Received 14 March 2016; accepted 24 April 2016; published 27 April 2016

ABSTRACT

As erosion has become one of the serious oral health problems, some fluoride-releasing dental materials have been developed to protect enamel from demineralization. The purpose of this study was to evaluate the antidemineralization effect of PRG Barrier Coat^® and FujiVII^® (fluoride- releasing dental materials). Four square windows measuring 1 mm² were prepared on the labial enamel surface of each bovine tooth using masking tape and nail varnish. The first and second windows were half covered by fluoride-releasing material and control material, respectively, whereas the third and fourth windows were left untreated. All windows were immersed into 0.1 M lactic acid and 6wt% CM-cellulose (pH 4.5) at 38˚C for 21 days. Subsequently, the first and second windows were covered with nail varnish after removal of the materials, and the third and fourth windows were immersed into ultrapure water at 38˚C for 28 days after being half covered with fluoride-releasing and control materials, respectively. The following procedure was performed separately during evaluations of the fluoride-releasing materials, PRG Barrier Coat^®, and FujiVII^®, using eight and six bovine teeth, respectively. The first, second, third, and fourth windows were classified into DM-PRG; Demineralized-PRG or DM-FujiVII; Demineralized-FujiVII, DM-TCM; Demineralized-traditional cement or DM-TGIC; Demineralized-traditional glass ionomer cement, RM-PRG; Remineralized-PRG or RM-FujiVII; Remineralized-FujiVII, and RM-TCM; Remineralized- traditional cement or RM-TGIC; Remineralized-traditional glass ionomer cement, respectively. After nail varnish was removed, ∆Q values (mean ± SD) of the windows were measured using QLF-D and were compared between DM-PRG and DM-TCM, RM-PRG and RM-TCM, DM-FujiVII and DM- TGIC, and RM-FujiVII and RM-TGIC groups. ∆Q values of RM-PRG (−60 ± 44) and RM-FujiVII (−5.0 ± 10) were significantly higher than that of RM-TCM (−315 ± 193) and RM-TGIC (−56 ± 43), respectively. The fluoride releasing materials provided remineralization effects to bovine enamel.

Keywords:

Fluoride-Releasing Materials, Bovine Enamel, Erosion, Remineralization, Quantitative Light-Induced Fluorescence-Digital

1. Introduction

As erosion has become one of the serious oral health problems, some fluoride-releasing dental materials have been developed to protect enamel from demineralization. Erosion is initiated as demineralization because of nonbacterial acid exposure such as that occurring during bulimia, gastric acid reflex, and frequent intake of acidic food [1] [2] . The importance of detection and control of early demineralized lesions by dentists is constantly increasing since severe carious lesions are currently not as common in Japan as during the past. In general, an early demineralized lesion is treated with fluoride application, and the advantage of fluoride-releasing materials has already been reported [3] - [5] . However, to date, there has been insufficient reporting on the inhibition of demineralization and promotion of remineralization by fluoride-releasing materials. Quantitative Light- induced Fluorescence-Digital (QLF-D; Inspektor, Amsterdam, The Netherlands) is a device used to evaluate severity or the time-course change of the early demineralized lesion by calculating mineral density [6] [7] . PRG Barrier Coat^® is a light-cure coating material that contains surface pretreated glass (S-PRG) [8] . The S-PRG releases and recharges sodium, strontium, borate, aluminum, silicate, and fluoride ions depending on the oral surroundings, resulting in protective effects on early demineralized enamel. Glass ionomer cement is one of the materials that is applied to protect pulp and to fill cavities in dental treatment. It contains fluoroaluminosilicate glass that releases fluoride as one of the ingredients. FujiVII^® is newly developed glass ionomer cement that possesses an improved fluoride-releasing property [3] . In this study, the antidemineralization effect of PRG Barrier Coat^® and FujiVII^® on bovine enamel was evaluated in vitro using QLF-D. The current study was approved by the ethical committee on experiments in Meikai University (approval number: A1305).

2. Materials and Methods

2.1. Preparation of the Tooth Samples

Eight and six bovine teeth for the evaluation of PRG Barrier Coat^® and FujiVII^®, respectively, were polished by 400-, 600-, and 800-grit silicon carbide abrasive paper to remove extraneous matter from the enamel surface. Four square windows measuring 1 mm² were prepared on the labial enamel surface of each tooth using masking tape and nail varnish (SUNPALKO Co., Ltd., Kyoto, Japan). The teeth were completely coated with nail varnish except for the window areas. The evaluation of PRG Barrier Coat^® was carried out initially, following by the evaluation of FujiVII^®. Eight and six bovine teeth were available for the evaluation of PRG Barrier Coat^® and FujiVII^®, respectively. As a result, the number of the samples used differed between the two evaluations of fluoride-releasing dental materials.

2.2. Application of PRG Barrier Coat^®, FujiVII^®, and Control Materials before Demineralization

For the eight bovine teeth, in the initial evaluation of PRG Barrier Coat^®, half of the window area was covered with PRG Barrier Coat^® (a Demineralized-PRG;DM-PRG group) in one of the four windows, another window was covered with traditional tooth coating material in the same way (a Demineralized-traditional coating material; DM-TCM group), whereas the two remaining windows were left untreated (Figure 1(a)). The six bovine teeth for evaluation of FujiVII^® were prepared in a similar way; half of the window area was covered with FujiVII^® (a Demineralized-FujiVII; DM-FujiVII group) in one of the four windows, another window was covered with traditional glass ionomer cement in the same way (a Demineralized-traditional glass ionomer cement; DM-TGIC group), whereas the remaining two windows were left untreated (Figure 1(b)).

2.3. Incubation of the Naked Window Areas in a Lactic Acid

Tooth samples for evaluation of both PRG Barrier Coat^® and FujiVII^® were incubated in the same way. Every tooth sample was separately incubated in lactic acid solution that contained 0.1 M of lactic acid and 6 wt% of CM-cellulose (pH 4.5; Wako Pure Chemical Industries, Ltd., Osaka, Japan) at 38˚C for 21 days. On the 21^st day of incubation, the tooth samples were removed from the lactic acid solution and washed with ultrapure water. After the PRG Barrier Coat^® and traditional tooth coating material, or FujiVII^® and traditional glass ionomer cement were removed from each tooth sample, the windows that had been incubated with the aforementioned dental materials were completely covered with nail varnish.

2.4. Application of PRG Barrier Coat^®, FujiVII^®, and Control Materials before Remineralization

In the eight teeth used in the evaluation of PRG Barrier Coat^®, one of the two windows that were immersed into the lactic acid solution without any dental material was half covered by PRG Barrier Coat^® (a Remineralized- PRG; RM-PRG group), and the other window was half covered with traditional coating material (a Remineralized-traditional coating material; RM-TCM group), respectively (Figure 2(a)). In the six teeth used in the evaluation of FujiVII^®, one of the two windows that were immersed into the lactic acid solution without any dental material was half covered by FujiVII^® (a Remineralized-FujiVII; RM-FujiVII group), and the other window was half covered with traditional glass ionomer cement (a Remineralized-traditional glass ionomer cement;

RM-TGIC group), respectively. All the tooth samples for the both evaluations were incubated in ultrapure water at 38˚C for 10 days (Figure 2(b)). After the incubation, the tooth samples were washed with ultrapure water, following which all the materials and nail varnish on the tooth surface were removed (Figure 3).

2.5. Measurement of Mineral Density

The value of ∆Q on the border of the dental material in each window area (Figure 4) was measured by QLF-D. The images were captured from the labial aspect of the sample teeth in a darkroom, using proprietary software (C3 v1.19, Inspektor Research Systems BV, Amsterdam, The Netherlands) under the following settings: shutter speed of 1/60s, aperture value of 5.6, and ISO speed of 1600 [6] . The distance between the lens and the window was 10 cm and the shooting angle was maintained as 90˚ to the window surface. The mean values were compared between the DM-PRG and DM-TCM groups, DM-FujiVII and DM-TGIC groups, RM-PRG and RM- TCM groups, and RM-FujiVII and RM-TGIC groups. A student’s t-test was used to compare the significance of the difference between the two groups and p < 0.05 was considered significant.

3. Results

Values were expressed as mean ± standard deviation. Window areas were demineralized or de- and remineralized hence turned in white without any parenchyma loss. QLF made possible to evaluate mineral density in early demineralized lesion. ∆Q values in the window areas were evaluated under the condition described in the Materials and Method section. As shown in Table 1 and Table 2, the ∆Q value in the RM-PRG group (−60 ± 44)

^**p < 0.01.

^*p < 0.05.

was significantly higher than that in the RM-TCM group (−315 ± 193; p < 0.01), and the ∆Q value in the RM-FujiVII group (−5 ± 10) was also significantly higher than that in the RM-TGIC group (−56 ± 43; p < 0.05), respectively.

4. Discussion

Lussi and Carvalho (2015) [9] mentioned in their study on fluorides and other protective agents against demineralization that the effectiveness of fluoride in caries prevention has been convincingly proven. In addition, both previous in vitro and clinical studies reported that fluoride improves remineralization [10] [11] , supporting our results. Lippert et al. (2013) [12] reported in their in vitro study that fluoride reduced enamel demineralization in a mild lesion; however, application of fluoride-releasing materials did not reduce demineralization of enamel in the current study. It could be considered that 0.1 M of lactic acid and 6 wt% of CM-cellulose (pH 4.5) as a demineralization solution resulted in a too severe condition for released fluoride to reduce demineralization of enamel. Moreover, ten Cate et al. (2006) [13] reported in their in vitro study on the correlation between artificially induced demineralized lesion depth and the concentration of topical fluoride application, that fluoride can drive demineralization further into enamel by resulting in less soluble surface tissue, by not neutralizing acids penetrating into the tissue, thereby supporting our results that mineral density in enamel was not affected by topical fluoride application during demineralization.

PRG Barrier Coat^® is a tooth coating material that is often applied to cervical, contact, and caries prone areas to prevent tooth decay or erosion. It contains S-PRG ionomer as fillers, which releases and recharges F⁻, Sr²⁺, Na⁺, , Al³⁺, and [14] and hence provides a protective property against demineralized lesions [15] . PRG Barrier Coat^® improved remineralization of eroded enamel in the present study, supporting previous reports. Although enamel specimens were eroded in the present study, S-PRG fillers were reported to have additionally reduced biofilm formation [11] [16] [17] .

Glass ionomer cements have been used in pediatric restorative dentistry for many years because of favorable properties such as biocompatibility, chemical adhesion to dentin and enamel, a coefficient of thermal expansion similar to that of tooth structure, versatility, and most importantly, its fluoride-releasing property [18] . FujiVII^® is a newly developed type of glass ionomer cement whose flowability has been greatly improved, facilitating close contact between the tooth surface and the cement and thereby resulting in an improved remineralization effect by efficiently providing fluoride to enamel.

QLF-D is a device used to evaluate severity or the time-course change of the early demineralized lesion by calculating mineral density [6] [7] . When a tooth is lit in a blue light, fluorescence is reflected especially on the enamel-dentin junction. If a demineralized lesion exists in the enamel, the volume of reflected fluorescence is reduced. QLF-D senses the difference in reflected fluorescence in the volume between the unaffected and demineralized regions, detects dimensions of the region where the decreased fluorescence is observed, and then calculates mineral density in the demineralized lesion (∆Q value) by multiplying the rate of decrease in fluorescence (expressed in a negative value) and the dimensions of the region where the decreased fluorescence was observed (pixels). Hence, the ∆Q values in the current study were expressed as negative values accompanying the unit of “%pixels.” As the QLF-D facilitates a noninvasive method of evaluating enamel density, it is applied in both in vivo and in vitro studies all over the world [7] [19] .

Bovine enamel is used in general studies on demineralization [20] and remineralization [21] . In addition to the general rules applicable to studies within this field, bovine enamel was used in the present study because the donor cows were fed in the same surroundings and were sacrificed at almost the same age. It was expected that the same feeding condition would lead to very similar properties among enamel specimens in terms of acid resistance. However, the result indicated that ∆Q value varied markedly between evaluations on PRG Barrier Coat^® and FijiVII^®. Since the bovine teeth used in the evaluation on PRG Barrier Coat^® and FijiVII^® were purchased at discrete days from the same meat trader, the results suggested that acid resistance might vary more from cow to cow than has been reported in the past.

5. Conclusions

1) Both PRG Barrier Coat^® and FijiVII^® offered improved remineralization of initially demineralized enamel in comparison with their corresponding conventional products.

2) Acid resistance of bovine enamel varies from donor to donor even the donors were fed and sacrificed under very similar/same conditions.

Acknowledgements

This manuscript was subsidized by JSPS KAKENHI Grant Number 15K20607.

Cite this paper

Koji Watanabe,Takashi Sasabe,Shigeru Watanabe, (2016) Evaluating Acid Resistance Effect of Fluoride-Releasing Dental Materials Using Quantitative Light-Induced Fluorescence-Digital in Vitro. Open Journal of Stomatology,06,127-134. doi: 10.4236/ojst.2016.64016