Materials Sciences and Applications
Vol.08 No.10(2017), Article ID:78959,12 pages
10.4236/msa.2017.810052

Composition and Band Gap Controlled AACVD of ZnSe and ZnSxSe1−x Thin Films Using Novel Single Source Precursors

Yousef Alghamdi

Department of Chemistry, Faculty of Science, King Abdulaziz University, Jeddah, KSA

Copyright © 2017 by author and Scientific Research Publishing Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY 4.0).

http://creativecommons.org/licenses/by/4.0/

Received: July 21, 2017; Accepted: September 5, 2017; Published: September 8, 2017

ABSTRACT

Polycrystalline thin films of ZnSe and ZnSxSe1−x have been deposited on glass substrates by Aerosol Assisted Chemical Vapour Deposition (AACVD) from bis(diethyldiselenocarbamato)zinc(II) and a 1:1 and 1:0.75 mixtures of bis(diethyldiselenocarbamato)zinc(II) and bis(diethyldithiocarbamato)zinc(II) as precursors. All films were characterized by p-XRD, SEM, EDX, Raman spectroscopy, photoluminescence (PL and UV/Vis spectroscopy. The band gap of pure ZnSe thin films was found to be 2.25 whereas the band gap of ZnSxSe1−x films varied from 2.55 to 2.66 eV depending on the sulfur content in the films. PL emission spectra showed a clear blue shift for ZnSxSe1−x films compared to ZnSe due to the sulphur content in the films which increase the band gap. The band gap of ZnSSe can be controlled by sulfur to selenium ratio in the alloy. The morphology of the ZnSe thin films changed from small randomly shaped crystallites to triangles whereas the morphology of ZnSxSe1−x was mainly based on cuboids.

Keywords:

Bis(diethyldiselenocarbamato)zinc(II), ZnSe, ZnSSe, AACVD, SEM

1. Introduction

Metal selenides are wide band gap materials and have applications in light-emitting devices, solar cells, sensors, and optical recording materials [1] [2] [3] [4] . ZnSe is ideal material for blue-green laser diodes [1] [2] , mid-IR laser sources for remote sensing applications [5] , and in optically controlled switching devices due to its large photo resistivity [6] . Zinc selenide thin films had been fabricated by photochemical deposition (PCD) [7] , chemical bath deposition (CBD) [8] [9] and electrochemical deposition (ECD) [10] , but all these methods have their own drawbacks including higher annealing temperatures for PCD, controlling rate of reaction for CBD and the use of only conductive substrates for ECD [7] .

Several reports have been published for the use of single-source precursors for the deposition of metal chalcogenide [11] - [22] . A range of chalcogenides have been deposited from M[ESi(SiMe)3]2 (M = Zn, Cd, Hg; E = S, Se or Te) complexes as single source precursors [23] [24] . Metal complexes with the general formula [M(R2PSe2)n] (M = Zn, Cd, Pb, In, Ga, Cu, Bi, Ni; R = iPr, Ph) have been synthesised and used for the deposition of metal selenide thin films by CVD [25] . Other metal complexes used as single source precursors include: [(M(E2CNR2)2] (symmetrical) or [M(E2CNRR’)2] (unsymmetrical) (R, R’ = alkyl, E = S, Se; M = Zn, Cd) [22] , mixed alkyl/dithio- or diseleno-carbamato complexes [M(E2CNRR’)2], where R = Me, Et, But or Me3CCH2, M = Zn or Cd; E = S or Se; R’ = Me or Et [26] [27] [28] [29] , imino-bis(dialkylphos-phineselenide) complexes [M[(EPiPr2)2N]2] (M = Cd, Zn; E = S, Se) and [M[(SePPh2)2N]2] (M = Cd, Zn) [30] [31] [32] [33] [34] .

ZnSxSe1?x is found to be one of the best substituent for CdS as a buffer layer. When the sulphur composition is larger than 0.2, then it becomes another good candidate for cladding layers for blue laser diodes [35] . Polycrystalline ZnSxSe1?x thin films were deposited by co-evaporation of ZnS and ZnSe [36] , by low-pressure metal-organic chemical vapour deposition (LP-MOCVD) process from the zinc alkyls dimethylzinc (DMZ) or diethylzinc (DEZ) and H2Se and H2S [37] , and by molecular beam epitaxy (MBE) using radio-frequency (RF) plasma [38] . We have recently reported the deposition of CdSe and CdSSe thin films from molecular precursors by AACVD [39] . Herein we report the deposition of highly crystalline hexagonal ZnSe thin films from bis(diethyldiselenocarbamato)zinc(II) complex and ZnSSe composite from a mixture of bis(diethyldiselenocarbamato)zinc(II) and bis(diethyldithiocarbamato)zinc(II) complexes and their detailed optical and structural characterisation. To the best of our knowledge ZnSe or ZnSSe thin films have never been deposited by AACVD method from diselenocarbamato complexes of zinc.

2. Experimental

2.1. Synthesis of Precursors

Bis(diethyldiselnocarbamato)zinc(II)[Zn(Se2CNEt2)2] and bis(diethyldithiocarba- mato)-zinc(II) [Zn(S2CNEt2)2] precursors were synthesised using method described in literature [27] [28] [29] [30] . In a typical synthesis sodium salt of diethyl dithiocarbamate ([Na(S2CNEt2)2]) was reacted with zinc nitrate (Zn(NO3)2) in a water solution. The white precipitate of [Zn(S2CNEt2)2] was separated by filtration, washed with water and dried under vacuum.

2.2. Thermogravimetric Analysis

Thermogravimetric analysis measurements were carried out by a Seiko SSC/S200 model under a heating rate of 10˚C∙min−1 under nitrogen. Indium metal is used as a reference to calibrate the instrument. TGA was performed by School of Chemistry, University of Manchester, micro-analysis team

2.3. Deposition of Thin Films

The depositions of thin films were carried out at 300˚C and 350˚C using 14 mmol of the [Zn(Se2CNEt2)2] precursor in 15 mL THF and for the deposition of ZnSSe; 1:1 ratio of [Zn(Se2CNEt2)2] (7 mmol) and [Zn(S2CNEt2)2] (7 mmol) in 15 mL THF and Zn(Se2CNEt2)2] (5 mmol) and [Zn(S2CNEt2)2] (7 mmol) in 15 mL THF to reduce the amount of Se on the thin films at 350˚C.

The depositions were carried out onto glass slides with the dimensions of 1 × 3 cm by AACVD. In a typical experiment, the precursor was dissolved in 15 mL THF in a two-necked 100 mL round-bottom flask. The flask was connected with an argon gas inlet carried the aerosols generated by a PIFCO ultrasonic humidifier to the reactor tube connected to other neck of the flask and placed in a Carbolite furnace. The gas flow rate was controlled at 160 Sccm through a Platon flow gauge. The precursor mist was thermolysed in the hot zone at the surface of glass substrate and resulted in the deposition of thin film as reported previously [39] .

2.4. Characterisation of Thin Films

XRD patterns were recorded on a Bruker D8 AXE diffractometer (Cu-Kα) from 20 to 80 degrees with a step size of 0.05. SEM studies were carried out by using a Philips XL 30 FEGSEM and EDAX analysis for the composition of films were carried out by using a DX4 instrument. TEM i were recorded on a Tecnai F30 microscope and Raman spectra were measured by Renishaw 1000 Micro Raman system. UV/Vis spectra were carried out by Perkin Elmer Lambda 1050 spectrophotometer. And PL spectra were taken by using HOIBO Fluorolog FL3 iHR at excitation wavelength of 400 nm.

3. Results and Discussion

Bis(diethyldithio/diselenocarbamato)zinc(II) complexes can easily be synthesised by a single step reaction and are stable at room temperature for periods of years as the complexes used in these experiments were synthesised 5 years ago. The analysis of the complexes after 5 years proved that no decomposition occurred. These complexes are soluble in common organic solvents such as toluene, THF, chloroform. Both decompose in the same the same manner and in the same temperature range (vide infra) making them suitable to be used as a mixture in different ratios to control the sulfur or selenium concentration in the alloy. The effect of precursor concentration and deposition temperature on the stoichiometric composition and morphology of the ZnSe and ZnSSe thin films were investigated.

3.1. Thermogravimetric Analysis (TGA)

Thermogravimetric analysis (TGA) of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] films were studied from 10˚C - 600˚C under nitrogen. [Zn(S2CNEt2)2] and [Zn(Se2CNEt2)2] decomposed in one relatively sharp step with almost similar rate and resulted with ~8% and ~10% residual mass, which found to be half or less than half of the mass of the expected metal chalcogenides; ZnS (27%) or ZnSe (20%). The sharp transition shows a one-step decomposition for both complexes to give the metal chalcogenides and all the rest of impurities volatilised. The less quantity of the residue appears to be due to the volatility of sulphur and selenium at high temperatures. Decomposition of both precursors at similar temperature makes them highly suitable for depositing ZnSe, ZnS, and ZnSSe thin films by AACVD within a temperature range of 250˚C to 350˚C (Figure 1).

3.2. AACVD of ZnSe Thin Films

3.2.1. Powder X-Ray Diffraction for ZnSe Thin Films

Depositions were carried out at 300˚C and 350˚C using 14 mmol of the [Zn(Se2CNEt2)2] precursor in 15 mL THF.

Films deposited at 300˚C were slightly yellow and thick, p-XRD did not give any diffraction peaks indicating the amorphous nature of the deposited material whereas, films deposited at 350˚C were thick adherent, specular golden in appearance. Figure 2(a) shows the p-XRD pattern of ZnSe thin films deposited at 350˚C. The main peaks at about 27.3˚, 45.2˚ and 53.6˚ correspond to cubic ZnSe (ICDD: 01-088-2345).

3.2.2. Scanning Electron Microscopy of ZnSe Films

Morphology of the films was studied using by SEM. Figure 2(b) shows the SEM images of the films with an inset at higher magnification. The films are based on

Figure 1. Thermogravimetric analysis of complexes [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] under N2.

(a) (b)

Figure 2. (a) p-XRD pattern of ZnSe thin films deposited at 350˚C by AACVD. Peaks are labelled with cubic ZnSe (ICDD: 01-088-2345); (b) SEM images of ZnSe films with an inset at higher magnification.

small (100 - 300 nm) random crystallites thickly packed together. EDX analysis showed Zn:Se ratio as 49.44:50.55, which is very close to the 1:1 ratio expected for ZnSe.

3.2.3. Raman and PL Spectra of ZnSe Films

Raman spectra showed peaks at 205, 253, 412 and 498 cm−1 which are close to the Raman peaks for the TO, LO and 2LO phonon modes of ZnSe (~206, 252 and 493 cm−1) [40] - [45] (Figure 3(a)).

PL spectra showed a very strong emission between 530 to 580 nm (Figure 3(b)). The emission maximum shift towards the higher energy, as compared to the bulk values, is due to the smaller size of crystallites and large surface defects and Zn vacancies at the interstitial sites [46] .

3.3. AACVD of Zinc Sulfoselenide (ZnSxSe1−x) Thin Films

3.3.1. p-XRD of ZnSSe Thin Films

The deposition was carried out at 300˚C and 350˚C but no deposition occurred at 300˚C. Thick specular yellow films were obtained at 350˚C using 1:1 and 1:0.75 ratios of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] precursors. The p-XRD patterns of ZnSxSe1−x thin films deposited using 1:1 ratio of mixture are shown in Figure 4. The p-XRD patterns were indexed using the standard patterns for cubic ZnSe0.5S.0.5 (ICDD: 04-001-6856) space group F-43m, lattice parameters, a = b = c = 5.500 Å. The main peaks at 2θ: 28.07 (111), 32.53 (200), 46.67 (220), 55.35 (311) and 58.04 (222) are slightly shifted from the standard pattern. Minor peaks are due to the contamination of binary phases as ZnS and ZnSe (Figure 4).

1:0.75 molar ratio of [Zn(Se2CNEt2)2]and [Zn(S2CNEt2)2] precursor mixture at 350˚C produced thin orange adherent films. The p-XRD patterns showed good matching with cubic ZnSe0.5S.0.5 (ICDD: 04-001-6856). The main peaks were observed at 2θ: 28.07 (111), 32.53 (200), 46.67 (220), 55.35 (311) and 58.04 (222) similar to those observed for films deposited from 1:1 mixture. Again the films

Figure 3. (a) Raman spectra of ZnSe, ZnSSe1, and ZnSSe2 thin films deposited at 350˚C by AACVD, ZnSSe1, ZnSSe2 are films deposited using 1:1 and 1:0.75 mmol of [Zn(S2CNEt2)2] and [Zn(Se2CNEt2)2] precursors at 350˚C; (b) Photoluminescence spectra of ZnSe, ZnSSe1, and ZnSSe2.

Figure 4. p-XRD patterns of ZnSSe thin films deposited at 350˚C using 1:1 and 1:0.75 mmol of [Zn(S2CNEt2)2] and [Zn(Se2CNEt2)2] precursors. Sticks pattern is the reference patterns for cubic ZnSe0.5S.0.5 (ICDD: 04-001-6856). (*) shows ZnSe peaks and (˚) shows the ZnS peaks.

had minor contamination of ZnS and ZnSe phases. The p-XRD patterns showed good agreement with the reported X-ray diffraction data related to the ZnSSe thin films for different x-values (x= 0, 0.2, 0.4, 0.6). It can be noted that the higher the x-value the more the (1 1 1) peak shifts from the ZnSe (1 1 1) peak to ZnS(1 1 1) peak as reported [35] .

3.3.2. Morphology of ZnSSe Thin Films

The SEM images of ZnSxSe1−x thin films deposited using 1:1 ratio of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] precursor mixture showed irregular shaped crystallites which showed some kind of tetragonal morphologies (Figure 5). EDX result showed the ratio of Zn: S: Se: 47.34:36.68:13.98 giving a stoichiometric formula of Zn1.0Se0.77S0.30. The EDX results gave good explanation for the larger deviation of the p-XRD patterns peaks from the ZnS patterns than the ZnSe pattern. Morphology of the ZnSxSe1−x films deposited using 1:0.75 molar ratio of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] is based on a mixture of irregular and cubic crystallites.

EDX results showed the ratio of Zn: S: Se: 49.25:23.84:26.91 giving a stoichiometric formula of Zn1.0Se0.48S0.54. The elemental map of the films showed uniform distribution of elements on the entire area of the substrate (Figure 6).

3.3.3. Raman Spectroscopic Studies of ZnSSe Thin Films

Raman spectra of ZnSxSe1−x thin films deposited using 1:1 ratio of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] precursor mixture showed strong peaks at 240 cm−1 which shifted from the ZnSe peaks at (253 cm−1) and the peak at 300 cm−1 corresponds to ZnS phases (306 cm−1). Similarly the peak at 490 cm−1 corresponds to the Raman mode of ZnSe (498 cm−1). Other peak observed at 550 cm−1 was closer to the peak for ZnS (546 cm−1) (Figure 3(a)) [31] [32] [33] [34] [35] [37] . The Raman spectra of the ZnSxSe1−x films deposited using 1:0.75 molar ratio of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] showed strong peaks at 240 cm−1 which is shifted from the ZnSe peak at 252 cm−1 along with peaks at 300 cm−1 which correspond

(a) (b)

Figure 5. (a) and (b) are the SEM images (5000× magnification) of ZnSxSe1−x films obtained at 350˚C using 1:1 and 1:0.75 molar ratio [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] precursor mixtures. Inset shows images at 15000x magnification.

Figure 6. Elemental mapping of (a) ZnSSe films obtained at 350˚C with stoichiometric formulae Zn1.0Se0.48S0.54 deposited from 1:0.75 molar ratio of [Zn(Se2CNEt2)2]and [Zn(S2CNEt2)2] precursor mixtures; (b) Distribution of Zn; (c) Distribution of Se and; (d) Distribution of S.

to ZnS peak at 306 cm−1 [47] . Other peaks are similar to those observed for the films obtained from 1:1 mixture.

3.3.4. PL Spectra of ZnSSe Films

PL spectra of the ZnSxSe1−x films deposited using two different precursor mixture concentrations (1:1 and 1: 0.75 molar ratio of [Zn(Se2CNEt2)2] and [Zn(S2CNEt2)2] mixture) showed less intense emission than the ZnSe films. The Se rich ZnSSe films showed PL at about 485 nm which gave a band gap of about 2.55 eV. Whereas the one with 1:1 ratio of S:Se showed PL absorption about 465 nm which gave an average band gap of 2.66 eV. Both values found to be higher than the band gap for ZnSe (2.25 eV) (Figure 3(b)). PL absorption showed that the absorption shifted towards blue region because of the presence of S and PL absorption decreases with increase in S content in the ZnSSe films. PL spectra measured for these films showed blue shift compared to ZnSe films and showed band gap around 2.4 eV (referred as ZnSSe1). The values showed good agreement with the reported values of ZnSxSe1?x thin films with increase in value of S content [33] .

4. Conclusion

The band gap of ZnSe had been tuned from 2.25 eV to 2.66 eV by increasing the sulfur content in the alloy (ZnSxSe1−x). XRD and Raman spectra showed the purity of ZnSe and confirmed the formation of ternary phase (ZnSSe). The morphology of the films was changed by addition of sulphur into the selenium precursor. The recent use of thin film absorber layers in solar energy conversion devices has led to the real possibility of sustainable and inexpensive replacements for silicon-based photovoltaics based on compound semiconductors. Our new manuscript shows how band gap tuning can be achieved from the doping of sulphur or selenium in metal chalcogenide thin films. Chemical vapour deposition (CVD) techniques to produce these films are currently highly sought-after as they have the potential for eventual scale up should these materials for solar cells be the solution to the renewable energy problem.

Acknowledgements

YA is thankful to University of King Abdulaziz University for Funding.

Cite this paper

Alghamdi, Y. (2017) Composition and Band Gap Controlled AACVD of ZnSe and ZnSxSe1−x Thin Films Using Novel Single Source Precursors. Materials Sciences and Applications, 8, 726-737. https://doi.org/10.4236/msa.2017.810052

References

  1. 1. Haase, M.A., Qiu, J., Depuydt, J.M. and Cheng, H. (1991) Blue Green Laser Diodes. Applied Physics Letters, 59, 1272-1974.
    https://doi.org/10.1063/1.105472

  2. 2. Jeon, H., Ding, J., Patterson, W. and Nurmikko, A.V. (1991) Blue Green Injection Laser Diodes in (Zn,Cd)Se/ZnSe Quantum Wells. Applied Physics Letters, 59, 3619-3622.
    https://doi.org/10.1063/1.105625

  3. 3. Lakshmikvmar, S.T. (1994) Selenization of Cu and in Thin Films for the Preparation of Selenide Photo-Absorber Layers in Solar Cells Using Se Vapour Source. Solar Energy Materials and Solar Cells, 32, 7-9.
    https://doi.org/10.1016/0927-0248(94)90251-8

  4. 4. Zhu, Y.-C. and Bando, Y. (2003) Preparation and Photoluminescence of Single-Crystal Zinc Selenide Nanowires. Chemical Physics Letters, 377, 367-370.
    https://doi.org/10.1016/S0009-2614(03)01197-7

  5. 5. Mirov, S.B., Fedorov, V.V., Graham, K., Moskalev, I.S., Badikov, V.V. and Panyutin, V. (2002) Erbium Fiber Laser-Pumped Continuous-Wave Microchip Cr2+:ZnS and Cr2+:ZnSe Lasers. Optics Letters, 27, 909-914.
    https://doi.org/10.1364/OL.27.000909

  6. 6. Kouklin, N., Menon, L., Wong, A.Z., Thompson, D.W., Woollam, J.A. and Williams, P.F. (2001) Giant Photoresistivity and Optically Controlled Switching in Self-Assembled Nanowires. Applied Physics Letters, 79, 4423.
    https://doi.org/10.1063/1.1427156

  7. 7. Lokhande, C.D., Patil, P.S., Tributsch, H. and Ennaoui, A. (1998) ZnSe Thin Films by Chemical Bath Deposition Method. Solar Energy Materials and Solar Cells, 55, 379-393.
    https://doi.org/10.1016/S0927-0248(98)00112-3

  8. 8. Natarajan, C., Sharon, M., Lévy-Clément, C. and Neumann-Spallart, M. (1994) Electrodeposition of Zincselenide. Thin Solid Films, 237, 118-123.
    https://doi.org/10.1016/0040-6090(94)90247-X

  9. 9. Gal, D. and Hodes, G. (2000) Electrochemical Deposition of ZnSe and (Zn,Cd)Se Films from Nonaqueous Solutions. Journal of the Electrochemical Society, 147, 1825-1828.
    https://doi.org/10.1149/1.1393441

  10. 10. Pol, S.V., Pol, V.G. and Gedanken, A. (2007) Encapsulating ZnS and ZnSe Nanocrystals in the Carbon Shell: A RAPET Approach. The Journal of Physical Chemistry, 111, 13309-13314.

  11. 11. Ludolph, B., Malik, M.A., O’Brien, P. and Revaprasadu, N. (1998) Novel Single Molecule Precursor Routes for the Direct Synthesis of Highly Monodispersed Quantum dots of Cadmium or Zinc Sulfide or Selenide. Chemical Communications, No. 17, 1849-1850.
    https://doi.org/10.1039/a805411h

  12. 12. Revaprasadu, N., Malik, M.A., O’Brien, P. and Wakefield, G. (1999) Deposition of Zinc Sulfide Quantum Dots from a Single-Source Molecular Precursor. Journal of Materials Research, 14, 3237-3240.
    https://doi.org/10.1557/JMR.1999.0437

  13. 13. Malik, M.A., Motevalli, M. and O’Brien, P. (1995) Structural Diversity in the Carbamato Chemistry of Zinc: X-Ray Single-Crystal Structures of
    [(Me2NCH2)2Zn(O2CN(C2H5)2)2] and [C5H5NZn2Me(O2CN(C2H5)2)3]. Inorganic Chemistry, 34, 6223-6225.
    https://doi.org/10.1021/ic00128a042

  14. 14. Memon, A.A., Afzaal, M., Malik, M.A., Nguyen, C., O’Brien, P. and Raftery, J. (2006) The N-Alkyldithiocarbamato Complexes [M(S2CNHR)2] (M = Cd(ii)Zn(ii); R = C2H5, C4H9, C6H13, C12H25); Their Synthesis, Thermal Decomposition and Use to Prepare of Nanoparticles and Nanorods of CdS. Dalton Transactions, No. 37, 4499-4505.
    https://doi.org/10.1039/b606661e

  15. 15. Binks, D.J., Bants, S.P., West, D.P., Malik, M.A. and O’Brien, P. (2003) CdSe/CdS Core/Shell Quantum Dots as Sensitizer of a Photorefractive Polymer Composite. Journal of Modern Optics, 50, 299.

  16. 16. Malik, M.A., Motevalli, M., Saeed, T. and O’Brien, P. (1993) Methylzinc or Methylcadmium-N,N,N-Trimethyl-Propylenediamine Dithiocarbamates: Precursors for Zinc or Cadmium Sulfide. The X-Ray Crystal Structure of Methylcadmiumtrimethylpropylene-Diaminedithiocarbamate Benzene Solvate. Advanced Materials, 5, 653. https://doi.org/10.1002/adma.19930050913

  17. 17. Panneerselvam, A., Nguyen, C.Q., Malik, M.A., O’Brien, P. and Raftery, J. (2009) The CVD of Silver Selenide Films from Dichalcogenophosphinato and Imidodichalcogenodiphosphinatosilver(I) Single-Source Precursors. Journals of Materials Chemistry, 19, 419-427.
    https://doi.org/10.1039/B812074A

  18. 18. Malik, M.A., et al. (1999) Studies of the Thermal Decomposition of Some Diselenocarbamato Complexes of Cadmium or Zinc: Molecular Design for the Deposition of MSe Films by CVD. Journal of Materials Chemistry, 10, 2433-2437.

  19. 19. Akhtar, M., Akhter, J., Malik, M.A., O’Brien, P., Tuna, F., Raftery, J. and Helliwell, M. (2011) Deposition of Iron Sulfide Nanocrystals from Single Source Precursors. Journal of Materials Chemistry, 26, 9737-9745.
    https://doi.org/10.1039/c1jm10703h

  20. 20. Afzaal, M., Malik, M.A. and O’Brien, P. (2010) Chemical Routes to Chalcogenide Materials as Thin Films or Particles with Critical Dimensions with the Order of Nanometers. Journal of Materials Chemistry, 20, 4031-4040.
    https://doi.org/10.1039/b923898k

  21. 21. Malik, M.A., et al. (1999) Novel Single-Molecule Precursor Routes for the Direct Synthesis of InS and InSe Quantum Dots. Journal of Materials Chemistry, 9, 2885-2888.
    https://doi.org/10.1039/a905578i

  22. 22. Abdelhady, L., Ramasamy, K., Malik, M.A., O’Brien, P., Haigh, S.J. and Raftery, J. (2011) New Routes to Copper Sulfide Nanostructures and Thin Films. Journal of Materials Chemistry, 44, 17888-17895.
    https://doi.org/10.1039/c1jm13277f

  23. 23. Dabbousi, B., Bonasia, P.J. and Arnold, J. (1991) Tris(trimethylsilyl)silanetellurol: Preparation, Characterization, and Synthetic Utility of a Remarkably Stable Tellurol. Journal of Chemical Society, 113, 3186-3188.
    https://doi.org/10.1021/ja00008a065

  24. 24. Adeogun, A., Nguyen, C.Q., Afzaal, M., Malik, M.A. and O’Brien, P. (2006) Facile and Reproducible Syntheses of Bis(dialkylselenophosphenyl)-Selenides and -Diselenides: X-Ray Structures of (iPr2PSe)2Se, (iPr2PSe)2Se2 and (Ph2PSe)2Se. Chemical Communications, 2179.

  25. 25. Nguyen, C.Q., Adeogun, A., Afzaal, M., Malik, M.A. and O’Brien, P. (2006) Metal Complexes of Selenophosphinates from Reactions with (R2PSe)2Se: [M(R2PSe2)n] (M = ZnII, CdII, PbII, InIII, GaIII, CuI, BiIII, NiII; R = iPr, Ph) and [MoV2O2Se2(Se2PiPr2)2]. Chemical Communications, No. 20, 2182.
    https://doi.org/10.1039/b603198f

  26. 26. Abrahams, I., Malik, M.A., Motevalli, M. and O’Brien, P. (1994) Some Complexes of Neopentylcadmium Species with Dithio- and Di-Selenocarbamates: The Synthesis, Characterization and Single Crystal X-Ray Structure of a Mixed Neopentyl/Diethyldiselenocarbamate of Cadmium: [(CH3)3CCH2CdSe2CNEt2]2. Journal of Organometallic Chemistry, 465, 73-77.
    https://doi.org/10.1016/0022-328X(94)87038-1

  27. 27. Hursthouse, M.B., Malik, M.A., Motevalli, M. and O’Brien, P. (1991) Mixed Alkyl Dialkylthiocarbamates of Zinc and Cadmium: Potential Precursors for II/VI Materials. X-Ray Crystal Structure of [MeZnS2CNEt2]2. Organometallics, 10, 730-732.
    https://doi.org/10.1021/om00049a036

  28. 28. Malik, M.A. and O’Brien, P. (1991) Mixed Methyl and Ethylzinc Complexes with Diethylselenocarbamate: Novel Precursors for Zinc Selenide. Chemistry of Materials, 3, 999-1000.
    https://doi.org/10.1021/cm00018a007

  29. 29. Malik, M.A., Motevalli, M., O’Brien, P. and Walsh, J.R. (1992) Mixed Neopentyl or Tbutyl Zinc Complexes with Diethyl-Thio or -Selenocarbamates: Potential Precursors for Zinc Chalcogenides. Organometallics, 11, 3436.
    https://doi.org/10.1021/om00045a033

  30. 30. Hursthouse, M.B., Malik, M.A., Motevalli, M. and O’Brien, P. (1992) Synthesis and Characterization of Some Mixed Alkyl Selenocarbamates of Zinc and Cadmium: Novel Precursors for II/VI Materials. Journal of Materials Chemistry, 2, 949-955.
    https://doi.org/10.1039/jm9920200949

  31. 31. Afzaal, M., Crouch, D., O’Brien, P. and Park, J.H. (2002) New Approach towards the Deposition of I-III-VI Thin Films. Materials Research Society Symposium Proceedings, 692, 215-220.

  32. 32. Osakada, K. and Yamamoto, T. (1987) Formation of ZnS and CdS by Thermolysis of Homoleptic Thiolato Compounds [M(SMe)2]n(M = Zn,Cd). Journal of the Chemical Society, Chemical Communications, No. 14, 1117.
    https://doi.org/10.1039/c39870001117

  33. 33. Brennan, J.G., Siegrist, T., Carroll, P.J., Stuczynski, S.M., Reynders, P., Brus, L.E. and Steigerwald, M.L. (1990) Bulk and Nanostructure Group II-VI Compounds from Molecular Organometallic Precursors. Chemical Materials, 2, 403-409.
    https://doi.org/10.1021/cm00010a017

  34. 34. Afzaal, M., Crouch, D., Malik, M.A., Motevalli, M., O’Brien, P., Park, J.-H. and Woollins, J.D. (2004) Deposition of II-VI Thin Films by LP-MOCVD Using Novel Single-Source Precursors. European Journal of Inorganic Chemistry, No. 1, 171-177.
    https://doi.org/10.1002/ejic.200300101

  35. 35. Afzaal, M., Crouch, D., Malik, M.A., Motevalli, M., O’Brien, P. and Park, J.-H. (2003) Deposition of CdSe Thin Films Using a Novel Single-Source Precursor; [MeCd{(SePiPr2)2N}]2. Journal of Materials Chemistry, 13, 639-640.
    https://doi.org/10.1039/b300608p

  36. 36. Rojas, F.E., Rodríguez, J.A., Quiñones, C., Rodríguez, O. and Gordillo, G. (2004) Effect of Surface Roughness on the Optical Constants of ZnSxSe1-x Thin Films. Physica Status Solidi (A), 201/10, 2366-2369.
    https://doi.org/10.1002/pssa.200304906

  37. 37. Stutius, W. (1982) Growth and Doping of ZnSe and ZnSxSe1-x by Organometallic Chemical Vapor Deposition. Journal of Crystal Growth, 59, 1-9.
    https://doi.org/10.1016/0022-0248(82)90302-5

  38. 38. Teraguchi, N., Hirata, S., H. Mouri, H., Tomomura, Y., Suzuki, A. and Takiguchi, H. (1995) Growth and Characterization of N-Doped ZnSxSe1-x (0 ≦ x < 0.3) by Molecular Beam Epitaxy. Journal of Crystal Growth, 50, 803-806.
    https://doi.org/10.1016/0022-0248(95)80050-M

  39. 39. Kevin, P., Alghamdi, Y. and Malik, M.A. (2015) Morphology and Band Gap Controlled AACVD of CdSe and CdSxSe1-x Thin Films Using Novel Single Source Precursors: Bis(diethyldithio/diselenocarbamato)cadmium(II). Materials Science in Semiconductor Processing, 40, 848-854.
    https://doi.org/10.1016/j.mssp.2015.07.076

  40. 40. Shakir, M., Kushwaha, K., Maurya, K.K., Bhagavannarayana, G. and Wahab, M.A. (2009) Characterization of ZnSe Nanoparticles Synthesized by Microwave Heating Process. Solid State Communications, 149, 2047-2049.
    https://doi.org/10.1016/j.ssc.2009.08.021

  41. 41. Zhang, H., Yang, H.Q., Xie, X.L., Zhang, F.H. and Li, L. (2009) Preparation and Photocatalytic Activity of Hollow ZnSe Microspheres via Ostwald Ripening. Journal of Alloys and Compounds, 473, 65-70.
    https://doi.org/10.1016/j.jallcom.2008.06.018

  42. 42. Zahn, D.R.T. (1998) Raman Monitoring of Wide Bandgap MBE Growth. Applied Surface Science, 123/124, 276-282.
    https://doi.org/10.1016/S0169-4332(97)00435-2

  43. 43. Li, H., Wang, B. and Li, L. (2010) Study on Raman Spectra of Zinc Selenide Nanopowders Synthesized by Hydrothermal Method. Journal of Alloys and Compounds, 506/1, 327-330.
    https://doi.org/10.1016/j.jallcom.2010.06.201

  44. 44. Elschner, B. and Schlaak, M. (1967) Electron Paramagnetic Resonance in Cadmium Oxide. Physics Letters, 24, 10-12.
    https://doi.org/10.1016/0375-9601(67)90168-5

  45. 45. Jiang, Y., Meng, X.-M., Yu, W.-C., Liu, J., Ding, J.X., Lee, C.-S. and Lee, S.-T. (2004) Zinc Selenide Nanoribbons and Nanowires. The Journal of Physical Chemistry B, 108, 2784-2787.
    https://doi.org/10.1021/jp035595+

  46. 46. Cheng, Y.C., Jin, C.Q., Gao, F., Wu, X.L., Zhong, W., Li, S.H. and Chu, P.K. (2009) Raman Scattering Study of Zinc Blende and Wurtzite ZnS. Journal of Applied Physics, 106, Article ID: 123505.
    https://doi.org/10.1063/1.3270401

  47. 47. Xu, H., Liang, Y., Liu, Z., Zhang, X. and Hark, S. (2008) Synthesis and Optical Properties of Tetrapod-Like ZnSSe Alloy Nanostructures. Advanced Materials, 20, 3294-3297.
    https://doi.org/10.1002/adma.200800821

Journal Menu>>