymerization. Journal of Applied Polymer Science, 127, 5059-5064. http://dx.doi.org/10.1002/app.38124
  21. Tanaka, M., Nakata, K. and Oyama, Y. (1970) Coalescence of Dispersed Liquid Droplets in a Batch Type of Stirred Tank Reactor. Kagaku Kogaku, 34, 893-897. http://dx.doi.org/10.1252/kakoronbunshu1953.34.893
  22. O’shima, E. and Tanaka, M. (1982) Coalescence and Breakup of Droplets in Suspension Polymerization of Styrene. Kagaku Kogaku Ronbunshu, 8, 86-90. http://dx.doi.org/10.1252/kakoronbunshu.8.86
  23. Tanaka, M. (1985) Local Droplet Diameter Variation in a Stirred Tank. Canadian Journal of Chemical Engineering, 63, 723-727. http://dx.doi.org/10.1002/cjce.5450630504
  24. Tanaka, M. and O’Shima, E. (1988) Dispersing Behaviour of Droplets in Suspension Polymerization of Styrene in a Loop Reactor. The Canadian Journal of Chemical Engineering, 66, 29-35. http://dx.doi.org/10.1002/cjce.5450660104
  25. Yuan, H.G., Kalfas, G. and Ray, W.H. (1991) Suspension Polymerization. Journal of Macromolecular Science, Part C, 31, 215-299. http://dx.doi.org/10.1080/15321799108021924
  26. Mizuno, K., Taguchi, Y. and Tanaka, M. (2005) The Effect of the Surfactant Adsorption Layer on the Growth Rate of the Polyurethane Capsule Shell. Journal of Chemical Engineering of Japan, 38, 45-48. http://dx.doi.org/10.1252/jcej.38.45